Method for forming a silicide layer and barrier layer on a semiconductor device rear surface
Assignee: Hitachi Ltd
•
Filing: 1991-12-19
•
Granted: 1993-06-08
•
Expires: 2011-12-19
Abstract
Abstract A method of manufacturing a semiconductor device wherein the back surface of a semiconductor chip is adhered closely to a substrate or a seal member through a soldering material or the like, and a metallized layer is formed on the back surface of the chip for attaining good adhesion. The metallized layer according to the present invention is a layer formed by laminating a metal silicide, a barrier metal and an oxidation preventing metal successively on the back of the chip. The layer of the metal silicide can be formed in a known heat treatment process, for example, simultaneously with the formation of bump electrodes, on a main surface of the semiconductor chip by the heat used at the time of forming such bump electrodes, or simultaneously with the mounting of the semiconductor chip by the heat used at the time of the chip mounting.
Inventors
- 👤 Hiroshi Akasaki
- 👤 Kanji Otsuka
- 👤 Tetsuya Hayashida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 08:52
CPC Classifications
H; H10; H10W; H10W72/00; H10W72/30; H10W95/00; H10W70/00; H10W70/60; H10W70/67; H10W70/68; H10W70/685; H10W72/071; H10W72/072; H10W72/07231; H10W72/07236; H10W72/073; H10W72/07331; H10W72/07337; H10W72/20; H10W72/251; H10W72/252; H10W72/29; H10W72/351; H10W72/352; H10W72/381; H10W72/50; H10W72/59; H10W72/851; H10W72/874; H10W72/877; H10W74/00; H10W76/00; H10W76/10; H10W76/17; H10W90/00; H10W90/701; H10W90/721; H10W90/724; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/4913; Y10T29/49144; Y10T29/49147; Y10T29/49149
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
104 words
A method for manufacturing a semiconductor device comprising the steps of: (a) providing a first substrate of silicon having a main surface with circuits and plural electrodes formed thereon and also having a back surface on an opposite side; (b) forming on the back surface a first metallic layer comprising a barrier metal and an oxidation preventing metal; (c) forming simultaneously bump electrodes on the electrodes and a second metallic layer of a metal silicide between said back surface and the barrier metal; and (d) fixing a second substrate into close contact with the back surface of the first substrate through an adhesive layer.
Claim 2
Independent Claim
104 words
A method for manufacturing a semiconductor device comprising the steps of: (a) providing a first substrate of silicon having a main surface with circuits and plural electrodes formed thereon and also having a back surface on an opposite side; (b) forming on the back surface a first metallic layer comprising a barrier metal and an oxidation preventing metal; (c) forming simultaneously bump electrodes on the electrodes and a second metallic layer of a metal silicide between said back surface and the barrier metal; and (d) fixing a second substrate into close contact with the back surface of the first substrate through an adhesive layer.
Claim 3
Dependent Claim
34 words
A method for manufacturing a semiconductor device according to claim 1, wherein the bump electrodes and the metal silicide layer are formed in an atmosphere at a temperature of not higher than 350° C.
Claim 4
Dependent Claim
19 words
A method for manufacturing a semiconductor device according to claim 1, wherein the adhesive layer is formed of solder.
Claim 5
Dependent Claim
28 words
A method for manufacturing a semiconductor device according to claim 1, wherein the metal silicide is one of Ni 2 Si, Pt 2 Si and Pd 2 Si.
Claim 6
Dependent Claim
22 words
A method for manufacturing a semiconductor device according to claim 1, wherein the barrier metal is one of Ni, Pt and Pd.
Claim 7
Dependent Claim
23 words
A method for manufacturing a semiconductor device according to claim 1, wherein the oxidation preventing metal is one of Au, Ag and Pt.
Claim 8
Independent Claim
138 words
A method for manufacturing a semiconductor device comprising the steps of: (a) providing a semiconductor chip of silicon having a main surface with circuits and plural bump electrodes formed thereon and also having on an opposite side a back surface with a first metallic layer formed thereon, the first metallic layer comprising at least two metals; (b) mounting the semiconductor chip onto a substrate having plural electrodes on the main surface thereof in such a manner that the bump electrodes and the electrodes of the substrate are interconnected electrically, and at the same time forming a second metallic layer of a metal silicide between the back surface of the semiconductor chip and the first metallic layer; and (c) sealing the semiconductor chip by sealing means through an adhesive layer formed on the back surface of the semiconductor chip.
Claim 9
Independent Claim
138 words
A method for manufacturing a semiconductor device comprising the steps of: (a) providing a semiconductor chip of silicon having a main surface with circuits and plural bump electrodes formed thereon and also having on an opposite side a back surface with a first metallic layer formed thereon, the first metallic layer comprising at least two metals; (b) mounting the semiconductor chip onto a substrate having plural electrodes on the main surface thereof in such a manner that the bump electrodes and the electrodes of the substrate are interconnected electrically, and at the same time forming a second metallic layer of a metal silicide between the back surface of the semiconductor chip and the first metallic layer; and (c) sealing the semiconductor chip by sealing means through an adhesive layer formed on the back surface of the semiconductor chip.
Claim 10
Dependent Claim
39 words
A method for manufacturing a semiconductor device according to claim 7, wherein the mounting of the semiconductor chip and the formation of the metal silicide are performed in an atmosphere at a temperature of not higher than 350° C.
Claim 11
Dependent Claim
38 words
A method for manufacturing a semiconductor device according to claim 7, wherein the first metallic layer is formed by laminating a barrier metal and an oxidation preventing metal successively from the back surface side of the semiconductor chip.
Claim 12
Dependent Claim
41 words
A method for manufacturing a semiconductor device according to claim 7, wherein the first metallic layer is formed by laminating a metal silicide, a barrier metal and an oxidation preventing metal successively from the back surface side of the semiconductor chip.
Claim 13
Dependent Claim
19 words
A method for manufacturing a semiconductor device according to claim 7, wherein the adhesive layer is formed of solder.
Claim 14
Dependent Claim
22 words
A method for manufacturing a semiconductor device according to claim 9, wherein the barrier metal is one of Ni, Pt and Pd.
Claim 15
Dependent Claim
23 words
A method for manufacturing a semiconductor device according to claim 9, wherein the oxidation preventing metal is one of Au, Ag and Pt.
Claim 16
Dependent Claim
28 words
A method for manufacturing a semiconductor device according to claim 10, wherein the metal silicide is one of Ni 2 Si, Pt 2 Si and Pd 2 Si.
Claim 17
Dependent Claim
22 words
A method for manufacturing a semiconductor device according to claim 10, wherein the barrier metal is one of Ni, Pt and Pd.
Claim 18
Dependent Claim
23 words
A method for manufacturing a semiconductor device according to claim 10, wherein the oxidation preventing metal is one of Au, Ag and Pt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-07 | 1996-12-07 | 1997-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-07 | 2000-12-07 | 2001-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-07 | 2004-12-07 | 2005-06-08 | $7700.00 | Window Closed / Lapsed |