Living polymerization of olefins to end-functionalized polymers
Assignee: University of Akron
•
Filing: 1990-03-28
•
Granted: 1991-11-19
•
Expires: 2010-03-28
Abstract
Abstract This invention provides a novel catalyst composed of a complex of an organic ether and a Lewis acid, preferably boron trichloride that can add olefin monomers to increase the molecular weight of the complex from as low as 200 to in excess of 100,000 preferably 500 or 1000 to 10,000 and higher, with the complex being active viz., living, until the complex dies, viz., is decomposed or destroyed so that polymers in the liquid or easily liquefiable range of 300 to about 10,000 and preferably 500 or 1000 to 10,000 and higher can be made or those more difficult to be liquefied or unliquefiable, viz., those of over 10,000 up to 100,000 and having useful end groups such as the halogens and specifically chloride.
Inventors
- 👤 Joseph P. Kennedy
- 👤 Munmaya K. Mishra
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:21
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
75 words
A method of producing a living polymer complex exhibiting supernonnucleophilic counter anions comprising the steps of: a. reacting a Lewis acid and an organic ether at -10° C. or lower to yield a carbocationic center; and b. reacting said carbocationic center with an olefin monomer to yield said living polymer complex wherein said supernonnucleophilic counter anions do not cause deprotonation of the growing living polymer complex and chain transfer to the monomer does not occur.
Claim 2
Independent Claim
75 words
A method of producing a living polymer complex exhibiting supernonnucleophilic counter anions comprising the steps of: a. reacting a Lewis acid and an organic ether at -10° C. or lower to yield a carbocationic center; and b. reacting said carbocationic center with an olefin monomer to yield said living polymer complex wherein said supernonnucleophilic counter anions do not cause deprotonation of the growing living polymer complex and chain transfer to the monomer does not occur.
Claim 3
Dependent Claim
17 words
The living polymer complex of claim 1 wherein the Lewis acid is a chloride or a bromide.
Claim 4
Dependent Claim
37 words
The method of claim 1 wherein the Lewis acid is selected from the class consisting of BCl 3 , AlCl 3 , TiCl 4 , SbF 5 , FeCl 3 , ZnCl 2 and VCl 4 .
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein the reaction of the Lewis acid and organic ether occurs in a chlorohydrocarbon.
Claim 6
Dependent Claim
39 words
The method of claim 1 wherein sufficient olefin monomer has been added while maintaining the temperature below the decomposition temperature of said complex to increase its molecular weight to within a range of 1,000 to above a hundred thousand.
Claim 7
Dependent Claim
49 words
The method of claim 1 wherein the olefin reacts with the complex to give a polymer complex and to consume essentially all said olefin by 30 minutes but still has ability to add more olefin and polymer complex formed molecular weight is proportional to the monomer to initiator ratio.
Claim 8
Dependent Claim
24 words
The method of claim 1 wherein the molecular weight increase of said complex is proportional to monomer concentration divided by concentration of said complex.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein sufficient olefin monomers is contacted with said complex to increase its molecular weight to at least 1,000.
Claim 10
Dependent Claim
41 words
The method of claim 1 wherein the complex and olefin are fed simultaneously to a reactor and the temperature produced by mixing said complex and olefin would require 10 minutes to decompose half of the said complex fed to the reactor.
Claim 11
Dependent Claim
44 words
The method of claim 1 wherein the olefin monomers are isobutylene plus isoprene, said monomers being mixed with an ether complex of boron chloride at a temperature of about -30° C. to decomposition temperature of said complex to give a complex in rubber range.
Claim 12
Dependent Claim
13 words
The method of claim 1 wherein the organic ether is a tertiary ether.
Claim 13
Dependent Claim
19 words
The method of claim 11 wherein the tertiary ether has a tertiary carbon atom adjacent an ether carbon atom.
Claim 14
Dependent Claim
24 words
The method of claim 12 wherein a tertiary carbon atom is adjacent an ether carbon atom containing from 4 to about 12 carbon atoms.
Claim 15
Dependent Claim
18 words
The method of claim 1 wherein part of the organic ether forms an end group in the polymer.
References Cited (Backward Citations)
GB589393A
Cited
JPH0297509A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-11-18 | 1995-05-20 | 1995-11-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-11-18 | 1999-05-20 | 1999-11-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-11-18 | 2003-05-20 | 2003-11-19 | $7700.00 | Window Closed / Lapsed |