Polyethylene composition
Assignee: Eneos Corp
•
Filing: 1991-12-30
•
Granted: 1993-02-23
•
Expires: 2011-12-30
Abstract
Abstract A polyethylene composition which has excellent flow characteristics and mechanical properties, especially low temperature mechanical properties as well as thermal stability, elasticity and workability for molding. The polyethylene composition comprises 20 to 80 wt. % of an ethylene- alpha -olefin copolymer of higher molecular weight having (a) intrinsic viscosity ( eta 1) of 1.2 to 9.0 dl/g, (b) density (d1) of 0.890 to 0.935 g/cm3 (c) a specific areal ratio calculated with an elution temperature-eluate volume curve in elution fractionation, and (d) a specific quantity of the content which is soluble in 25 DEG C. o-dichlorobenzene, and 80 to 20 wt. % of ethylene homopolymer or ethylene- alpha -olefin copolymer of lower molecular weight having (e) intrinsic viscosity ( eta 2) of 0.2 to 1.6 dl/g, (f) density (d2) of 0.890 to 0.980 g/cm3 and, wherein the above ( eta 1) is larger than ( eta 2), and the prepared composition has an intrinsic viscosity ( eta ) of 0.77 to 5.2 dl/g, a density (d) of 0.890 to 0.950 g/cm3 and a specific N-value of 1.7 to 3.5.
Inventors
- 👤 Toshifumi Morimoto
- 👤 Takaaki Hattori
- 👤 Noboru Ikegami
- 👤 Hirofumi Nishibu
- 👤 Toshiyuki Miyauchi
- 👤 Kunimichi Kubo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:01
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0807; C08L23/0815; C08L2205/00; C08L2205/02
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
295 words
A polyethylene composition which comprises: (I) 20 to 80 wt. % of a copolymer of ethylene and α-olefins having 3 to 18 carbon atoms, which copolymer meets the following conditions (a) to (d): (a) intrinsic viscosity (η 1 ) 1.2 to 9.0 dl/g (b) density (d 1 ): 0.890 to 0.935 g/cm 3 (c) in the elution temperature-eluate volume curve in continuously temperature rising elution fractionation, the ratio S (Ib/Ia) of the area Ib under the curve of elution temperature of 25° to 90° C. to the area Ia under the curve of elution temperature of 90° C. and above, is not larger than the value S 1 which is calculated with the following equation, S.sub.1 =20 η.sub.1.sup.-1 exp [-50(d.sub.1 -0.900)] (d) the quantity W wt. % of the content which is soluble in 25° C. o-dichlorobenzene is not smaller than the value W 1 which is calculated with the following equation, W.sub.1 =20 exp (-η.sub.1) and (II) 80 to 20 wt. % of ethylene homopolymer and/or the copolymer of ethylene and α-olefins having 3 to 18 carbon atoms, which meet the following conditions (e) and (f), (e) intrinsic viscosity (η 2 ): 0.2 to 1.6 dl/g (f) density (d 2 ): 0.890 to 0.980 g/cm 3 the value (η 1 ) is larger than (η 2 ), and the intrinsic viscosity (η) of the composition is 0.77 to 5.2 dl/g, the density (d) thereof is 0.890 to 0.950 g/cm 3 and the N-value calculated with the following equation is 1.7 to 3.5. ##EQU3## wherein "γ" is an apparent shear rate (sec -1 at 170° C.) and "τ" is an apparent shear stress (dyne/cm 2 at 170° C.) and the subscripts "20" and "150" indicates loads of 20 kg/cm 2 and 150 kg/cm 2 .
Claim 2
Dependent Claim
295 words
A polyethylene composition which comprises: (I) 20 to 80 wt. % of a copolymer of ethylene and α-olefins having 3 to 18 carbon atoms, which copolymer meets the following conditions (a) to (d): (a) intrinsic viscosity (η 1 ) 1.2 to 9.0 dl/g (b) density (d 1 ): 0.890 to 0.935 g/cm 3 (c) in the elution temperature-eluate volume curve in continuously temperature rising elution fractionation, the ratio S (Ib/Ia) of the area Ib under the curve of elution temperature of 25° to 90° C. to the area Ia under the curve of elution temperature of 90° C. and above, is not larger than the value S 1 which is calculated with the following equation, S.sub.1 =20 η.sub.1.sup.-1 exp [-50(d.sub.1 -0.900)] (d) the quantity W wt. % of the content which is soluble in 25° C. o-dichlorobenzene is not smaller than the value W 1 which is calculated with the following equation, W.sub.1 =20 exp (-η.sub.1) and (II) 80 to 20 wt. % of ethylene homopolymer and/or the copolymer of ethylene and α-olefins having 3 to 18 carbon atoms, which meet the following conditions (e) and (f), (e) intrinsic viscosity (η 2 ): 0.2 to 1.6 dl/g (f) density (d 2 ): 0.890 to 0.980 g/cm 3 the value (η 1 ) is larger than (η 2 ), and the intrinsic viscosity (η) of the composition is 0.77 to 5.2 dl/g, the density (d) thereof is 0.890 to 0.950 g/cm 3 and the N-value calculated with the following equation is 1.7 to 3.5. ##EQU3## wherein "γ" is an apparent shear rate (sec -1 at 170° C.) and "τ" is an apparent shear stress (dyne/cm 2 at 170° C.) and the subscripts "20" and "150" indicates loads of 20 kg/cm 2 and 150 kg/cm 2 .
Claim 3
Dependent Claim
44 words
The polyethylene composition as claimed in claim 1, wherein the α-olefin used for preparing said ethylene-α-olefin copolymer as said higher molecular weight component (I) is at least one member selected from the group consisting of 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 1-heptene, 1-octene, 1-nonene and 1-decene.
Claim 4
Dependent Claim
18 words
The polyethylene composition as claimed in claim 1, wherein said lower molecular weight component (II) is ethylene homopolymer.
Claim 5
Dependent Claim
40 words
The polyethylene composition as claimed in claim 1, wherein said lower molecular weight component (II) is a copolymer of ethylene and at least an α-olefin selected from the group consisting of 1-butene, 1-pentene, 1-hexene, 4-methyl-1-pentene, 1-heptene, 1-octene, 1-nonene and 1-decene.
Claim 6
Dependent Claim
26 words
The polyethylene composition as claimed in claim 1 or 4, wherein said lower molecular weight component (II) is a mixture of ethylene homopolymer and ethylene-α-olefin copolymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-02-23 | 1996-08-24 | 1997-02-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-02-23 | 2000-08-24 | 2001-02-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-02-23 | 2004-08-24 | 2005-02-23 | $7700.00 | Window Closed / Lapsed |