US5234149A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Debondable metallic bonding method
Assignee: Agere Systems LLC
•
Filing: 1992-08-28
•
Granted: 1993-08-10
•
Expires: 2012-08-28
Abstract
Abstract One or more metallized chip terminals of an electronic device, such as an integrated circuit chip or a laser chip, in one embodiment are temporarily bonded to one or more metallized substrate pads of a wiring substrate, as for the purpose of electrically testing the electronic device. The composition of the metallized chip terminals is suitably different from that of the metallized substrate pads. The pads and terminals are aligned and electrically connected together with a solder located between them under pressure and a temperature above the melting point of the solder. The solder is cooled, and electrical tests of the electronic device are performed by means of electrical access from testing circuitry to the chip terminals through the substrate pads. Then the solder is heated again above its melting point while being immersed in a liquid flux, whereby the liquid solder wets the metallized chip terminals but not the metallized substrate pads, and the device is gently mechanically pulled away from the wiring substrate and is cooled thereafter. This substrate can thereafter be reused for testing other electronic devices that have similarly suitably metallized terminals. In another embodiment, testing can be performed or not as may be desired; and, as for the purpose of chip operation as an integrated circuit or laser, the chip can be allowed to remain permanently bonded to the substrate in the form of a heat-sinking or heat-spreading submount, or it can be allowed to remain only temporarily bonded to the submount and subsequently pulled away from the submount for the purpose of reuse of the submount for another chip.
Inventors
- 👤 Avishay Katz
- 👤 Chien-Hsun Lee
- 👤 King L. Tai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:46
CPC Classifications
G; G01; G01R; G01R1/00; G01R1/02; G01R1/04; H; H10; H10P; H10P74/00; H10W; H10W72/00; H10W72/01; H10W72/012; H10W72/071; H10W72/072; H10W72/20; H10W72/221; H10W72/222; H10W72/241; H10W72/251; H10W72/252; H10W72/90; H10W72/951; H10W72/952; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49147; Y10T29/49149
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
282 words
A method of bonding each of a first set of one or more localized metallized regions on a set of wiring terminals of a first device, each of the localized regions having a first device metallization, to a separate one of each of a second set of one or more metallized regions located on a set of pads of a second device, each of the localized regions of the second set having a second metallization that is different from the first metallization, comprising the steps of: (a) forming a separate solder ball on each of the metallized regions of the first set; (b) bringing each such solder ball into contiguity with an exposed surface of a separate one of the metallized regions of the second set; (c) heating each such solder ball to a first temperature that is higher than its melting point, whereby each solder ball becomes a flattened solder ball; and (d) cooling each flattened solder ball to a second temperature that is below its melting temperature, the first and second metallizations having differing first and second compositions, respectively, such that when each flattened solder ball is heated to a third temperature while immersed in a liquid flux that facilitates wetting the first but not the second metallization, the third temperature being higher than the melting point of the solder, each of the flattened solder balls becomes a melted solder ball that wets each of the metallized regions of the first set but does not wet any of the metallized regions of the second set, whereby the first device can be mechanically pulled away from the second device while the melted solder balls are thus immersed in the liquid flux.
Claim 2
Independent Claim
282 words
A method of bonding each of a first set of one or more localized metallized regions on a set of wiring terminals of a first device, each of the localized regions having a first device metallization, to a separate one of each of a second set of one or more metallized regions located on a set of pads of a second device, each of the localized regions of the second set having a second metallization that is different from the first metallization, comprising the steps of: (a) forming a separate solder ball on each of the metallized regions of the first set; (b) bringing each such solder ball into contiguity with an exposed surface of a separate one of the metallized regions of the second set; (c) heating each such solder ball to a first temperature that is higher than its melting point, whereby each solder ball becomes a flattened solder ball; and (d) cooling each flattened solder ball to a second temperature that is below its melting temperature, the first and second metallizations having differing first and second compositions, respectively, such that when each flattened solder ball is heated to a third temperature while immersed in a liquid flux that facilitates wetting the first but not the second metallization, the third temperature being higher than the melting point of the solder, each of the flattened solder balls becomes a melted solder ball that wets each of the metallized regions of the first set but does not wet any of the metallized regions of the second set, whereby the first device can be mechanically pulled away from the second device while the melted solder balls are thus immersed in the liquid flux.
Claim 3
Dependent Claim
80 words
The method of claim 1 in which the first device metallization is formed prior to step (a) by the steps comprising co-depositing chromium and copper overlying the terminals, whereby a co-deposited chrome-copper layer is formed; depositing thereon a copper layer; and depositing thereon a gold or a tin layer, and in which the second device metallization is formed prior to step (b) by the steps comprising depositing overlying the pads a layer of tungsten or tantalum or molybdenum or titanium.
Claim 4
Dependent Claim
37 words
The method of claim 2 in which the second device metallization is formed, prior to the step (b) by the steps comprising forming, overlying each of the pads, a metallic barrier layer that does not contain copper.
Claim 5
Dependent Claim
18 words
The method of claim 1 further comprising, prior to step (b), a step of preparing the second device.
Claim 6
Dependent Claim
18 words
The method of claim 1 further comprising, prior to step (a), a step of preparing the first device.
Claim 7
Independent Claim
276 words
A method of temporarily bonding each of a first set of one or more localized metallized regions on a set of wiring terminals of a first device, each of the localized regions having a first device metallization, to a separate one of each of a second set of one or more metallized regions located on a set of pads of a second device, each of the localized regions of the second set having a second metallization that is different from the first metallization, comprising the steps of: (a) forming a separate solder ball on each of the metallized regions of the first set; (b) bringing each such solder ball into contiguity with an exposed surface of a separate one of the metallized regions of the second set; (c) heating each such solder ball to a first temperature that is higher than its melting point, whereby each solder ball becomes a flattened solder ball; (d) immersing each flattened solder ball in a liquid flux that facilitates wetting the first but not the second device metallization by the solder; (e) heating each such solder ball to a second temperature that is higher than the melting point of the solder, whereby the solder becomes melted solder, the first and second metallizations having different first and second compositions, respectively, such that solder in the presence of the liquid flux at the second temperature wets each of the metallized regions of the first set but does not wet the metallized regions of the second set; and (f) mechanically pulling apart the first device from the second device while the solder balls are thus melted and thus immersed in the liquid flux.
Claim 8
Independent Claim
276 words
A method of temporarily bonding each of a first set of one or more localized metallized regions on a set of wiring terminals of a first device, each of the localized regions having a first device metallization, to a separate one of each of a second set of one or more metallized regions located on a set of pads of a second device, each of the localized regions of the second set having a second metallization that is different from the first metallization, comprising the steps of: (a) forming a separate solder ball on each of the metallized regions of the first set; (b) bringing each such solder ball into contiguity with an exposed surface of a separate one of the metallized regions of the second set; (c) heating each such solder ball to a first temperature that is higher than its melting point, whereby each solder ball becomes a flattened solder ball; (d) immersing each flattened solder ball in a liquid flux that facilitates wetting the first but not the second device metallization by the solder; (e) heating each such solder ball to a second temperature that is higher than the melting point of the solder, whereby the solder becomes melted solder, the first and second metallizations having different first and second compositions, respectively, such that solder in the presence of the liquid flux at the second temperature wets each of the metallized regions of the first set but does not wet the metallized regions of the second set; and (f) mechanically pulling apart the first device from the second device while the solder balls are thus melted and thus immersed in the liquid flux.
Claim 9
Dependent Claim
22 words
The method of claim 6 further comprising, prior to step (a), the steps of forming the first metallization and the second metallization.
Claim 10
Dependent Claim
47 words
A method according to claim 7 of temporarily bonding, to each of the second set of localized regions of the second device, each of the first set of localized regions of each of a plurality of the first devices, one of the first devices after the other.
Claim 11
Dependent Claim
82 words
The method of claim 7 in which the first device metallization is formed prior to step (a) by the steps comprising co-depositing chromium and copper overlying the terminals, whereby a co-deposited chrome-copper layer is formed; depositing thereon a copper layer; and depositing thereon a gold or a tin protective capping layer, and in which the second device metallization is formed prior to step (b) by the steps comprising depositing overlying the pads a layer of tungsten or tantalum or molybdenum or titanium.
Claim 12
Dependent Claim
18 words
The method of claim 6 further comprising, prior to step (b), a step of preparing the second device.
Claim 13
Dependent Claim
47 words
A method according to claim 10 of temporarily bonding, to each of the second set of localized regions of the second device, each of the first set of localized regions of each of a plurality of the first devices, one of the first devices after the other.
Claim 14
Dependent Claim
18 words
The method of claim 6 further comprising, prior to step (a), a step of preparing the first device.
Claim 15
Dependent Claim
33 words
The method of claim 6 further comprising, between steps (a) and (b), the step of heating each solder ball to a temperature that is sufficient to soften it, but not to melt it.
Claim 16
Dependent Claim
38 words
The method of claim 6 further comprising, during step (c), or between steps (b) and (c), or between steps (b) and (c) and during step (c), the step of immersing each solder ball in a reducing gas ambient.
Claim 17
Dependent Claim
37 words
The method of claim 6 further including, between the step (c) and the step (d), the step of cooling each flattened solder ball to a third temperature that is lower than the melting temperature of the solder.
Claim 18
Dependent Claim
64 words
The method of claim 15 further comprising, after the step of cooling to a third temperature, the step of applying test voltages to the first device through at least one of the metallized regions of the second and first sets, respectively, and the step of measuring a response through at least one other of a metallized region of the first and second sets, respectively.
Claim 19
Dependent Claim
18 words
The method of claim 16 further comprising, prior to step (b), a step of preparing the second device.
Claim 20
Dependent Claim
18 words
The method of claim 16 further comprising, prior to step (a), the step of preparing the first device.
Claim 21
Dependent Claim
20 words
A method of testing a plurality of the first devices, one after the other, each in accordance with claim 17.
Claim 22
Dependent Claim
46 words
A method according to claim 6 of temporarily bonding, to each of the second set of localized regions of the second device, each of the first set of localized regions of each of plurality of the first devices, one of the first devices after the other.
References Cited (Backward Citations)
US3141226A
Cited
US3429040A
Cited
US3436818A
Cited
US3716907A
Cited
US4396140A
Cited
US4889275A
Cited
US4940181A
Cited
US5007163A
Cited
US5060844A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-08-09 | 1997-02-08 | 1997-08-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-08-09 | 2001-02-08 | 2001-08-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-08-09 | 2005-02-08 | 2005-08-10 | $7700.00 | Window Closed / Lapsed |