Method of making polyaniline solid electrolyte capacitor
Assignee: Vishay Sprague Inc
•
Filing: 1991-10-31
•
Granted: 1993-06-29
•
Expires: 2011-10-31
Abstract
Abstract Highly conducting polyaniline is produced in situ in a tantalum capacitor by subjecting an excess of monomeric aniline to a solution having a low concentration of ammonium persulfate reagent. The monomer is oxidized by the reagent in preference to the polymer, so that the presence of excess monomer protects the polymer as it is produced against further oxidation to a less conductive species.
Inventors
- 👤 Sidney D. Ross
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 00:15
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/004; H01G9/022; H01G9/025; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
85 words
A method for producing a polyaniline solid electrolyte in a porous pellet comprising (a) impregnating said pellet with a solution of monomeric aniline and a diluent, (b) heating to a temperature sufficient to drive off said diluent and leave said aniline, and (c) immersing said pellet in a solution of ammonium persulfate and sulfuric acid having a concentration of persulfate that is substantially less than needed to oxidize all of said monomeric aniline so as to thereby polymerize less than all of said monomeric aniline.
Claim 2
Independent Claim
85 words
A method for producing a polyaniline solid electrolyte in a porous pellet comprising (a) impregnating said pellet with a solution of monomeric aniline and a diluent, (b) heating to a temperature sufficient to drive off said diluent and leave said aniline, and (c) immersing said pellet in a solution of ammonium persulfate and sulfuric acid having a concentration of persulfate that is substantially less than needed to oxidize all of said monomeric aniline so as to thereby polymerize less than all of said monomeric aniline.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein said diluent is methanol in a ratio of 1:5 of said aniline and said methanol, and said temperature is between 100° and 200° C.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein said concentration if 5 to 12 grams ammonium persulfate per 100 ml lN sulfuric acid.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein said persulfate and said aniline are present in a molar ratio of persulfate/aniline of less than 1.
Claim 6
Dependent Claim
43 words
The method of claim 1 wherein at least one impregnation subsequent to said impregnating step is in pure aniline and the concentration of persulfate is higher than said concentration while still substantially less than enough to oxidize all of said subsequent pure aniline.
References Cited (Backward Citations)
US4803596A
Cited
US4780796A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-28 | 1996-12-28 | 1997-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-28 | 2000-12-28 | 2001-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-28 | 2004-12-28 | 2005-06-29 | $7700.00 | Window Closed / Lapsed |