Method and apparatus for monitoring corrosion
Assignee: Purafil Inc
•
Filing: 1991-12-23
•
Granted: 1993-05-04
•
Expires: 2011-12-23
Abstract
Abstract A method and apparatus for using a coated piezoelectric crystal to monitor and report corrosion in terms recognized as conforming to an industry standard is disclosed. The present invention provides a method of and system for monitoring corrosion in a corrosive atmosphere, comprising and carrying out the steps of exciting in the atmosphere a crystal, coated with a corrodible metallic substance and having a known vibration frequency; measuring the change in the frequency of vibration resulting from corrosion of the corrodible substance during each of a plurality of intervals of time, including a reference interval and at least one subsequent measurement interval; generating a thickness signal representing the thickness of corrosion corresponding to the measured change in frequency during the measurement interval; and converting the corrosion thickness signal for the measurement interval to a reference signal representing the thickness of corrosion accumulated during the reference interval. The invention also preferably includes correcting the measured frequency change during each interval to account for any deviation in the temperature in the atmosphere from a preset standard temperature. The present invention also preferably includes a humidity sensor, which serves as the impetus for providing an alarm to the user if the relative humidity is above a preset limit, or if the relative humidity changes during an interval by more than a preset limit. A corrosion monitor according to the present invention finds application in such environments as industrial process measurement and control rooms, motor control centers, electrical rooms, semiconductor clean rooms, electronic fabrication sites, commercial data centers, museums, libraries, and archival storage rooms.
Inventors
- 👤 Michael W. Osborne
- 👤 William G. England
- 👤 Xiuyi Zhang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:20
CPC Classifications
G; G01; G01N; G01N17/00; G01N17/04
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
207 words
A method of monitoring corrosion in a corrosive atmosphere, comprising the steps of: exciting in the atmosphere a crystal, coated with a corrodible metallic substance and having a characteristic vibration frequency; obtaining an initial frequency measurement of said crystal at the time of initial exposure of said crystal to the atmosphere; periodically obtaining subsequent frequency measurements of said crystal at times after said initial frequency measurement; determining and monitoring the cumulative corrosion thickness built up on said crystal from the time of initial exposure to each of the times of said periodic subsequent frequency measurements; defining a measurement interval beginning at the time of one of said subsequent frequency measurements and ending at the time of another of said subsequent frequency measurements; and converting the frequency change from the beginning to the end of said measurement interval to a corrosion thickness signal corrected by a corrective value dependent on the cumulative corrosion built up on said crystal; said corrected corrosion thickness signal representing the corrosion thickness that would have resulted if, at the beginning of said measurement interval, a new, unexposed reactivity monitoring coupon prepared according to a reactivity monitoring standard had been used to monitor corrosion during said measurement interval, expressed in accordance with said standard.
Claim 2
Independent Claim
207 words
A method of monitoring corrosion in a corrosive atmosphere, comprising the steps of: exciting in the atmosphere a crystal, coated with a corrodible metallic substance and having a characteristic vibration frequency; obtaining an initial frequency measurement of said crystal at the time of initial exposure of said crystal to the atmosphere; periodically obtaining subsequent frequency measurements of said crystal at times after said initial frequency measurement; determining and monitoring the cumulative corrosion thickness built up on said crystal from the time of initial exposure to each of the times of said periodic subsequent frequency measurements; defining a measurement interval beginning at the time of one of said subsequent frequency measurements and ending at the time of another of said subsequent frequency measurements; and converting the frequency change from the beginning to the end of said measurement interval to a corrosion thickness signal corrected by a corrective value dependent on the cumulative corrosion built up on said crystal; said corrected corrosion thickness signal representing the corrosion thickness that would have resulted if, at the beginning of said measurement interval, a new, unexposed reactivity monitoring coupon prepared according to a reactivity monitoring standard had been used to monitor corrosion during said measurement interval, expressed in accordance with said standard.
Claim 3
Dependent Claim
38 words
The method of claim 1, wherein said coated crystal initially vibrates at about 6 MHz, and wherein said corrective value is about: 2-(1-(CC/4000)) where CC is said cumulative corrosion thickness value at the end of said measurement interval.
Claim 4
Dependent Claim
70 words
The method of any of claim 1, further comprising the steps of: monitoring the relative humidity in said corrosive atmosphere; and providing a warning signal indicating that corrosion in said atmosphere is related to humidity whenever said relative humidity exceeds a predetermined level or rises at greater than a predetermined rate, at the same time as said corrosion thickness signal for one of said measurement intervals exceeds a predetermined thickness.
Claim 5
Dependent Claim
19 words
The method of claim 1, wherein said reactivity monitoring standard follows substantially an ISA coupon procedure for monitoring corrosion.
Claim 6
Dependent Claim
23 words
The method of claim 1, further comprising the step of correcting said initial and subsequent frequency measurements to account for surrounding temperature variations.
Claim 7
Dependent Claim
95 words
The method of claim 5, wherein said step of converting the frequency change from the beginning to the end of said measurement interval to a corrosion thickness signal comprises generating an uncorrected incremental thickness signal prior to applying said corrective value, said incremental thickness signal being obtained by multiplying said temperature-corrected frequency measurements at the beginning and end of said measurement interval by a thickness conversion factor to obtain cumulative corrosion thickness values for the beginning and end of said measurement interval, and subtracting said cumulative corrosion thickness values to obtain said incremental thickness signal.
Claim 8
Dependent Claim
32 words
The method of claim 1, wherein said corrective value is determined by comparing frequency changes of said coated crystal with corrosion accumulated on reactivity monitoring coupons placed in a common test atmosphere.
Claim 9
Dependent Claim
16 words
The method of claim 7, further comprising the step of storing said corrected corrosion thickness signal.
Claim 10
Dependent Claim
16 words
The method of claim 8, further comprising the step of displaying said corrected corrosion thickness signal.
Claim 11
Dependent Claim
26 words
The method of claim 9, further comprising the steps of measuring and displaying an indicia of the temperature condition at which said frequency measurements are made.
Claim 12
Dependent Claim
22 words
The method of claim 10, wherein said corrodible substance is a metal selected from the group consisting of copper, silver, and nickel.
Claim 13
Independent Claim
215 words
An apparatus for monitoring corrosion in a corrosive atmosphere, comprising: means for exciting in the atmosphere a crystal, coated with a corrodible metallic substance and having a known vibration frequency; frequency measuring means for obtaining an initial frequency measurement of said crystal at the time of initial exposure of said crystal to the atmosphere, and for periodically obtaining subsequent frequency measurements of said crystal at times after said initial frequency measurement; converter means for: determining and monitoring the cumulative corrosion thickness built up on said crystal from the time of initial exposure to each of the times of said periodic subsequent frequency measurements; defining a measurement interval beginning at the time of one of said subsequent frequency measurements and ending at the time of another of said subsequent frequency measurements; and converting the frequency change from the beginning to the end of said measurement interval to a corrosion thickness signal corrected by a corrective value dependent on the cumulative corrosion built up on said crystal; said corrected corrosion thickness signal representing the corrosion thickness that would have resulted if, at the beginning of said measurement interval, a new, unexposed reactivity monitoring coupon prepared according to a reactivity monitoring standard had been used to monitor corrosion during said measurement interval, expressed in accordance with said standard.
Claim 14
Independent Claim
215 words
An apparatus for monitoring corrosion in a corrosive atmosphere, comprising: means for exciting in the atmosphere a crystal, coated with a corrodible metallic substance and having a known vibration frequency; frequency measuring means for obtaining an initial frequency measurement of said crystal at the time of initial exposure of said crystal to the atmosphere, and for periodically obtaining subsequent frequency measurements of said crystal at times after said initial frequency measurement; converter means for: determining and monitoring the cumulative corrosion thickness built up on said crystal from the time of initial exposure to each of the times of said periodic subsequent frequency measurements; defining a measurement interval beginning at the time of one of said subsequent frequency measurements and ending at the time of another of said subsequent frequency measurements; and converting the frequency change from the beginning to the end of said measurement interval to a corrosion thickness signal corrected by a corrective value dependent on the cumulative corrosion built up on said crystal; said corrected corrosion thickness signal representing the corrosion thickness that would have resulted if, at the beginning of said measurement interval, a new, unexposed reactivity monitoring coupon prepared according to a reactivity monitoring standard had been used to monitor corrosion during said measurement interval, expressed in accordance with said standard.
Claim 15
Dependent Claim
38 words
The apparatus of claim 12, wherein said coated crystal initially vibrates at about 6 MHz, and wherein said corrective value is about: 2-(1-(CC/4000)) where CC is said cumulative corrosion thickness value at the end of said measurement interval.
Claim 16
Dependent Claim
31 words
The apparatus of claim 12, further comprising a temperature sensor, and wherein said converter means includes means for correcting said initial and subsequent frequency measurements to account for surrounding temperature variations.
Claim 17
Dependent Claim
98 words
The apparatus of claim 14 wherein said converter means for converting the frequency change from the beginning to the end of said measurement interval to a corrosion thickness signal comprises means for generating an uncorrected incremental thickness signal prior to applying said corrective value, said incremental thickness signal being obtained by multiplying said temperature-corrected frequency measurements at the beginning and end of said measurement interval by a thickness conversion factor to obtain cumulative corrosion thickness values for the beginning and end of said measurement interval, and subtracting said cumulative corrosion thickness values to obtain said incremental thickness signal.
Claim 18
Dependent Claim
69 words
The apparatus of claim 12, further comprising: means for monitoring the relative humidity in said corrosive atmosphere; and means for providing a warning signal indicating that corrosion in said atmosphere is related to humidity whenever said relative humidity exceeds a predetermined level or rises at greater than a predetermined rate, at the same time as said corrosion thickness signal for one of said measurement intervals exceeds a predetermined thickness.
Claim 19
Dependent Claim
15 words
The apparatus of claim 16, further comprising means for storing said corrected corrosion thickness signal.
Claim 20
Dependent Claim
15 words
The apparatus of claim 17, further comprising means for displaying said corrected corrosion thickness signal.
Claim 21
Dependent Claim
25 words
The apparatus of claim 18, further comprising means for measuring and displaying an indicia of the temperature condition at which said frequency measurements are made.
Claim 22
Dependent Claim
22 words
The apparatus of claim 19, wherein said corrodible substance is a metal selected from the group consisting of copper, silver, and nickel.
Claim 23
Dependent Claim
14 words
The apparatus of claim 19, wherein said corrodible substance is a gold-coated corrodible metal.
References Cited (Backward Citations)
US3253219A
Cited
US4282181A
Cited
US4338563A
Cited
US4514681A
Cited
US4539846A
Cited
US4808538A
Cited
US4587479A
Cited
US4755744A
Cited
US4783987A
Cited
US4869874A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-03 | 1996-11-02 | 1997-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-03 | 2000-11-02 | 2001-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-03 | 2004-11-02 | 2005-05-04 | $7700.00 | Window Closed / Lapsed |