Method of making composite laminate parts combining resin transfer molding and a trapped expansion member
Assignee: Northrop Grumman Corp
•
Filing: 1990-08-03
•
Granted: 1993-04-20
•
Expires: 2010-08-03
Abstract
Abstract In a process for forming composite laminate parts from reinforcing fibers and resin, a mold is selected which has a mold cavity having a part definition surface therein and a resin passageway leading to the cavity. An expansion member capable of expanding to a larger volume in response to heat is located in the cavity in conjunction reinforcing fibers which will form a part of the composite laminate part. The mold cavity is closed and resin is injected through the resin passageway to saturate the fibers. The expansion member is heated to expand the expansion member an amount sufficient to consolidate the resin and the reinforcing fibers between the expansion member and the part definition surface to shape the fibers and the resin into a component laminate part mimicking the shape of the part definition surface and to expel any excess resin from the cavity to the passageway. The resin is then cured within the mold for a time sufficient for the consolidated fibers and resin to maintain the shape of the part definition surface.
Inventors
- 👤 Darryl G. James
- 👤 Aubrey G. Jackson, Jr.
- 👤 Stephen M. Novak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 00:11
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/44; B29C70/443; B29C43/00; B29C43/02; B29C43/10; B29C43/12; Y; Y10; Y10S; Y10S425/00; Y10S425/014; Y10S425/044
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
210 words
A resin transfer process for forming a composite part from dry reinforcing fibers and resin comprising: selecting a mold having a mold cavity, said mold having a resin passageway into said cavity, said cavity including a part definition surface for defining the shape of a composite part to be formed; selecting an expansion member made of a solid, thermally expandable elastomeric material capable of expanding to a larger volume in response to being heated; locating said expansion member in said mold cavity; locating reinforcing fibers in said mold cavity in association with said expansion member; closing said mold cavity; injecting resin into said closed mold cavity through said resin passageway to saturate said fibers; heating said expansion member to expand said expansion member an amount sufficient to consolidate said resin and said reinforcing fibers between said expansion member and said part definition surface to shape said fibers and said resin into a component part mimicking the shape of said part definition surface; curing said resin within said mold for a time sufficient for said consolidated fibers and resin to maintain the shape of said part definition surface; and cooling said mold, part, and said expansion member and removing said expansion member from said part and said part from said mold.
Claim 2
Dependent Claim
210 words
A resin transfer process for forming a composite part from dry reinforcing fibers and resin comprising: selecting a mold having a mold cavity, said mold having a resin passageway into said cavity, said cavity including a part definition surface for defining the shape of a composite part to be formed; selecting an expansion member made of a solid, thermally expandable elastomeric material capable of expanding to a larger volume in response to being heated; locating said expansion member in said mold cavity; locating reinforcing fibers in said mold cavity in association with said expansion member; closing said mold cavity; injecting resin into said closed mold cavity through said resin passageway to saturate said fibers; heating said expansion member to expand said expansion member an amount sufficient to consolidate said resin and said reinforcing fibers between said expansion member and said part definition surface to shape said fibers and said resin into a component part mimicking the shape of said part definition surface; curing said resin within said mold for a time sufficient for said consolidated fibers and resin to maintain the shape of said part definition surface; and cooling said mold, part, and said expansion member and removing said expansion member from said part and said part from said mold.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein said thermally expandable elastomeric member is silicone rubber.
Claim 4
Dependent Claim
80 words
The method of claim 1 including: selecting a plurality of identical elastomeric expansion members; and cycling said expansion members whereby when one of said plurality of elastomeric expansion members is located in said mold and is heated from said unexpanded state to said expanded state the remainder of said plurality of elastomeric expansion members are located external said mold; and cooling said remainder of said plurality of expansion members whereby they contract from said expanded state to said unexpanded state.
Claim 5
Dependent Claim
25 words
The method of claim 1 including: embedding a heating means for heating in said expansion member; and heating said expansion member with said heating means.
Claim 6
Dependent Claim
28 words
The method of claim 1 including: contacting a surface of said expansion member with a heating means for heating; and heating said expansion member with said heating means.
Claim 7
Dependent Claim
44 words
The method of claim 5 including: contacting said expansion member with said heating means at a surface distal from where said expansion member contacts said fibers and said resin during said consolidation of said resin and said reinforcing fibers against said part definition surface.
Claim 8
Dependent Claim
62 words
The method of claim 1 including: selecting said mold such that said mold cavity has at least two intersecting sections; and selecting said elastomeric expansion member such that it has a number of connected segments equal to the number of said intersecting sections of said mold cavity with each of said segments sized to fit within one of said mold cavity sections.
Claim 9
Dependent Claim
40 words
The method of claim 7 including: selecting said elastomeric expansion member such that the thickness of said member about one of its said connected segments is greater than the thickness of said member about a further of said connected segments.
Claim 10
Dependent Claim
56 words
The method of claim 8 including: selecting said mold such that the dimension about a first of said section of said mold cavity is greater than the dimension about a further of said sections; and positioning said first of said connected segments of said expansion member within said first of said section of said mold cavity.
Claim 11
Dependent Claim
66 words
The method of claim 9 including: sizing said expansion member such that ratio of the dimension of said first section of said mold cavity to the thickness of said first segment of said expansion member is greater than the ratio of the dimension of a further of said section of said mold cavity to the thickness of a further of said segments of said expansion member.
Claim 12
Dependent Claim
66 words
The method of claim 1 including: sizing said expansion member with respect to said mold cavity and selecting an amount of said reinforcing fiber such that when said mold cavity is closed prior to the injection of said resin into said closed mold cavity the combined volume of said expansion member and the volume of said reinforcing fiber is smaller than the volume of said cavity.
Claim 13
Dependent Claim
81 words
The method of claim 1 including: selecting said mold as a multiple element mold having at least two component parts with said part definition surface formed on one of said component parts and with a recess formed on the remainder, and wherein said component parts abut together and when abutted together said part definition surface and said recess forming said mold cavity; and expelling any excess resin from said cavity through said passageway in response to expansion of said expansion member.
Claim 14
Dependent Claim
34 words
The method of claim 12 including: selecting said mold such that the geometry of said recess includes at least one planar surface, said planar surface positioned so as to oppose said part definition surface.
Claim 15
Dependent Claim
14 words
The method of claim 1 including: selecting said reinforcing fibers as a fiber preform.
Claim 16
Dependent Claim
44 words
The method of claim 14 wherein: said fiber preform is selected from the group consisting of non-woven fiber mats, woven fiber fabrics, knitted fibers, stitched fibers, braided fibers, single layers of fibers, multiple layers of fibers and fibers adhered together with a sizing agent.
Claim 17
Dependent Claim
28 words
The method of claim 1 including: locating an amount of said reinforcing fibers in said cavity greater than 60 percent by weight of the weight of composite part.
Claim 18
Dependent Claim
30 words
The method of claim 16 including: locating an amount of said reinforcing fibers in said cavity essentially equal to about 75 percent by weight of the weight of composite part.
Claim 19
Dependent Claim
233 words
A resin transfer molding process for forming a composite part from dry reinforcing fibers and resin comprising: providing a mold having a mold cavity, said mold having a resin passageway into said cavity, said cavity including a part definition surface for defining the shape of a composite part to be formed; providing an expansion member made of solid elastomeric material capable of expanding to a larger volume in response to being heated; providing a resin injector located in operative association with said passageway; said passageway means serving to conduct resin from said resin injector to said cavity, locating said expansion member in said mold cavity; locating reinforcing fibers in said mold cavity in association with said expansion member; closing said mold cavity; injecting resin into said closed mold cavity through said resin passageway to saturate said fibers; heating said expansion member to expand said expansion member an amount sufficient to consolidate said resin and said reinforcing fibers between said expansion member and said part definition surface to shape said fibers and said resin into a component part mimicking the shape of said part definition surface; curing said resin within said mold for a time sufficient for said consolidated fibers and resin to maintain the shape of said part definition surface; and cooling said mold, part, and said expansion member and removing said expansion member from said part and said part from said mold.
Claim 20
Dependent Claim
233 words
A resin transfer molding process for forming a composite part from dry reinforcing fibers and resin comprising: providing a mold having a mold cavity, said mold having a resin passageway into said cavity, said cavity including a part definition surface for defining the shape of a composite part to be formed; providing an expansion member made of solid elastomeric material capable of expanding to a larger volume in response to being heated; providing a resin injector located in operative association with said passageway; said passageway means serving to conduct resin from said resin injector to said cavity, locating said expansion member in said mold cavity; locating reinforcing fibers in said mold cavity in association with said expansion member; closing said mold cavity; injecting resin into said closed mold cavity through said resin passageway to saturate said fibers; heating said expansion member to expand said expansion member an amount sufficient to consolidate said resin and said reinforcing fibers between said expansion member and said part definition surface to shape said fibers and said resin into a component part mimicking the shape of said part definition surface; curing said resin within said mold for a time sufficient for said consolidated fibers and resin to maintain the shape of said part definition surface; and cooling said mold, part, and said expansion member and removing said expansion member from said part and said part from said mold.
References Cited (Backward Citations)
US3165569A
Cited
US3264392A
Cited
US3704970A
Cited
US4123494A
Cited
US4167430A
Cited
US4271116A
Cited
US4473208A
Cited
US4492607A
Cited
US4624820A
Cited
US4683099A
Cited
US4702870A
Cited
US4704240A
Cited
US4986948A
Cited
US4808362A
Cited
US4762740A
Cited
US4911876A
Cited
US4889668A
Cited
US5061418A
Cited
US4880583A
Cited
US4952135A
Cited
US5041260A
Cited
US5087193A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-04-19 | 1996-10-19 | 1997-04-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-04-19 | 2000-10-19 | 2001-04-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-04-19 | 2004-10-19 | 2005-04-20 | $7700.00 | Window Closed / Lapsed |