Mixing process for generating in-situ reinforced thermoplastics
Assignee: Virginia Tech Intellectual Properties Inc
•
Filing: 1991-05-01
•
Granted: 1993-07-06
•
Expires: 2011-05-01
Abstract
Abstract A method for blending polymeric materials includes the steps of producing a melt stream of a first polymer from a first extruder (12) and a separate melt stream of a second polymer from a second extruder (14), joining the melt streams at a T-junction (16), distributing the first polymer within said second polymer using a static mixer (10), and extruding the blend through a die (18). In particular, using this method liquid crystal polymer fiber reinforcement can be formed in-situ within a matrix material.
Inventors
- 👤 Donald G. Baird
- 👤 Ashish Sukhadia
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:24
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08L23/12; C08L101/00; C08L67/00; C08L67/02; C08L2205/00; C08L2205/12
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
102 words
A method for blending polymer materials, comprising the steps of: producing a first melt stream of a matrix polymer; producing a second melt stream of a liquid crystal polymer separate from said first melt stream; combining said first melt stream with said second melt stream prior to any other mixing of said first and second melt streams by dividing said first melt stream and said second melt stream and recombining them in geometrically different configurations with a static mixer or like element to form a blend; and allowing liquid crystal polymer fibers to form in-situ in said matrix polymer in said blend.
Claim 2
Independent Claim
102 words
A method for blending polymer materials, comprising the steps of: producing a first melt stream of a matrix polymer; producing a second melt stream of a liquid crystal polymer separate from said first melt stream; combining said first melt stream with said second melt stream prior to any other mixing of said first and second melt streams by dividing said first melt stream and said second melt stream and recombining them in geometrically different configurations with a static mixer or like element to form a blend; and allowing liquid crystal polymer fibers to form in-situ in said matrix polymer in said blend.
Claim 3
Dependent Claim
40 words
A method as recited in claim 1 wherein said matrix polymer and said fiber forming polymer have overlapping thermal processing ranges such that said steps of producing said first and second melt streams are accomplished at approximately the same temperature.
Claim 4
Dependent Claim
38 words
A method as recited in claim 1 wherein said matrix polymer and said fiber forming polymer have non-overlapping thermal processing ranges such that said steps of producing said first and second melt streams are accomplished at divergent temperatures.
Claim 5
Dependent Claim
35 words
A method as recited in claim 1 wherein said steps of producing said first and second melt streams include the steps of extruding said first and second melt streams from first and second extruders, respectively.
Claim 6
Dependent Claim
22 words
A method as recited in claim 1 wherein said matrix polymer is selected from the group consisting of polypropylene and polyethylene terephthalate.
Claim 7
Dependent Claim
79 words
A method as recited in claim 1 wherein said fiber forming polymer is selected from the group consisting of a copolyester of 27 mole % 2-hydroxy-6-naphthoic acid and 73 mole % hydroxybenzoic acid, a liquid crystal polyesteramide composed of 58 mole % 2-hydroxy-6-naphthoic acid, 21 mole % terephthalic acid, and 21 mole % 4'-hydroxy acetanilide, a copolyester comprised of terephthalic acid, hydroquinone, and phenyl hydroquinone, a copolyester of 60-80 mole % polyethylene terephthalate and 20-40 mole % para-hydroxybenzoic acid.
Claim 8
Dependent Claim
18 words
A method as recited in claim 1 further comprising the step of passing said blend through a die.
Claim 9
Dependent Claim
15 words
A method as recited in claim 1 further comprising the step of pelletizing said blend.
Claim 10
Dependent Claim
23 words
A method as recited in claim 1 further comprising the step of cooling said first melt stream before performing said step of dividing.
References Cited (Backward Citations)
US3937772A
Cited
US4012348A
Cited
US4433083A
Cited
US4547541A
Cited
EP0217563A2
Cited
US4728698A
Cited
EP0291323A2
Cited
EP0340655A2
Cited
US4919875A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-07-05 | 1997-01-04 | 1997-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-07-05 | 2001-01-04 | 2001-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-07-05 | 2005-01-04 | 2005-07-06 | $7700.00 | Window Closed / Lapsed |