Assignee: Toyota Motor Corp
•
Filing: 1987-12-07
•
Granted: 1989-05-23
•
Expires: 2007-12-07
Abstract
Abstract Herein disclosed is a process for forming a dispersion alloy layer on a metallic base. The powder of an alloy system, which will separate into two or more multi-liquid phases at a temperature equal to or higher than its melting point and will solidify, when quenched, with its individual liquid phases being separate and in which the ratio of the minimum to the maximum specific weight its individual liquid phases is 0.3 or higher, such as the powder of any alloy system of Cu-Ni(15%)-Fe(8%)-Si(3%)-B(1.5%) is applied to a metallic base. The powder thus applied is then melting and agitated while being irradiated with a laser beam oscillated. The agitated melt of the powder is then quenched to solidify with the movement of the laser beam thereby to form on the metallic base the dispersion alloy layer in which the solid particles of at least one of those phase such as silicide particles are dispersed in the matrix of the remaining one of the phases.
Inventors
- 👤 Kazuhiko Mori
- 👤 Katsuhiko Ueda
- 👤 Soya Takagi
- 👤 Minoru Kawasaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 01:55
CPC Classifications
B; B23; B23K; B23K26/00; B23K26/34; B22; B22F; B22F10/00; B22F10/20; B22F10/25; B22F10/30; B22F10/36; B22F7/00; B22F7/06; B22F7/062; B23K26/20; B23K26/32; B23K35/00; B23K35/02; B23K35/0222; B23K35/0244; B23K35/22; B23K35/24; B23K35/30; B23K35/302; C; C22; C22C; C22C32/00; C22C32/0047; C22C9/00; C22C9/06; C22F; C22F1/00; C22F1/08; C23; C23C; C23C24/00; C23C24/08; C23C24/10; C23C24/103; B23K2101/00; B23K2101/005; B23K2103/00; B23K2103/02; B23K2103/04; B23K2103/06; B23K2103/08; B23K2103/10; B23K2103/12; B23K2103/18; B23K2103/50; Y; Y02; Y02P; Y02P10/00; Y02P10/25; Y10; Y10S; Y10S148/00; Y10S148/902; Y10S148/903; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12069; Y10T428/12076; Y10T428/12083; Y10T428/12097; Y10T428/12139; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12903
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
218 words
A process for forming a dispersion alloy layer on a metallic base, comprising the steps of: applying to a metallic base either an alloy powder made of an alloy system, which will separate into two or more multi-liquid phases at a temperature equal to or higher than its melting point and will solidify, when quenched, with its individual liquid phases being separate and in which the ratio of the minimum to the maximum specific weight of the separately solidifying liquid phases is 0.3 or higher, or a mixed powder which can compose said alloy system; irradiating the alloy or mixed powder on said metallic base with a laser beam to melt the same, while oscillating said laser beam with a frequency of 10 to 500 Hz in a direction generally perpendicular to a primary relative moving direction to agitate the melt of said alloy or mixed powder on said metallic base; and moving said laser beam in said primary relative moving direction relative to said metallic base to quench said melt to solidify at a quenching rate of 10 3 deg/sec or higher thereby to form on said metallic base a dispersion alloy layer in which the solid particles of at least one of said phases are dispersed in the matrix of the remaining one of said phases.
Claim 2
Dependent Claim
218 words
A process for forming a dispersion alloy layer on a metallic base, comprising the steps of: applying to a metallic base either an alloy powder made of an alloy system, which will separate into two or more multi-liquid phases at a temperature equal to or higher than its melting point and will solidify, when quenched, with its individual liquid phases being separate and in which the ratio of the minimum to the maximum specific weight of the separately solidifying liquid phases is 0.3 or higher, or a mixed powder which can compose said alloy system; irradiating the alloy or mixed powder on said metallic base with a laser beam to melt the same, while oscillating said laser beam with a frequency of 10 to 500 Hz in a direction generally perpendicular to a primary relative moving direction to agitate the melt of said alloy or mixed powder on said metallic base; and moving said laser beam in said primary relative moving direction relative to said metallic base to quench said melt to solidify at a quenching rate of 10 3 deg/sec or higher thereby to form on said metallic base a dispersion alloy layer in which the solid particles of at least one of said phases are dispersed in the matrix of the remaining one of said phases.
Claim 3
Dependent Claim
23 words
A process according to claim 1, wherein said laser beam is focused to have a diameter ranging from 0.5 mm to 5.0 mm.
Claim 4
Dependent Claim
26 words
A process according to claim 1, wherein said laser beam has an energy concentration ranging from 1×10 2 W/mm 2 to 2×10 4 W/mm 2 .
Claim 5
Dependent Claim
31 words
A process according to claim 1, wherein the relative moving velocity of said laser beam in said primary relative moving direction is set within a range of 450 to 2,000 mm/min.
Claim 6
Dependent Claim
14 words
A process according to claim 1, wherein said alloy system is a copper-based alloy.
Claim 7
Dependent Claim
24 words
A process according to claim 1, wherein said solid particles are selected from the group consisting of a silicide, a carbide and a boride.
References Cited (Backward Citations)
US967009A
Cited
UST967009I4
Cited
US4269868A
Cited
JPS5732373A
Cited
US4299860A
Cited
US4537793A
Cited
JPS61296973A
Cited
US4725708A
Cited
US4746540A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-22 | 1992-11-21 | 1993-05-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-22 | 1996-11-21 | 1997-05-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-22 | 2000-11-21 | 2001-05-23 | $7700.00 | Window Closed / Lapsed |