Assignee: NATION CENTER FOR MANFACTURING SCIENCES (NCMS) A NOT-FOR-PROFIT DELAWARE Corp
•
Filing: 1989-01-12
•
Granted: 1990-04-24
•
Expires: 2009-01-12
Abstract
Abstract Method of making a composite coated article by the steps of: (a) initiating chemical vapor deposition of separated diamond or diamond-like particles onto a nondiamond or nondiamond-like substrate surface by use of low pressure metastable deposition of carbon in the presence of atomic hydrogen and at a temperature (i.e., 600°-950° C.) that favors the nucleation of such particles, the substrate being selected to retain its strength related properties after said chemical vapor deposition (ie., SiAlON, Si 3 N 4 , SiC, Si, Ti, Co cemented WC, TiC, Ni-Mo cemented TiCN); (b) substantially suppressing nucleation of additional particles (heating to above about 1000° C.) before formation of a contiguous film of said particles while permitting the existing particles to grow to a predetermined maximum crystal size consistent with separated crystals; and (c) depositing a mechanically tough, diamond and substrate-wetting metal binding material (i.e., Ti, Ni, Co, Mn, Cr, Mo, Fe) onto and across said separaed particles and exposed substrate surface to form the composite coated article. Chemical vapor deposition comprises thermal decomposition (i.e., microwave plasma, discharge, filament heating) of a hydrocarbon gas containing hydrogen, with or without diamond seeding. The binding material preferably contains a brazing agent (i.e., Cu, Ag, Sn).
Inventors
- 👤 Robert C. McCune
- 👤 Ronald J. Baird
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 10:43
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/26; C23C16/27; C23C16/274; C22; C22C; C22C26/00; C23C16/278; C23C16/56; C22C2204/00; Y; Y10; Y10S; Y10S427/00; Y10S427/103
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
150 words
A method of making a composite coated article by the steps of: (a) initiating chemical vapor deposition of separated diamond or diamond-like particles onto a nondiamond or nondiamond-like substrate surface by use of low pressure metastable deposition of carbon in the presence of atomic hydrogen and at a temperature that favors the nucleation of such particles, the substrate being selected to facilitate such diamond or diamond-like deposition and to retain its strength related properties after said chemical vapor deposition; (b) substantially suppressing nucleation of additional particles before formation of a contiguous film of said particles while permitting the existing particles to grow to a predetermined maximum crystal size consistent with separated crystals; and (c) adhering a mechanically tough diamond and substrate-wetting, metal binding material onto and across said separated particles and exposed substrate surface to form the composite coated article with little or no graphitization or dissolution of said particles.
Claim 2
Independent Claim
150 words
A method of making a composite coated article by the steps of: (a) initiating chemical vapor deposition of separated diamond or diamond-like particles onto a nondiamond or nondiamond-like substrate surface by use of low pressure metastable deposition of carbon in the presence of atomic hydrogen and at a temperature that favors the nucleation of such particles, the substrate being selected to facilitate such diamond or diamond-like deposition and to retain its strength related properties after said chemical vapor deposition; (b) substantially suppressing nucleation of additional particles before formation of a contiguous film of said particles while permitting the existing particles to grow to a predetermined maximum crystal size consistent with separated crystals; and (c) adhering a mechanically tough diamond and substrate-wetting, metal binding material onto and across said separated particles and exposed substrate surface to form the composite coated article with little or no graphitization or dissolution of said particles.
Claim 3
Dependent Claim
45 words
The method as in claim 1, in which said chemical vapor deposition of step (a) comprises thermal decomposition of a hydrocarbon gas containing hydrogen, and step (c) comprises physical deposition at a substrate temperature that does not exceed 500° C. for longer than three minutes.
Claim 4
Dependent Claim
28 words
The method as in claim 1, in which said particles of step (a) are heterogeneously arranged as a result of diamond seeding to carry out chemical vapor deposition.
Claim 5
Dependent Claim
38 words
The method as in claim 1 in which said particles of step (a) are homogeneously arranged as a result of carburizing nucleation to carry out chemical vapor deposition, each nucleus comprising four-coordinated carbon atoms with sp 3 bonding.
Claim 6
Dependent Claim
15 words
The method as in claim 2, in which thermal decomposition is facilitated by filament heating.
Claim 7
Dependent Claim
15 words
The method as in claim 2, in which thermal decomposition is facilitated by plasma discharge.
Claim 8
Dependent Claim
30 words
The method as in claim 1, in which said temperature favoring nucleation is in the range of 600°-950° C. with said low pressure being in the range of 50-100 Torr.
Claim 9
Dependent Claim
16 words
The method as in claim 1, in which said binding material is a refractory carbide former.
Claim 10
Dependent Claim
14 words
The method as in claim 1, in which said article is a cutting tool.
Claim 11
Dependent Claim
28 words
The method as in claim 1, in which suppression of step (d) comprises raising the temperature of said substrate during chemical vapor deposition to at least 1000° C.
Claim 12
Dependent Claim
19 words
The method as in claim 1, in which said maximum crystal size of step (b) is about 10 microns.
Claim 13
Dependent Claim
29 words
The method as in claim 11, in which the density of the grown particles is generally limited to a density of about one particle per 100 μm 2 .
Claim 14
Dependent Claim
36 words
The method as in claim 1, in which said substrate is selected from the group consisting of Si 3 N 4 , SiAlON, SiC, Si, W, Ti, Co cemented WC, and TiC, Ni-Mo alloy cemented TiCN.
Claim 15
Dependent Claim
31 words
The method as in claim 1, in which said binding material is selected from the group consisting of Ti, Ni, Co, Mn, Cr, Mo, W, Zr, Ta, Si, Hf, and Fe.
Claim 16
Dependent Claim
23 words
The method as in claim 1, in which said binding material comprises an agent to make the material more brazeable at lower temperatures.
Claim 17
Dependent Claim
22 words
The method as in claim 15, in which said brazing agent is selected from the group consisting of Cu, Ag, and Sn.
Claim 18
Dependent Claim
20 words
The method as in claim 1, in which said binding material is an alloy selected from either Ti-Ni-Cu or Ni-Mn-Sn-Ti.
Claim 19
Dependent Claim
29 words
The method as in claim 1, in which said binding material is deposited by sputtering, vaporization, atomized powder metal, electrophoretic deposition, electrolytic solution deposition, or electroless metal solution deposition.
Claim 20
Dependent Claim
48 words
The method as in claim 1, in which the density of nucleation of step (a) is reduced by controlling the substrate temperature during CVD to the lower end of the temperature range of 600°-950° C. and/or by treating the surface of the substrate to have less defect sites.
Claim 21
Independent Claim
231 words
A method of making a diamond composite coated tool, comprising the steps of: (a) providing a tool substrate selected from materials that retain at least 90% of their strength related properties after exposure to processing temperatures up to 1050° C. for up to 20 hours; (b) initiating chemical vapor deposition of substantially separated single crystal diamond nucleation particles onto a surface of said substrate, said deposition being (i) by use of a low pressure surrounding gas containing about 1% by volume methane and the remainder essentially hydrogen, (ii) at a substrate temperature of 800°-950° C., and (iii) for a period of 2-4 hours; (c) substantially suppressing further. nucleation of additional particles before formation of a contiguous film of said particles by increasing the substrate temperature to a temperature of 1000° C. or greater for a period of 1-4 hours that permits the existing particles to grow to a crystal size consistent with said separation; (d) tooling said coated tool substrate-under vacuum to evolve hydrogen from the tool substrate; (e) depositing a mechanically tough, diamond and tool wetting material onto and across said separated particles and exposed substrate surface, said deposited material comprising an alloy selected from the group consisting of the alloy families of Ti-Ni-Cu and Ni-Mn-Sn-Ti; and (f) either during step (e) or thereafter, heating said deposited material to form a chemical and mechanical bond with diamond and tool substrate.
Claim 22
Independent Claim
231 words
A method of making a diamond composite coated tool, comprising the steps of: (a) providing a tool substrate selected from materials that retain at least 90% of their strength related properties after exposure to processing temperatures up to 1050° C. for up to 20 hours; (b) initiating chemical vapor deposition of substantially separated single crystal diamond nucleation particles onto a surface of said substrate, said deposition being (i) by use of a low pressure surrounding gas containing about 1% by volume methane and the remainder essentially hydrogen, (ii) at a substrate temperature of 800°-950° C., and (iii) for a period of 2-4 hours; (c) substantially suppressing further. nucleation of additional particles before formation of a contiguous film of said particles by increasing the substrate temperature to a temperature of 1000° C. or greater for a period of 1-4 hours that permits the existing particles to grow to a crystal size consistent with said separation; (d) tooling said coated tool substrate-under vacuum to evolve hydrogen from the tool substrate; (e) depositing a mechanically tough, diamond and tool wetting material onto and across said separated particles and exposed substrate surface, said deposited material comprising an alloy selected from the group consisting of the alloy families of Ti-Ni-Cu and Ni-Mn-Sn-Ti; and (f) either during step (e) or thereafter, heating said deposited material to form a chemical and mechanical bond with diamond and tool substrate.
Claim 23
Dependent Claim
15 words
The method as in claim 20, in which said substrate material is Ni-Mo cemented TiCN.
Claim 24
Dependent Claim
26 words
The method as in claim 20 in which said deposition is carried out by microwave plasma deposition at a deposition chamber pressure of about 50-100 Torr.
References Cited (Backward Citations)
US3517464A
Cited
US3639151A
Cited
US3961103A
Cited
US4260397A
Cited
US4505721A
Cited
US4766007A
Cited
US4707384A
Cited
US4825049A
Cited
US4752504A
Cited
US4849249A
Cited
US4756964A
Cited
US4761308A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-23 | 1993-10-23 | 1994-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-23 | 1997-10-23 | 1998-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-23 | 2001-10-23 | 2002-04-24 | $7700.00 | Window Closed / Lapsed |