Conductive polymer compositions having improved properties under electrical stress

Claim 2

A conductive polymer composition which has a resistivity at 23° C. of less than 10 6 ohm-cm and which comprises (1) an organic polymer component which is present in amount 20 to 91% by volume of the composition; (2) a conductive filler component which consists essentially of carbon black or graphite or a mixture of carbon black and graphite, which has been dispersed in said polymer component and which is present in amount 4 to 65% by volume of the composition; and (3) an arc-controlling additive which is a particulate material and which has been dispersed in said polymer component.

Claim 3

A composition according to claim 1 wherein said arc-controlling additive is present in amount 10 to 35% by volume of the composition.

Claim 4

A composition according to claim 1 wherein said arc-controlling additive is an inorganic material.

Claim 5

A composition according to claim 1 wherein said conductive filler and said arc-controlling additive have a total surface area of at least 1,800 m 2 per 100 cc. of said composition.

Claim 6

A composition which exhibits PTC behavior, which has a resistivity at 23° C. of less than 10 6 ohm-cm and which comprises (1) an organic polymer component which is present in amount 20 to 91% by volume of the composition; (2) a conductive filler component which consists essentially of carbon black or graphite or a mixture of carbon black and graphite, which has been dispersed in said polymer component and which is present in amount 4 to 65% by volume of the composition; and (3) an arc-controlling additive which is a particulate material and which has been dispersed in said polymer component.

Claim 7

A composition which exhibits PTC behavior, which has a resistivity at 23° C. of less than 10 6 ohm-cm and which comprises (1) an organic polymer component which is present in amount 20 to 91% by volume of the composition; (2) a conductive filler component which consists essentially of carbon black or graphite or a mixture of carbon black and graphite, which has been dispersed in said polymer component and which is present in amount 4 to 65% by volume of the composition; and (3) an arc-controlling additive which is a particulate material and which has been dispersed in said polymer component.

Claim 8

A composition according to claim 5 in which the conductive filler component comprises carbon black having a particle size, D, which is from 20 to 150 millimicrons and a surface area, S, in m 2 /g such that S/D is not more than 10.

Claim 9

A composition according to claim 6 which has a resistivity at 23° C. of less than 20 ohm.cm.

Claim 10

A composition according to claim 5 wherein the quantity ##EQU2## is less than 1.

Claim 11

A composition according to claim 5 wherein the polymer component has at least 10% crystallinity.

Claim 12

A composition according to claim 9 wherein the polymer component consists essentially of one or more crystalline polymers selected from polyolefins and copolymers of at least one olefin and at least one polar comonomer copolymerisable therewith.

Claim 13

A composition according to claim 5 wherein the polymer component comprises at least 75% by weight of polyethylene.

Claim 14

A composition according to claim 11 wherein the polymer component consists essentially of polyethylene.

Claim 15

A composition according to claim 10 which has been cross-linked to a gel fraction of at least 0.6.

Claim 16

An electrical device which comprises (A) a PTC element composed of a conductive polymer composition which exhibits PTC behavior, which has a resistivity at 23° C. of less than 10 6 ohm.cm, and which comprises (1) an organic polymer component which is present in amount 20 to 91% by volume of the composition and which has at least 10% crystallinity; (2) a conductive filler component which consists essentially of carbon black, which has been dispersed in said polymer component, and which is present in amount 4 to 65% by volume of the composition; and (3) an arc-controlling additive which is a particulate material and which has been dispersed in said polymer component and (B) at least two electrodes which can be connected to a source of electrical power and which when so connected cause current to flow through the PTC element.

Claim 17

An electrical device which comprises (A) a PTC element composed of a conductive polymer composition which exhibits PTC behavior, which has a resistivity at 23° C. of less than 10 6 ohm.cm, and which comprises (1) an organic polymer component which is present in amount 20 to 91% by volume of the composition and which has at least 10% crystallinity; (2) a conductive filler component which consists essentially of carbon black, which has been dispersed in said polymer component, and which is present in amount 4 to 65% by volume of the composition; and (3) an arc-controlling additive which is a particulate material and which has been dispersed in said polymer component and (B) at least two electrodes which can be connected to a source of electrical power and which when so connected cause current to flow through the PTC element.

Claim 18

A device according to claim 14 wherein the composition has been melt-extruded.

Claim 19

A device according to claim 14 wherein said arc-controlling additive is present in amount 10 to 35% by volume of the composition.

Claim 20

A device according to claim 14 in which the conductive filler component comprises carbon black having a particle size, D, which is from 20 to 150 millimicrons and a surface area, S, in m 2 /g such that S/D is not more than 10.

Claim 21

A device according to claim 17 wherein the conductive polymer has a resistivity at 23° C. of less than 20 ohm.cm., and wherein the quantity ##EQU3## is less than 1.

Claim 22

A device according to claim 18 wherein the polymer component consists essentially of one or more crystalline polymers selected from polyolefins and copolymers of at least one olefin and at least one polar comonomer copolymerisable therewith.

Claim 23

A device according to claim 14 wherein the conductive polymer has been cross-linked to a gel fraction of at least 0.6.