Fabricating crosslinked polyimide high temperature composites and resins
Assignee: RTX Corp
•
Filing: 1991-07-29
•
Granted: 1993-01-12
•
Expires: 2011-07-29
Abstract
Abstract A polyimide resin or composite may be pretreated by heating a reaction mixture that initially includes an aromatic diamine monomer, an end cap monomer, and an aromatic dianhydride monomer to a temperature between about 250° C. and about 300° C. for a period sufficient to completely imidize the reaction mixture to an imide resin without substantial crosslinking. A crosslinked reinforced polyimide composite article may be fabricated by heating a plurality of prepregs to a first temperature between about 250° C. and about 300° C. for a first period sufficient to completely imidize the prepreg without substantial crosslinking. Each prepreg has a plurality of reinforcing fibers and a reaction mixture. The prepregs are stacked in a desired orientation to form a laminated structure before or after heating to the first temperature and further heated at a superatmospheric pressure to a second temperature for a second period to form a crosslinked reinforced polyimide composite article by consolidating the prepregs and crosslinking the imide resin in the prepreg.
Inventors
- 👤 Daniel A. Scola
- 👤 John H. Vontell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:14
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/24; C08J5/241; C08J5/243; C08J2379/00; C08J2379/04; C08J2379/08; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31721
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
133 words
A method for fabricating a crosslinked reinforced polyimide composite article, comprising: (a) heating a plurality of prepregs to a first temperature between about 25° C. and about 300° C. for a first period sufficient to completely imidize the prepregs without substantial crosslinking, wherein each prepreg comprises a plurality of reinforcing fibers and a reaction mixture that initially comprises an aromatic diamine monomer, an end cap monomer, and an aromatic dianhydride monomer; (b) stacking the prepregs in a desired orientation to form a laminated structure; (c) heating the stacked prepregs at a superatmospheric pressure to a second temperature for a second period to form a crosslinked reinforced polyimide composite article by consolidating the prepregs and crosslinking the imide resins in the prepreg; whereby the composite article has less than about 2 vol. % voids.
Claim 2
Independent Claim
133 words
A method for fabricating a crosslinked reinforced polyimide composite article, comprising: (a) heating a plurality of prepregs to a first temperature between about 25° C. and about 300° C. for a first period sufficient to completely imidize the prepregs without substantial crosslinking, wherein each prepreg comprises a plurality of reinforcing fibers and a reaction mixture that initially comprises an aromatic diamine monomer, an end cap monomer, and an aromatic dianhydride monomer; (b) stacking the prepregs in a desired orientation to form a laminated structure; (c) heating the stacked prepregs at a superatmospheric pressure to a second temperature for a second period to form a crosslinked reinforced polyimide composite article by consolidating the prepregs and crosslinking the imide resins in the prepreg; whereby the composite article has less than about 2 vol. % voids.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein the reaction mixture comprises 1,4'-phenylene diamine, the monomethylester of 5-norbornene-2,3-dicarboxylic acid, and the dimethylester of 4,4'-hexafluoroisopropylidene biphthalic acid.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the prepregs are heated to the first temperature at atmospheric pressure.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein the first period is between about 30 minutes and about 120 minutes.
Claim 6
Dependent Claim
31 words
The method of claim 1 wherein the second temperature is between about 290° C. and about 320° C. and the second period is between about 1 hr and about 2 hr.
Claim 7
Dependent Claim
54 words
The method of claim 1 further comprising: (d) heating the crosslinked reinforced polyimide composite to a temperature between about 320° C. and about 400° C. for about 8 hr to about 24 hr to form a postcured crosslinked reinforced polyimide composite article; whereby the composite article has less than about 2 vol. % voids.
Claim 8
Dependent Claim
13 words
The method of claim 1 wherein step (a) is performed before step (b).
Claim 9
Dependent Claim
13 words
The method of claim 1 wherein step (b) is performed before step (a).
Claim 10
Dependent Claim
28 words
The method of claim 1 wherein the first temperature is between about 275° C. and about 300° C. and the first period is about 30 min or less.
Claim 11
Dependent Claim
14 words
A crosslinked reinforced polyimide composite article made according to the method of claim 1.
Claim 12
Independent Claim
96 words
A method for pretreating a polyimide resin or composite including heating a reaction mixture that initially comprises an aromatic diamine monomer, an end cap monomer, and an aromatic dianhydride monomer to an elevated temperature, wherein the improvement comprises: heating the reaction mixture to a temperature between about 250° C. and about 300° C. for a period sufficient to completely imidize the reaction mixture to an imide resin without substantial crosslinking, wherein the imide resin is capable of being further processed into a crosslinked polyimide resin or composite article having less than about 2 vol. % voids.
Claim 13
Independent Claim
96 words
A method for pretreating a polyimide resin or composite including heating a reaction mixture that initially comprises an aromatic diamine monomer, an end cap monomer, and an aromatic dianhydride monomer to an elevated temperature, wherein the improvement comprises: heating the reaction mixture to a temperature between about 250° C. and about 300° C. for a period sufficient to completely imidize the reaction mixture to an imide resin without substantial crosslinking, wherein the imide resin is capable of being further processed into a crosslinked polyimide resin or composite article having less than about 2 vol. % voids.
Claim 14
Dependent Claim
63 words
The method of claim 11 wherein the aromatic diamine monomer is selected from the group consisting of 1,4'-phenylene diamine and ##STR10## where Y is SO 2 , O, S, SO, NH, C═O, SiH 2 , Se, CH 2 , ##STR11## NR 3 and R 3 is an alkyl or aryl radical and R' is an alkyl or aryl radical or CF 3 .
Claim 15
Dependent Claim
39 words
The method of claim 11 wherein the end cap monomer is selected from the group consisting of the monomethylester of 5-norbornene-2,3-dicarboxylic acid, the monomethylester of itaconic acid, the monoethylester of 2,5-bicycle (2.2.1)-heptadiene-2,3-dicarboxylic acid, and the monoethylester of maleic acid.
Claim 16
Dependent Claim
26 words
The method of claim 11 wherein the aromatic dianhydride monomer is the diethyl ester of 4,4'-hexafluoroisopropylidene biphthalic acid or the dimentylester of 4,4'-(2,2,2-trifluoro-1-phenylethylidene) biphthalic tetracarboxylic acid.
Claim 17
Dependent Claim
25 words
The method of claim 11 wherein the reaction mixture comprises 1,4'-phenylene diamine, the monomethylester of 5-norbornene-2,3-dicarboxylic acid, and the dimethyl diester of 4,4'-hexafluoroisopropylidene biphthalic acid.
Claim 18
Dependent Claim
19 words
The method of claim 11 wherein the reaction mixture is heated for about 30 minutes to about 120 minutes.
Claim 19
Dependent Claim
14 words
The method of claim 11 wherein the reaction mixture is heated at atmospheric pressure.
Claim 20
Dependent Claim
28 words
The method of claim 11 wherein the reaction mixture is heated to a temperature between about 275° C. and about 300° C. for about 30 min or less.
References Cited (Backward Citations)
US3925587A
Cited
US4197339A
Cited
US4576857A
Cited
US4600769A
Cited
US4579782A
Cited
US4765942A
Cited
US4898754A
Cited
US4769197A
Cited
US4877653A
Cited
US5104474A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-01-12 | 1996-07-13 | 1997-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-01-12 | 2000-07-13 | 2001-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-01-12 | 2004-07-13 | 2005-01-12 | $7700.00 | Window Closed / Lapsed |