Method of forming weld bead of pure copper on ferroalloy base material
Assignee: Toyota Industries Corp
•
Filing: 1991-04-03
•
Granted: 1993-07-27
•
Expires: 2011-04-03
Abstract
Abstract In forming a weld bead of pure copper on a ferroalloy base material by laying a powder of copper and melting the powder by a high density energy source such as laser beams, TIG arc or electron beams, the powder of copper is beforehand mixed with a powder of an auxiliary metal having a higher melting point than pure copper. In order to ensure the substantial purity in copper of the weld bead, the powder mixture should not include more than 16 wt % nickel.
Inventors
- 👤 Minoru Kawasaki
- 👤 Soya Takagi
- 👤 Shinji Kato
- 👤 Kazuhiko Mori
- 👤 Yasuo Kotetsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:19
CPC Classifications
B; B23; B23K; B23K9/00; B23K9/04; B23K15/00; B23K15/0046; B23K15/0086; B23K26/00; B23K26/20; B23K26/32; B23K26/34; B23K26/342; B23K35/00; B23K35/001; B23K35/004; B23K35/22; B23K35/24; B23K35/30; B23K35/302; C; C22; C22C; C22C9/00; C22C9/06; B23K2103/00; B23K2103/50
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
157 words
A method of forming a weld bead on a carbon-containing ferroalloy base material, with said weld bead having a copper component, said method comprising laying a powder mixture comprising pure copper and an auxiliary metal or alloy including at least nickel in an amount not exceeding 16 wt. %, with said auxiliary metal or alloy having a higher melting point than pure copper and being weldable to said ferroalloy base material, thereafter melting said powder mixture by an energy source to form a melt therefrom and cooling said melt to form said weld bead at a cooling rate at which said auxiliary metal or alloy forms a solidified layer in contact with said ferroalloy base material prior to solidification of said copper component to prevent diffusion of carbon from said ferroalloy base material to said copper component prior to solidification thereof, whereby contamination of said weld bead by carbon diffusion from the ferroalloy base material is avoided.
Claim 2
Independent Claim
157 words
A method of forming a weld bead on a carbon-containing ferroalloy base material, with said weld bead having a copper component, said method comprising laying a powder mixture comprising pure copper and an auxiliary metal or alloy including at least nickel in an amount not exceeding 16 wt. %, with said auxiliary metal or alloy having a higher melting point than pure copper and being weldable to said ferroalloy base material, thereafter melting said powder mixture by an energy source to form a melt therefrom and cooling said melt to form said weld bead at a cooling rate at which said auxiliary metal or alloy forms a solidified layer in contact with said ferroalloy base material prior to solidification of said copper component to prevent diffusion of carbon from said ferroalloy base material to said copper component prior to solidification thereof, whereby contamination of said weld bead by carbon diffusion from the ferroalloy base material is avoided.
Claim 3
Dependent Claim
21 words
A method according to claim 1, wherein a nickel content of the powder mixture is not more than 15 wt %.
Claim 4
Dependent Claim
21 words
A method according to claim 1, wherein a nickel content of the powder mixture is not more than 13 wt %.
Claim 5
Dependent Claim
21 words
A method according to claim 1, wherein a nickel content of the powder mixture is not less than 4 wt %.
Claim 6
Dependent Claim
18 words
A method according to claim 1, wherein the copper content of the powder mixture is 50-95 wt %.
Claim 7
Dependent Claim
18 words
A method according to claim 1, wherein the copper content of the powder mixture is 60-90 wt %.
Claim 8
Dependent Claim
25 words
A method according to claim 1, wherein a total content of B, Si and C of 0.5-7.5 wt % is included in the powder mixture.
Claim 9
Dependent Claim
23 words
A method according to claim 7, wherein the total content of B, Si and C of the powder mixture is 1.0-5.0 wt %.
Claim 10
Dependent Claim
33 words
A method according to claim 1, wherein any metal element constituting the auxiliary powder is selected so that the solubility thereof in copper at room temperature is not more than 0.5 wt %.
Claim 11
Dependent Claim
23 words
A method according to claim 1, wherein the density energy source is selected from laser beams, Tungsten inert gas arc and electron beams.
Claim 12
Dependent Claim
48 words
A method according to claim 10, wherein when laser beams or electron beams are used for the density energy source, the powder mixture is successively supplied onto the surface of the base material along a line of scanning of the laser or electron beams as said beams proceed.
References Cited (Backward Citations)
US2427517A
Cited
US4267241A
Cited
JPS62101392A
Cited
EP0221752A2
Cited
US4832982A
Cited
EP0344310A1
Cited
US4818307A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-07-26 | 1997-01-25 | 1997-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-07-26 | 2001-01-25 | 2001-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-07-26 | 2005-01-25 | 2005-07-27 | $7700.00 | Window Closed / Lapsed |