US5200231A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of manufacturing polycrystalline diamond layers
Assignee: US Philips Corp
•
Filing: 1992-01-10
•
Granted: 1993-04-06
•
Expires: 2012-01-10
Abstract
Abstract Method of manufacturing polycrystalline diamond layers, in which diamond crystallites are deposited by means of Chemical Vapour Deposition (CVD) on a substrate heated to a temperature ranging between 450° and 1200° C. from a gas phase comprising hydrogen and ≦30% of a carbon-containing gas at a pressure ranging between 10 -5 and 1 bar, in which method the substrate is contacted with a gas phase having an energy content which varies in time, such that at least at the start of the deposition process the substrate is in contact with a gas phase having an energy content which is suitable for nucleating diamond crystallites in the gas phase, whereafter the substrate is contacted with a gas phase having an energy content which is increased with respect to the content at the start of the process and further diamond crystallites are formed in situ on the substrate surface nucleated with diamond crystallites formed in the gas phase.
Inventors
- 👤 Peter K. Bachmann
- 👤 Hans Lydtin
- 👤 Arnd Ritz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:39
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/26; C23C16/27; C23C16/279; Y; Y10; Y10T; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
199 words
A method of manufacturing a layer of polycrystalline diamond on a substrate by a plasma induced chemical vapor deposition process comprising positioning a substrate in a reactor, heating said substrate to a temperature between 450° C.-1200° C., introducing a gas phase comprising hydrogen and ≦30% by volume of a carbon containing gas into said reactor at a pressure of between 10 -5 -1 bar so as to contact said heated substrate, coupling microwave energy at a frequency of 2.45 GHz into the reactor as the energy required for the deposition process, generating a pulsating plasma at the start of the deposition process by varying the power of the microwave energy coupled into the reactor between a low and a high power level of about 400 W and 1300 W respectively during a first period so as to cause diamond crystal nuclei to form from the gas phase and deposit on said substrate and, after said first period, adjusting the power of the microwave energy coupled into the reactor to a constant power level between said low and high power levels for a second period to thereby cause a layer of diamond crystallites to form on said diamond crystal nuclei.
Claim 2
Independent Claim
199 words
A method of manufacturing a layer of polycrystalline diamond on a substrate by a plasma induced chemical vapor deposition process comprising positioning a substrate in a reactor, heating said substrate to a temperature between 450° C.-1200° C., introducing a gas phase comprising hydrogen and ≦30% by volume of a carbon containing gas into said reactor at a pressure of between 10 -5 -1 bar so as to contact said heated substrate, coupling microwave energy at a frequency of 2.45 GHz into the reactor as the energy required for the deposition process, generating a pulsating plasma at the start of the deposition process by varying the power of the microwave energy coupled into the reactor between a low and a high power level of about 400 W and 1300 W respectively during a first period so as to cause diamond crystal nuclei to form from the gas phase and deposit on said substrate and, after said first period, adjusting the power of the microwave energy coupled into the reactor to a constant power level between said low and high power levels for a second period to thereby cause a layer of diamond crystallites to form on said diamond crystal nuclei.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein during the first period the power of the microwave energy coupled into the reactor is varied by a frequency variation of approximately 10 Hz.
Claim 4
Dependent Claim
17 words
A method as claimed in claim 1, characterized in that hydrocarbon gases containing methyl groups are used.
Claim 5
Independent Claim
193 words
A method of manufacturing a layer of polycrystalline diamond on a substrate by a plasma induced chemical vapor deposition process comprising positioning a substrate in a reactor, heating said substrate to a temperature between 450° C.-1200° C., introducing a gas phase comprising hydrogen and ≦30% by volume of a carbon containing gas into said reactor at a pressure of between 10 -5 -1 bar so as to contact said heated substrate, coupling microwave energy at a frequency of 2.45 GHz into the reactor as the energy required for the deposition process by generating a pulsating plasma at the start of the deposition process by varying the power of the microwave energy coupled into the reactor by a frequency variation of approximately 10 Hz between 400 and 1300 W during a first period so as to cause diamond crystal nuclei to form from the gas phase and deposit on said substrate and, after said first period, adjusting the power of the microwave energy coupled into the reactor to a constant value of approximately 1000 W for a second period to thereby cause a layer of diamond crystallites to form on said diamond crystal nuclei.
Claim 6
Independent Claim
193 words
A method of manufacturing a layer of polycrystalline diamond on a substrate by a plasma induced chemical vapor deposition process comprising positioning a substrate in a reactor, heating said substrate to a temperature between 450° C.-1200° C., introducing a gas phase comprising hydrogen and ≦30% by volume of a carbon containing gas into said reactor at a pressure of between 10 -5 -1 bar so as to contact said heated substrate, coupling microwave energy at a frequency of 2.45 GHz into the reactor as the energy required for the deposition process by generating a pulsating plasma at the start of the deposition process by varying the power of the microwave energy coupled into the reactor by a frequency variation of approximately 10 Hz between 400 and 1300 W during a first period so as to cause diamond crystal nuclei to form from the gas phase and deposit on said substrate and, after said first period, adjusting the power of the microwave energy coupled into the reactor to a constant value of approximately 1000 W for a second period to thereby cause a layer of diamond crystallites to form on said diamond crystal nuclei.
Claim 7
Dependent Claim
22 words
The method of claim 4 wherein the carbon gas is a hydrocarbon gas employed in the amount of about 0.5% by volume.
Claim 8
Dependent Claim
13 words
The method of claim 5 wherein the hydrocarbon gas contains a methyl group.
Claim 9
Dependent Claim
42 words
The method of claim 4 wherein the microwave power coupled into the reactor is kept at a constant value of approximately 1000 W for a period of approximately 900 minutes while the diamond crystallites are being formed on the diamond crystal nuclei.
Claim 10
Dependent Claim
17 words
A method as claimed in claim 4, characterized in that monocrystalline silicon discs are used as substrates.
Claim 11
Dependent Claim
24 words
A method as claimed in claim 1, characterized in that the pressure in the reactor is adjusted to a value of approximately 50 mbar.
Claim 12
Dependent Claim
17 words
A method as claimed in claim 6, characterized in that methane is used as a hydrocarbon gas.
References Cited (Backward Citations)
JPS60200898A
Cited
JPS62256795A
Cited
JPS6418991A
Cited
JPH01172294A
Cited
JPH01203293A
Cited
US4940015A
Cited
US4919974A
Cited
US5023109A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-04-05 | 1996-10-05 | 1997-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-04-05 | 2000-10-05 | 2001-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-04-05 | 2004-10-05 | 2005-04-06 | $7700.00 | Window Closed / Lapsed |