Process for cationic polymerizations
Assignee: University of Southern Mississippi
•
Filing: 1992-02-21
•
Granted: 1993-06-15
•
Expires: 2012-02-21
Abstract
Abstract Elastomeric polymers comprising polymerized alpha-olefins or conjugated alkadienes are produced by cationic polymerization in the presence of titanium tetrachloride and an electron pair donor selected from pyridine or a non-hindered alkylpyridine. The polymers have very narrow, mono-modal molecular weight distributions such a achived by anionic polymerization. Polymerization of each monomer is terminated prior to broadening of the molecular weight distribution which significantly detracts from polymer properties.
Inventors
- 👤 Robson F. Storey
- 👤 Youngkwan Lee
- 👤 Bret J. Chisholm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:05
CPC Classifications
C; C08; C08F; C08F297/00
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
73 words
A process for making an elastomeric polymer comprising an alpha-olefin or a conjugated alkadiene, comprising the steps of: cationically polymerizing an alpha-olefin monomer or a conjugated diene monomer in the presence of titanium tetrachloride and an electron pair donor selected from the group consisting of pyridine and non-hindered alkylpyridines to form living polymer molecules; and stopping polymerization of the monomer while the polydispersity index of the living polymer molecules is less than 1.2.
Claim 2
Dependent Claim
73 words
A process for making an elastomeric polymer comprising an alpha-olefin or a conjugated alkadiene, comprising the steps of: cationically polymerizing an alpha-olefin monomer or a conjugated diene monomer in the presence of titanium tetrachloride and an electron pair donor selected from the group consisting of pyridine and non-hindered alkylpyridines to form living polymer molecules; and stopping polymerization of the monomer while the polydispersity index of the living polymer molecules is less than 1.2.
Claim 3
Dependent Claim
20 words
The process of claim 1, wherein the polymerization of the monomer is stopped by addition of an alkenyl aromatic monomer.
Claim 4
Dependent Claim
56 words
The process of claim 2, further comprising the steps of: cationically polymerizing blocks of the alkenyl aromatic monomer onto the living polymer molecules in the presence of the titanium tetrachloride and the electron pair donor; and stopping polymerization of the alkenyl aromatic monomer while the polydispersity index of the living polymer molecules is less than 1.3.
Claim 5
Dependent Claim
28 words
The process of claim 3, wherein the electron pair donor has the aromatic structure: ##STR2## wherein R1 and R2 are independently hydrogen, methyl, ethyl, propyl, or butyl groups.
Claim 6
Dependent Claim
12 words
The process of claim 4, wherein the electron pair donor is pyridine.
Claim 7
Dependent Claim
17 words
The process of claim 5, wherein each polymerization step is stopped at 60%-90% conversion of the monomer.
Claim 8
Dependent Claim
123 words
A process for making a block copolymer comprising a block of an alpha-olefin or a conjugated alkadiene and a block of an alkenyl aromatic compound, comprising the steps of: cationically polymerizing an alpha-olefin monomer or a conjugated diene monomer in the presence of titanium tetrachloride and pyridine to form living polymer molecules; stopping polymerization of the monomer while the polydispersity index of the living polymer molecules is less than 1.2 by addition of an alkenyl aromatic monomer; cationically polymerizing blocks of the alkenyl aromatic monomer onto the living polymer molecules in the presence of the titanium tetrachloride and the electron pair donor; and stopping polymerization of the alkenyl aromatic monomer while the polydispersity index of the living polymer molecules is less than 1.3.
Claim 9
Dependent Claim
123 words
A process for making a block copolymer comprising a block of an alpha-olefin or a conjugated alkadiene and a block of an alkenyl aromatic compound, comprising the steps of: cationically polymerizing an alpha-olefin monomer or a conjugated diene monomer in the presence of titanium tetrachloride and pyridine to form living polymer molecules; stopping polymerization of the monomer while the polydispersity index of the living polymer molecules is less than 1.2 by addition of an alkenyl aromatic monomer; cationically polymerizing blocks of the alkenyl aromatic monomer onto the living polymer molecules in the presence of the titanium tetrachloride and the electron pair donor; and stopping polymerization of the alkenyl aromatic monomer while the polydispersity index of the living polymer molecules is less than 1.3.
Claim 10
Dependent Claim
35 words
The process of claim 7, wherein an alpha-olefin is polymerized to prepare the living polymer molecules and styrene is added to stop polymerization of the alpha-olefin and polymerize the styrene onto the living polymer molecules.
Claim 11
Dependent Claim
10 words
The process of claim 8, wherein the alpha-olefin is isobutylene.
Claim 12
Dependent Claim
26 words
The process of claim 9, wherein the cationic polymerization of the styrene is stopped while the living polymer molecules have a polydispersity index less than 1.2.
Claim 13
Dependent Claim
25 words
The process of claim 10, wherein cationic polymerization of the isobutylene is stopped while the living polymer molecules have a polydispersity index less than 1.1.
Claim 14
Dependent Claim
17 words
The process of claim 11, wherein each polymerization step is stopped at 60%-90% conversion of the monomer.
Claim 15
Dependent Claim
15 words
The process of claim 12, wherein the cationic polymerization is initiated with a difunctional initiator.
Claim 16
Dependent Claim
37 words
The process of claim 13, wherein each block of the isobutylene has a number average molecular weight from 2,000 to 200,000, and each block of the styrene has a number average molecular weight from 2,000 to 20,000.
Claim 17
Dependent Claim
112 words
An elastomeric polymer produced by the process of: cationically polymerizing an alpha-olefin or a conjugated diene monomer in the presence of titanium tetrachloride and an electron pair donor selected from the group consisting of pyridine and non-hindered alkylpyridines to form living polymer molecules; stopping polymerization of the monomer while the polydispersity index of the living polymer molecules is less than 1.2 by addition of an alkenyl aromatic monomer; cationically polymerizing the alkenyl aromatic monomer onto the living polymer molecules in the presence of the titanium tetrachloride and the electron pair donor; and stopping polymerization of the alkenyl aromatic monomer while the polydispersity index of the living polymer molecules is less than 1.3.
Claim 18
Dependent Claim
112 words
An elastomeric polymer produced by the process of: cationically polymerizing an alpha-olefin or a conjugated diene monomer in the presence of titanium tetrachloride and an electron pair donor selected from the group consisting of pyridine and non-hindered alkylpyridines to form living polymer molecules; stopping polymerization of the monomer while the polydispersity index of the living polymer molecules is less than 1.2 by addition of an alkenyl aromatic monomer; cationically polymerizing the alkenyl aromatic monomer onto the living polymer molecules in the presence of the titanium tetrachloride and the electron pair donor; and stopping polymerization of the alkenyl aromatic monomer while the polydispersity index of the living polymer molecules is less than 1.3.
Claim 19
Dependent Claim
13 words
The elastomeric polymer of claim 15, wherein the electron pair donor is pyridine.
Claim 20
Dependent Claim
15 words
The elastomeric polymer of claim 16, wherein the polymer consists of the block structure styrene-isobutylene-styrene.
Claim 21
Dependent Claim
47 words
The elastomeric polymer of claim 17, wherein: each block of the isobutylene has a number average molecular weight from 2,000 to 200,000; each block of the styrene has a number average molecular weight from 2,000 to 25,000; and the polymer has a polydispersity index less than 1.2.
References Cited (Backward Citations)
US5066730A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-14 | 1996-12-14 | 1997-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-14 | 2000-12-14 | 2001-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-14 | 2004-12-14 | 2005-06-15 | $7700.00 | Window Closed / Lapsed |