Method and apparatus for fluxless solder bonding
Assignee: International Business Machines Corp
•
Filing: 1990-05-16
•
Granted: 1993-04-27
•
Expires: 2010-05-16
Abstract
Abstract Method and apparatus for fluxlessly solder bonding a solder mound to a solder wettable surface. A heated gas, preferably a reducing or non-reactive gas, is directed at a solid solder mound. Gas is heated to a temperature sufficient to melt solder mound. The heated gas is directed at the molten solder mound at a momentum sufficient to disperse an oxide layer at the surface of the molten solder mound. Dispersing the oxide layer permits the molten solder to wet the solder wettable surface. The molten solder is cooled to form a solder bond.
Inventors
- 👤 Harry R. Bickford
- 👤 Raymond R. Horton
- 👤 Ismail C. Noyan
- 👤 Michael J. Palmer
- 👤 John C. Zyzo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:28
CPC Classifications
H; H10; H10P; H10P72/00; H10P72/04; H10P72/0446; B; B23; B23K; B23K1/00; B23K1/012; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3494
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
107 words
A method for a fluxless solder bonding a solder mound to a wettable surface comprising: placing said solder mound against said solder wettable surface; directing at said solder mound a gas, said gas having a predetermined temperature and momentum, said temperature being sufficient to melt said mound to a molten mass, there being an oxide at the surface of said molten mass, said gas momentum at said oxide being sufficient to disperse said oxide on said surface permitting the nonoxidized molten solder to wet said solder wettable surface without requiring flux; and cooling said molten solder to solder bond said solder mound to said solder wettable surface.
Claim 2
Independent Claim
107 words
A method for a fluxless solder bonding a solder mound to a wettable surface comprising: placing said solder mound against said solder wettable surface; directing at said solder mound a gas, said gas having a predetermined temperature and momentum, said temperature being sufficient to melt said mound to a molten mass, there being an oxide at the surface of said molten mass, said gas momentum at said oxide being sufficient to disperse said oxide on said surface permitting the nonoxidized molten solder to wet said solder wettable surface without requiring flux; and cooling said molten solder to solder bond said solder mound to said solder wettable surface.
Claim 3
Dependent Claim
15 words
The method of claim 1, wherein said solder bonding is done in an oxidizing atmosphere.
Claim 4
Dependent Claim
34 words
The method of claim 1, wherein said heated gas is mixed prior to being directed at said solder mound to provide a temperature profile sufficient to provide substantially uniform melting of said solder mound.
Claim 5
Dependent Claim
25 words
The method of claim 1, wherein said gas is selected from the group consisting of an oxidizing gas, a reducing gas and a non-reactive gas.
Claim 6
Dependent Claim
10 words
The method of claim 1, wherein said gas contains hydrogen.
Claim 7
Dependent Claim
23 words
The method of claim 1, wherein said heated gas prior to being directed towards said solder mound is deflected into a prefered direction.
Claim 8
Dependent Claim
21 words
The method of claim 1, wherein said solder wettable surface is selected from the group consisting of gold, paladium and platinum.
Claim 9
Independent Claim
136 words
A method for fluxless solder bonding in an oxidizing atmosphere a solder mound to a surface solder wettable surface comprising: placing said solder mound against said solder wettable surface; directing at said solder mound a gas, said gas having a predetermined temperature and momentum, said temperature being sufficient to melt said mound to a molten mass, there being an oxide on the surface of said molten mass, said gas momentum at said oxide being sufficient to disperse said oxide on said surface permitting the nonoxidized molten solder to wet said solder wettable surface; said heated gas being mixed prior to being directed at said solder mound to provide temperature profile sufficient to provide substantially uniform melting of said solder mound; and cooling said molten solder to solder bond said solder mound to said solder wettable surface.
Claim 10
Independent Claim
136 words
A method for fluxless solder bonding in an oxidizing atmosphere a solder mound to a surface solder wettable surface comprising: placing said solder mound against said solder wettable surface; directing at said solder mound a gas, said gas having a predetermined temperature and momentum, said temperature being sufficient to melt said mound to a molten mass, there being an oxide on the surface of said molten mass, said gas momentum at said oxide being sufficient to disperse said oxide on said surface permitting the nonoxidized molten solder to wet said solder wettable surface; said heated gas being mixed prior to being directed at said solder mound to provide temperature profile sufficient to provide substantially uniform melting of said solder mound; and cooling said molten solder to solder bond said solder mound to said solder wettable surface.
Claim 11
Independent Claim
100 words
An apparatus for fluxless solder bonding a solder mound to a solder wettable surface comprising; means for holding said solder wettable surface against said solder mound; means for heating a gas to a temperature sufficient to melt said solder mound to a molten mass having an oxide on the surface thereof; means for directing said gas at said solder mound at a predetermined momentum of said oxide sufficient to disperse said oxide on the surface of said molten mass; and means for permitting said molten mass to cool to form a solder bond between said surface and said solder mound.
Claim 12
Independent Claim
100 words
An apparatus for fluxless solder bonding a solder mound to a solder wettable surface comprising; means for holding said solder wettable surface against said solder mound; means for heating a gas to a temperature sufficient to melt said solder mound to a molten mass having an oxide on the surface thereof; means for directing said gas at said solder mound at a predetermined momentum of said oxide sufficient to disperse said oxide on the surface of said molten mass; and means for permitting said molten mass to cool to form a solder bond between said surface and said solder mound.
Claim 13
Dependent Claim
14 words
The apparatus of claim 9, further including a means for mixing said heated gas.
Claim 14
Independent Claim
58 words
A method comprising: placing a molten solder mound with an oxide on the surface thereon against a solder wettable surface; and directing a gas at said molten solder mound, said gas having a predetermined momentum sufficient to disperse said oxide on said surface permitting said molten solder to wet said solder wettable surface in the absence of flux.
Claim 15
Independent Claim
58 words
A method comprising: placing a molten solder mound with an oxide on the surface thereon against a solder wettable surface; and directing a gas at said molten solder mound, said gas having a predetermined momentum sufficient to disperse said oxide on said surface permitting said molten solder to wet said solder wettable surface in the absence of flux.
Claim 16
Independent Claim
60 words
An apparatus comprising: means for holding a solder wettable surface against a molten solder mound having an oxide on the surface thereof; and means for directing a gas at said molten solder mound at a predetermined momentum sufficient to disperse said oxide on said surface permitting said molten solder to wet said solder wettable surface in the absence of flux.
Claim 17
Independent Claim
60 words
An apparatus comprising: means for holding a solder wettable surface against a molten solder mound having an oxide on the surface thereof; and means for directing a gas at said molten solder mound at a predetermined momentum sufficient to disperse said oxide on said surface permitting said molten solder to wet said solder wettable surface in the absence of flux.
References Cited (Backward Citations)
US4552300A
Cited
US4899920A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-04-26 | 1996-10-26 | 1997-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-04-26 | 2000-10-26 | 2001-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-04-26 | 2004-10-26 | 2005-04-27 | $7700.00 | Window Closed / Lapsed |