Process for the production of a fine particle titanium dioxide

Claim 2

A process for producing fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, comprising the steps of preparing fine particle titanium dioxide, and adding fine particle tin dioxide having a particle size of 1 to 10 nm during preparation of the fine particle titanium dioxide, the tin dioxide being added in an amount of 0.5 to 10 weight percent with respect to the amount of titanium dioxide prepared.

Claim 3

The process according to claim 1, wherein the fine particle tin dioxide has a particle size of 1 to 4 nm.

Claim 4

The process according to claim 1, wherein the step of preparing the fine particle titanium dioxide comprises: a) slurrying a titanium dioxide hydrate with anatase structure prepared by the hydrolysis of a titanium sulphate solution in water to a concentration of 20 to 26 weight percent TiO 2 , b) heating the resulting titanium dioxide hydrate suspension to 60° to 70° C., c) adding the hot titanium dioxide hydrate suspension to aqueous sodium hydroxide solution at 90° to 100° C. while continually stirring, the amount of sodium hydroxide being such that after the addition of the titanium dioxide hydrate suspension the weight ratio of NaOH:TiO 2 in the mixture is 1.25 to 1.65, d) heating the mixture to boiling and holding it at the boiling point for 120 to 140 minutes, e) cooling the mixture to 50° to 60° C. and then filtering the mixture, f) washing the resulting filter cake until the SO 4 " content of the wash filtrate is less than 0.05 g 1 -1 , g) slurrying the washed filter cake in water to a TiO 2 concentration of 10 to 25 weight percent and adding hydrochloric acid containing 20 to 25 weight percent HCl to the resulting mixture until pH 2.8 to 3.1 is reached, h) heating the mixture to a temperature of 55° to 65° C. and holding the mixture at this temperature for 30 to 45 minutes while maintaining the pH in the range of 2.8 to 3.1, i) adding colloidal tin dioxide sol with a particle size of 1 to 10 nm to the mixture, j) peptizing the mixture containing the colloidal tin dioxide sol by the addition of hydrochloric acid containing 20 to 25 weight percent HCl while adding sufficient hydrochloric acid to give a weight ratio of HCl:TiO 2 from 0.15:1 to 0.25:1, k) heating the resulting suspension to boiling over a period of 30 to 45 minutes and holding it at the boiling point for 60 to 90 minutes, and l) neutralizing the suspension to a pH range of 4 to 11.

Claim 5

The process according to claim 3, wherein the fine particle tin dioxide has a particle size of 1 to 4 nm.

Claim 6

The process according to claim 4, where the suspension has a pH range of 6 to 8.

Claim 7

The process according to claim 1, wherein the step of preparing fine particle titanium dioxide comprises the hydrolysis of a tetravalent titanium compound under conditions which yield a rutile structure in the presence of tin dioxide with a particle size of 1-10 nm.

Claim 8

The process according to claim 6, wherein the fine particle tin dioxide has a particle size of 1 to 4 nm.

Claim 9

The process according to claim 6, wherein one of a titanium tetrachloride and a compound formed by the reaction of water with titanium tetrachloride is used as the tetravalent titanium compound.

Claim 10

The process according to claim 8, wherein the fine particle tin dioxide has a particle size of 1 to 4 nm.

Claim 11

The process according to claim 9, where the suspension has a pH range of 6 to 8.

Claim 12

The process according to claim 1, wherein the tin dioxide is used as a colloidal sol prepared by slow addition of tin tetrachloride to distilled water at a maximum temperature of 22° C. until a concentration of 180-220 g SnO 2 1 -1 is reached, diluting the solution to 10 g SnO 2 1 -1 with distilled water while ensuring that the temperature does not exceed 22° C., and aging the diluted solution for 1 hour at 20° to 22° C.

Claim 13

The process according to claim 11, wherein the step of preparing the fine particle titanium dioxide comprises: a) slurrying a titanium dioxide hydrate with anatase structure prepared by the hydrolysis of a titanium sulphate solution in water to a concentration of 20 to 26 weight percent TiO 2 , b) heating the resulting titanium dioxide hydrate suspension to 60° to 70° C., c) adding the hot titanium dioxide hydrate suspension to aqueous sodium hydroxide solution at 90° to 100° C. while continually stirring, the amount of sodium hydroxide being such that after the addition of the titanium dioxide hydrate suspension the weight ratio of NaOH:TiO 2 in the mixture is 1.25 to 1.65, d) heating the mixture to boiling and holding it at the boiling point for 120 to 140 minutes, e) cooling the mixture to 50° to 60° C. and then filtering the mixture, f) washing the resulting filter cake until the SO 4 " content of the wash filtrate is less than 0.05 g 1 -1 , g) slurrying the washed filter cake in water to a TiO 2 concentration of 10 to 25 weight percent and adding hydrochloric acid containing 20 to 25 weight percent HCl to the resulting mixture until pH 2.8 to 3.1 is reached, h) heating the mixture to a temperature of 55° to 65° C. and holding the mixture at this temperature for 30 to 45 minutes while maintaining the pH in the range of 2.8 to 3.1, i) adding colloidal tin dioxide sol with a particle size of 1 to 10 nm to the mixture, j) peptizing the mixture containing the colloidal tin dioxide sol by the addition of hydrochloric acid containing 20 to 25 weight percent HCl while adding sufficient hydrochloric acid to give a weight ratio of HCl:TiO 2 from 0.15:1 to 0.25:1, k) heating the resulting suspension to boiling over a period of 30 to 45 minutes, and holding it at the boiling point for 60 to 90 minutes and l) neutralizing the suspension to a pH range of 4 to 11.

Claim 14

The process according to claim 11, wherein the step of preparing fine particle titanium dioxide comprises the hydrolysis of a tetravalent titanium compound under conditions which yield a rutile structure in the presence of tin dioxide with a particle size of 1-10 nm.

Claim 15

The process according to claim 3, further comprising the step of separating the titanium dioxide produced from the liquid phase of the suspension by flocculation and filtration.

Claim 16

The process according to claim 14, further comprising the step of washing the separated titanium dioxide.

Claim 17

The process according to claim 14, further comprising the step of drying the separated titanium dioxide.

Claim 18

The process according to claim 16, further comprising the step of milling the dried titanium dioxide.

Claim 19

The process according to claim 17, further comprising the step, after neutralization of adding a conventional substance to prevent formation of hard agglomerates and before drying the titanium dioxide.

Claim 20

The process according to claim 17, further comprising the step of heat-treating the dried titanium dioxide at 300° to 800° C.

Claim 21

The process according to claim 19, wherein the step of heat-treating takes place at 400° to 600° C.

Claim 22

The process according to claim 1, further comprising the step of post-treating the titanium dioxide with at least one of inorganic and organic substances.

Claim 23

A fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of 10 to 100 nm long acicular particles with a rutile structure and a length:diameter ratio from 8:1 to 3.:1, wherein these particles contain 1 to 10 weight percent SnO 2 .

Claim 24

A fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of 10 to 100 nm long acicular particles with a rutile structure and a length:diameter ratio from 8:1 to 3.:1, wherein these particles contain 1 to 10 weight percent SnO 2 .

Claim 25

An aqueous suspension of fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of 10 to 100 nm long acicular particles with a rutile structure and a length:diameter ratio from 8:1 to 3.:1, wherein these particles contain 1 to 10 weight percent SnO 2 .

Claim 26

An aqueous suspension of fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of 10 to 100 nm long acicular particles with a rutile structure and a length:diameter ratio from 8:1 to 3.:1, wherein these particles contain 1 to 10 weight percent SnO 2 .

Claim 27

A fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of rounded particles with a rutile structure and a diameter of 10 to 100 nm which contain 0.5 to 10 weight percent SnO 2 .

Claim 28

A fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of rounded particles with a rutile structure and a diameter of 10 to 100 nm which contain 0.5 to 10 weight percent SnO 2 .

Claim 29

The fine particle titanium dioxide according to claim 13, wherein a coating of at least one of inorganic and organic substances is applied by post-treatment.

Claim 30

The fine particle titanium dioxide according to claim 24, wherein a coating of at least one of inorganic and organic substances is applied by post-treatment.

Claim 31

An aqueous suspension of fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of rounded particles with a rutile structure and a diameter of 10 to 100 nm which contain 0.5 to 10 weight percent SnO 2 and a coating of at least one of inorganic and organic substances applied by post-treatment.

Claim 32

An aqueous suspension of fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, consisting of rounded particles with a rutile structure and a diameter of 10 to 100 nm which contain 0.5 to 10 weight percent SnO 2 and a coating of at least one of inorganic and organic substances applied by post-treatment.

Claim 33

A fine particle titanium dioxide essentially transparent to visible light and essentially UV radiation absorbing, produced by the process of claim 1.