Process for treating aluminum surfaces in a vacuum apparatus
Assignee: Applied Materials Inc
•
Filing: 1991-05-23
•
Granted: 1993-04-13
•
Expires: 2011-05-23
Abstract
Abstract A process is described for inhibiting the vaporization or sublimation of aluminum base alloy surfaces when exposed to temperatures in excess of 400° C. in a vacuum chamber used for the processing of semiconductor wafers. The process comprises treating such aluminum base alloy surfaces with a plasma comprising a nitrogen-containing gas selected from the group consisting of nitrogen and ammonia. When nitrogen gas is used, the plasma must also contain hydrogen gas. When the vacuum chamber being treated is intended to be used for the deposition of tungsten, the maximum flow of the nitrogen-containing gas into the chamber for the initial 10 seconds of the treatment process must be controlled to avoid impairment of the subsequent tungsten depositions in the chamber. After the treatment step, the cleaned and treated aluminum surface is preferably passivated with nitrogen (N 2 ) gas.
Inventors
- 👤 Mei Chang
- 👤 Ashok Sinha
- 👤 Turgut Sahin
- 👤 Alfred Mak
- 👤 Cissy Leung
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 22:55
CPC Classifications
C; C23; C23G; C23G5/00; C23C; C23C16/00; C23C16/44; C23C16/4401; C23C16/4404; H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10P; H10P14/00; H10P14/40; H10P14/42; H10P14/43; H10P95/00; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/056
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
87 words
A process for treatment of an aluminum surface in a vacuum chamber used for the processing of materials on a semiconductor wafer which comprises: a) flowing into said chamber one or more gases, including a nitrogen-containing gas, selected from the group consisting of: i) a mixture of nitrogen (N 2 ) and hydrogen (H 2 ); and ii) ammonia (NH 3 ); and b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen-containing gas into said chamber.
Claim 2
Dependent Claim
87 words
A process for treatment of an aluminum surface in a vacuum chamber used for the processing of materials on a semiconductor wafer which comprises: a) flowing into said chamber one or more gases, including a nitrogen-containing gas, selected from the group consisting of: i) a mixture of nitrogen (N 2 ) and hydrogen (H 2 ); and ii) ammonia (NH 3 ); and b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen-containing gas into said chamber.
Claim 3
Dependent Claim
38 words
The process of claim 1 wherein said nitrogen-containing gas is flowed into said chamber at a rate equivalent to a rate of at least about 20 scm flowing into a chamber having a volume of about 6 liters.
Claim 4
Dependent Claim
21 words
The process of claim 2 wherein said treatment process is carried out for a period of at least about 10 seconds.
Claim 5
Dependent Claim
28 words
The process of claim 2 wherein the pressure in said chamber is maintained within a range of from about 200 milliTorr to about 2 Torr during said treatment.
Claim 6
Dependent Claim
28 words
The process of claim 2 wherein the temperature in said chamber is maintained within a range of from about 150° C. to about 525° C. during said treatment.
Claim 7
Dependent Claim
44 words
The process of claim 2 wherein said plasma is maintained within said chamber at a power level during said treatment equivalent to a power level of from about 100 to about 400 watts in a vacuum chamber having a volume of about 6 liters.
Claim 8
Dependent Claim
53 words
The process of claim 2 wherein said nitrogen-containing gas comprises nitrogen (N 2 ) and hydrogen is also flowed into said chamber during said treatment at a rate within a range equivalent to the flow of from about 250 sccm to about 1000 sccm into a chamber having a volume of 6 liters.
Claim 9
Dependent Claim
61 words
The process of claim 2 wherein a passivation step is carried out for an additional time period of at least about 5 seconds after said treatment step by flowing only nitrogen (N 2 ) into said chamber at a flow rate equivalent to a rate of at least about 100 sccm flowing into a chamber having a volume of 6 liters.
Claim 10
Dependent Claim
103 words
The process of claim 2 wherein said vacuum chamber is used for the deposition of tungsten and said flow of nitrogen-containing gas into said chamber for at least the first 10 seconds of the treatment does not exceed a rate equivalent to the flow of about 30 sccm into a chamber having a volume of 6 liters when nitrogen (N 2 ) is the nitrogen-containing gas; and hydrogen (H 2 ) is also flowed into said chamber during said treatment, at a minimum rate equivalent to a rate of at least 50 sccm flowing into a chamber having a volume of 6 liters.
Claim 11
Dependent Claim
38 words
The process of claim 9 wherein the flow of said nitrogen (N 2 ) gas during any additional time period beyond said 10 second period may exceed said 30 sccm maximum of said initial 10 second treatment period.
Claim 12
Dependent Claim
65 words
The process of claim 2 wherein said vacuum chamber is used for the deposition of tungsten and said flow of nitrogen-containing gas into said chamber for at least the first 10 seconds of the treatment does not exceed a rate equivalent to the flow of 50 sccm into a chamber having a volume of 6 liters when ammonia (NH 3 ) is the nitrogen-containing gas.
Claim 13
Dependent Claim
35 words
The process of claim 11 wherein the flow of said ammonia gas during any additional time period beyond said 10 second period may exceed said 50 sccm maximum of said initial i0 second treatment period.
Claim 14
Dependent Claim
161 words
A process for treatment of aluminum surfaces in a vacuum chamber used for the processing of materials on a semiconductor wafer which treatment process comprises: a) flowing into said chamber one or more gases, including a nitrogen-containing gas, said one or more gases selected from the group consisting of: i) a mixture of nitrogen (N 2 ) and hydrogen (H 2 ); and ii) ammonia (NH 3 ) at a rate equivalent to a rate of at least about 20 sccm flowing into a chamber having a volume of about 6 liters. b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen-containing gas into said chamber at a power level during said treatment equivalent to a power level of from about 100 to about 400 watts in a vacuum chamber having a volume of about 6 liters; and c) maintaining said treatment for a period of at least about 10 seconds.
Claim 15
Dependent Claim
161 words
A process for treatment of aluminum surfaces in a vacuum chamber used for the processing of materials on a semiconductor wafer which treatment process comprises: a) flowing into said chamber one or more gases, including a nitrogen-containing gas, said one or more gases selected from the group consisting of: i) a mixture of nitrogen (N 2 ) and hydrogen (H 2 ); and ii) ammonia (NH 3 ) at a rate equivalent to a rate of at least about 20 sccm flowing into a chamber having a volume of about 6 liters. b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen-containing gas into said chamber at a power level during said treatment equivalent to a power level of from about 100 to about 400 watts in a vacuum chamber having a volume of about 6 liters; and c) maintaining said treatment for a period of at least about 10 seconds.
Claim 16
Dependent Claim
28 words
The process of claim 13 wherein the pressure in said chamber is maintained within a range of from about 200 milliTorr to about 2 Torr during said treatment.
Claim 17
Dependent Claim
28 words
The process of claim 13 wherein the pressure in said chamber is maintained within a range of from about 125° C. to about 525° C. during said treatment.
Claim 18
Dependent Claim
42 words
The process of claim 13 wherein a passivation step is carried out for a time period of at least about 5 seconds after said treatment step by flowing only nitrogen (N 2 ) gas into said chamber during said additional time period.
Claim 19
Dependent Claim
160 words
A process for treatment of aluminum surfaces in a vacuum chamber used for the deposition of tungsten on a semiconductor wafer, which treatment process comprises: a) flowing nitrogen (N 2 ) into said chamber at a rate equivalent to a rate not exceeding about 30 sccm flowing into a chamber having a volume of about 6 liters; b) flowing hydrogen (H 2 ) gas into said chamber at a minimum rate equivalent to a rate of at least about 50 sccm flowing into a chamber having a volume of 6 liters; c) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen gas into said chamber at a power level during said treatment equivalent to a power level of from about 100 to about 400 watts in a vacuum chamber having a volume of about 6 liters; and d) maintaining said treatment for a period of at least about 10 seconds.
Claim 20
Dependent Claim
160 words
A process for treatment of aluminum surfaces in a vacuum chamber used for the deposition of tungsten on a semiconductor wafer, which treatment process comprises: a) flowing nitrogen (N 2 ) into said chamber at a rate equivalent to a rate not exceeding about 30 sccm flowing into a chamber having a volume of about 6 liters; b) flowing hydrogen (H 2 ) gas into said chamber at a minimum rate equivalent to a rate of at least about 50 sccm flowing into a chamber having a volume of 6 liters; c) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen gas into said chamber at a power level during said treatment equivalent to a power level of from about 100 to about 400 watts in a vacuum chamber having a volume of about 6 liters; and d) maintaining said treatment for a period of at least about 10 seconds.
Claim 21
Dependent Claim
42 words
The process of claim 17 wherein a passivation step is carried out for a time period of at least about 5 seconds after said treatment step by flowing only nitrogen (N 2 ) gas into said chamber during said additional time period.
Claim 22
Dependent Claim
126 words
A process for treatment of aluminum surfaces in a vacuum chamber used for the deposition of tungsten on a semiconductor wafer, which treatment process comprises: a) flowing ammonia (NH 3 ) into said chamber at a rate equivalent to a rate not exceeding about 50 sccm flowing into a chamber having a volume of about 6 liters; b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said ammonia gas into said chamber at a power level during said treatment equivalent to a power level of from about 100 to about 400 watts in a vacuum chamber having a volume of about 6 liters; and c) maintaining said treatment for a period of at least about 10 seconds.
Claim 23
Dependent Claim
126 words
A process for treatment of aluminum surfaces in a vacuum chamber used for the deposition of tungsten on a semiconductor wafer, which treatment process comprises: a) flowing ammonia (NH 3 ) into said chamber at a rate equivalent to a rate not exceeding about 50 sccm flowing into a chamber having a volume of about 6 liters; b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said ammonia gas into said chamber at a power level during said treatment equivalent to a power level of from about 100 to about 400 watts in a vacuum chamber having a volume of about 6 liters; and c) maintaining said treatment for a period of at least about 10 seconds.
Claim 24
Dependent Claim
41 words
The process of claim 19 wherein a passivation step is carried out for a time period of at least about 5 seconds after said treatment step by flowing nitrogen (N 2 ) gas into said chamber during said additional time period.
Claim 25
Dependent Claim
72 words
A process for treatment of an aluminum surface into a vacuum chamber used for the processing of materials on a semiconductor wafer which comprises: a) flowing a nitrogen-containing gas selected from the group consisting of nitrogen (N 2 ) and ammonia (NH 3 ) into said chamber; and b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen-containing gas into said chamber.
Claim 26
Dependent Claim
72 words
A process for treatment of an aluminum surface into a vacuum chamber used for the processing of materials on a semiconductor wafer which comprises: a) flowing a nitrogen-containing gas selected from the group consisting of nitrogen (N 2 ) and ammonia (NH 3 ) into said chamber; and b) igniting a plasma in said chamber and maintaining said plasma in said chamber during said flow of said nitrogen-containing gas into said chamber.
References Cited (Backward Citations)
US4992136A
Cited
US4975147A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-04-12 | 1996-10-12 | 1997-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-04-12 | 2000-10-12 | 2001-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-04-12 | 2004-10-12 | 2005-04-13 | $7700.00 | Window Closed / Lapsed |