Process for preparing monoliths of aerogels of metal oxides
Assignee: Enichem SpA
•
Filing: 1991-10-08
•
Granted: 1993-05-04
•
Expires: 2011-10-08
Abstract
Abstract A process for the preparation of monoliths of aerogels of metal oxides, which aerogel is either constituted by one single oxide, or is constituted by a mixture of oxides, is disclosed, which process consists of the following operating steps: (a) the relevant metal alkoxide(s) is/are mixed with water in the presence of a catalyst of acidic character; (b) the so obtained mixture is hydrolysed; (c) a colloidal suspension of the oxide of a metal equal to, or different from, the metal(s) used in the (a) step is added to the hydrolysate; (d) the so obtained colloidal solution is caused to turn into a gel (gelation) having the desired shape and dimensions; (e) the gel is washed; (f) the gel is dried at values of temperature and pressure which are higher than the critical pressure and temperature values of the solvent used for the washing.
Inventors
- 👤 Guido Cogliati
- 👤 Giovanni Bezzi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:25
CPC Classifications
B; B01; B01J; B01J13/00; B01J13/0091; C; C01; C01B; C01B13/00; C01B13/14; C01B13/32; C01B33/00; C01B33/113; C01B33/12; C01B33/14; C01B33/157; C01B33/158; C01B33/1585; C03; C03C; C03C1/00; C03C1/006; C01P; C01P2006/00; C01P2006/10; C01P2006/12; C01P2006/14; C01P2006/16; C03C2203/00; C03C2203/20; C03C2203/34; Y; Y10; Y10S; Y10S65/00; Y10S65/90; Y10S65/901
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
130 words
Process for preparing monoliths of an aerogel of at least one oxide, which process comprises the following operating steps: (a) mixing an alkoxide of at least one metal with water in the presence of an acidic catalyst to form a mixture; (b) hydrolyzing the mixture obtained in step (a) to form a hydrolysate; (c) adding an oxide of at least one metal as a fine powder having a high specific surface area to the hydrolysate of step (b) to form a colloidal solution; (d) causing the colloidal solution of step (c) to become a gel; (e) washing the gel; (f) drying the gel at values of temperature and pressure which are higher than the critical pressure and temperature values of the solvent used for the washing to form said monolith.
Claim 2
Dependent Claim
130 words
Process for preparing monoliths of an aerogel of at least one oxide, which process comprises the following operating steps: (a) mixing an alkoxide of at least one metal with water in the presence of an acidic catalyst to form a mixture; (b) hydrolyzing the mixture obtained in step (a) to form a hydrolysate; (c) adding an oxide of at least one metal as a fine powder having a high specific surface area to the hydrolysate of step (b) to form a colloidal solution; (d) causing the colloidal solution of step (c) to become a gel; (e) washing the gel; (f) drying the gel at values of temperature and pressure which are higher than the critical pressure and temperature values of the solvent used for the washing to form said monolith.
Claim 3
Dependent Claim
26 words
Process for preparing aerogel monoliths according to the claim 1, in which the metal of step (a) is selected from among silicon, aluminum, zirconium and titanium.
Claim 4
Dependent Claim
15 words
Process for preparing aerogel monoliths according to claim 1, in which the metal is silicon.
Claim 5
Dependent Claim
31 words
Process for preparing aerogel monoliths according to claim 1, which in step (a) of claim 1 the alkoxide is preferably selected from the group consisting of tetramethoxy silane and tetraethoxy silane.
Claim 6
Dependent Claim
28 words
Process for preparing aerogel monoliths according to claim 1, in which the gelation of step (d) is carried out at a temperature between room temperature and 50° C.
Claim 7
Dependent Claim
28 words
Process for preparing aerogel an monoliths according to claim 1, in which the gel washing of step (e) is carried out by means of a chlorinated organic solvent.
Claim 8
Dependent Claim
20 words
Process for preparing aerogel monoliths according to claim 6, in which the gel washing is preferably carried out with 1,1,1-trichloroethylene.
Claim 9
Dependent Claim
160 words
Process for preparing a monolith of aerogel of at least one oxide, said process consisting essentially of: (a) mixing an alkoxide of at least one metal selected from the group consisting of silicon, aluminum, zirconium and titanium with a liquid which consists of water in the presence of an acidic catalyst to form a mixture; (b) hydrolyzing the mixture of step (a) to form a hydrolysate; (c) adding an oxide of a metal selected from the group consisting of silicon, aluminum, zirconium and titanium to the hydrolyzate of step (b), as a fine powder having a high surface area to form a colloidal solution; (d) causing the colloidal solution of step (c) to turn into a gel; (e) washing the gel of step (d) with a chlorinated solvent; and (f) drying the gel of step (e) at a temperature and pressure which are higher than the critical pressure and temperature of the solvent used for washing, to form said monolith.
Claim 10
Dependent Claim
160 words
Process for preparing a monolith of aerogel of at least one oxide, said process consisting essentially of: (a) mixing an alkoxide of at least one metal selected from the group consisting of silicon, aluminum, zirconium and titanium with a liquid which consists of water in the presence of an acidic catalyst to form a mixture; (b) hydrolyzing the mixture of step (a) to form a hydrolysate; (c) adding an oxide of a metal selected from the group consisting of silicon, aluminum, zirconium and titanium to the hydrolyzate of step (b), as a fine powder having a high surface area to form a colloidal solution; (d) causing the colloidal solution of step (c) to turn into a gel; (e) washing the gel of step (d) with a chlorinated solvent; and (f) drying the gel of step (e) at a temperature and pressure which are higher than the critical pressure and temperature of the solvent used for washing, to form said monolith.
Claim 11
Dependent Claim
11 words
A process defined in claim 8, wherein the metal is silicon.
Claim 12
Dependent Claim
12 words
A process as defined in claim 8, wherein the metal is aluminum.
Claim 13
Dependent Claim
12 words
A process as defined in claim 8, wherein the metal is zirconium.
Claim 14
Dependent Claim
12 words
A process as defined in claim 8, wherein the metal is titanium.
References Cited (Backward Citations)
EP0048099A1
Cited
EP0131057A1
Cited
US4801318A
Cited
US4574063A
Cited
JPS60103024A
Cited
EP0184255A1
Cited
US4806328A
Cited
EP0234816A2
Cited
US4680049A
Cited
JPH06302819A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-03 | 1996-11-02 | 1997-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-03 | 2000-11-02 | 2001-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-03 | 2004-11-02 | 2005-05-04 | $7700.00 | Window Closed / Lapsed |