Planarization process for trench isolation in integrated circuit manufacture
Assignee: Hewlett Packard Development Co LP
•
Filing: 1991-06-28
•
Granted: 1992-12-29
•
Expires: 2011-06-28
Abstract
Abstract A method of planarizing the surface of a silicon wafer of the type employing trench isolation is disclosed where the trenches and active areas of wafer surface may be of varying widths. The trenches and active areas are covered with a conformal coating of silicon oxide, and, according to one embodiment, this coating is subjected to an etch to leave sidewall spacers of oxide at the sidewalls of the trenches, then a second conformal coating of oxide is applied. A first layer of photoresist is applied to the face and patterned to leave photoresist only in the wider trenches. According to another embodiment the remaining photoresist of the first layer is reflowed by a heat treatment to account for any misalignment or the like. A second layer of photoresist is applied, then etched back to the conformal coating on the active areas, leaving some resist in narrow trenches. A third layer of photoresist is applied and then the three layers of photoresist plus oxide are simultaneously etched back to the level of the tops of the active areas, leaving a substantially planar surface where there is a minimum of variation in height in the various areas of differing trench and active area widths.
Inventors
- 👤 Ching-Tai S. Wang
- 👤 Gregory J. Grula
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:34
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/06; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0143; H10W10/10; H10W10/17; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
305 words
A method of planarizing a face of a substrate or of a material deposited or grown on said substrate, comprising the steps of: etching trenches of various widths and of approximately equal depths in said face; forming a conformal coating of an insulator material on said face, coating the sidewalls of said trenches as well as flat surfaces in the trenches and between the trenches; etching said coating to leave sidewall spacers at the sidewalls of said trenches; forming a second conformal coating of the insulator material on said face, coating the spacers at said sidewalls of said trenches as well as flat surfaces in the trenches and between the trenches; depositing a first layer of photoresist over said second conformal coating and patterning said first layer of photoresist to leave said first layer of photoresist only in selected ones of said trenches, said selected ones having a width which is wider than other trenches of narrower width, the width of said selected ones leaving a substantial amount of the bottom of said selected ones not covered by said sidewall spacers after said step of etching said coating; said first layer having the top surface after said patterning at about the level of a top surface of said second conformal coating at said active areas; reflowing the remaining portions of said first layer of photoresist to fill any gaps at edges of said photoresist adjacent to the sidewalls; depositing a second layer of photoresist over said first layer of photoresist and over said second conformal coating; etching said second layer of photoresist to the level of the second conformal coating; depositing a third layer of photoresist; etching said layers of photoresist and said second conformal coating down to the level of tops of said flat areas between the trenches to leave a substantially planar surface.
Claim 2
Independent Claim
305 words
A method of planarizing a face of a substrate or of a material deposited or grown on said substrate, comprising the steps of: etching trenches of various widths and of approximately equal depths in said face; forming a conformal coating of an insulator material on said face, coating the sidewalls of said trenches as well as flat surfaces in the trenches and between the trenches; etching said coating to leave sidewall spacers at the sidewalls of said trenches; forming a second conformal coating of the insulator material on said face, coating the spacers at said sidewalls of said trenches as well as flat surfaces in the trenches and between the trenches; depositing a first layer of photoresist over said second conformal coating and patterning said first layer of photoresist to leave said first layer of photoresist only in selected ones of said trenches, said selected ones having a width which is wider than other trenches of narrower width, the width of said selected ones leaving a substantial amount of the bottom of said selected ones not covered by said sidewall spacers after said step of etching said coating; said first layer having the top surface after said patterning at about the level of a top surface of said second conformal coating at said active areas; reflowing the remaining portions of said first layer of photoresist to fill any gaps at edges of said photoresist adjacent to the sidewalls; depositing a second layer of photoresist over said first layer of photoresist and over said second conformal coating; etching said second layer of photoresist to the level of the second conformal coating; depositing a third layer of photoresist; etching said layers of photoresist and said second conformal coating down to the level of tops of said flat areas between the trenches to leave a substantially planar surface.
Claim 3
Dependent Claim
18 words
A method according to claim 1 wherein said substrate is silicon, and said insulator material is silicon oxide.
Claim 4
Dependent Claim
30 words
A method according to claim 2 wherein said step of etching trenches includes forming an etch mask of silicon nitride on said face in a pattern to define said trenches.
Claim 5
Dependent Claim
28 words
A method according to claim 3 wherein said step of etching said first, second and third layers of photoresist includes stopping on said etch mask of silicon nitride.
Claim 6
Independent Claim
333 words
A method of planarizing a face of a semiconductor body, comprising the steps of: etching trenches of various widths in said face to leave active areas of said face; forming a first conformal coating of insulator on said face, coating the sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; etching said coating to leave sidewall spacers at the edges of said trenches; forming a second conformal coating of said insulator on said face, coating the spacers at said sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; depositing a first layer of photoresist on said face over said second conformal coating and patterning said first layer to leave said layer only in first ones of said trenches, said first ones of said trenches being wider than certain other ones of said trenches, the width of said first ones leaving a substantial amount of the bottom of said first ones not covered by said sidewall spacers after said step of etching said coating; said first layer having a top surface after said patterning at about the level of the top surface of said second conformal coating at said active areas; reflowing said first layer of photoresist to fill any gaps at edges of said photoresist and to planarize the surface of said first layer of photoresist; depositing a second layer of photoresist over said face over said first layer of photoresist and over said second conformal coating; etching said second layer of photoresist to said second conformal coating to leave photoresist in said certain other ones of said trenches where said first layer is not present; depositing a third layer of photoresist on said face; etching said first, second and third layers of photoresist and said second conformal coating down to the level of tops of said active areas to leave a substantially planar surface for formation of devices in said active areas.
Claim 7
Independent Claim
333 words
A method of planarizing a face of a semiconductor body, comprising the steps of: etching trenches of various widths in said face to leave active areas of said face; forming a first conformal coating of insulator on said face, coating the sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; etching said coating to leave sidewall spacers at the edges of said trenches; forming a second conformal coating of said insulator on said face, coating the spacers at said sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; depositing a first layer of photoresist on said face over said second conformal coating and patterning said first layer to leave said layer only in first ones of said trenches, said first ones of said trenches being wider than certain other ones of said trenches, the width of said first ones leaving a substantial amount of the bottom of said first ones not covered by said sidewall spacers after said step of etching said coating; said first layer having a top surface after said patterning at about the level of the top surface of said second conformal coating at said active areas; reflowing said first layer of photoresist to fill any gaps at edges of said photoresist and to planarize the surface of said first layer of photoresist; depositing a second layer of photoresist over said face over said first layer of photoresist and over said second conformal coating; etching said second layer of photoresist to said second conformal coating to leave photoresist in said certain other ones of said trenches where said first layer is not present; depositing a third layer of photoresist on said face; etching said first, second and third layers of photoresist and said second conformal coating down to the level of tops of said active areas to leave a substantially planar surface for formation of devices in said active areas.
Claim 8
Dependent Claim
18 words
A method according to claim 5 wherein said semiconductor body is silicon, and said insulator is silicon oxide.
Claim 9
Dependent Claim
53 words
A method according to claim 6 wherein said step of etching trenches includes forming an etch mask of silicon nitride on said face in a pattern to define said trenches, and wherein said step of etching said first, second and third layers of photoresist includes stopping on said etch mask of silicon nitride.
Claim 10
Independent Claim
276 words
A method of planarizing a face of a semiconductor body, comprising the steps of: etching trenches of various widths in said face to leave active areas of said face; forming a conformal coating of silicon oxide on said face, coating the sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; depositing a first layer of photoresist on said face over said conformal coating and patterning said first layer to leave said layer only in first ones of said trenches, said first ones being wider than other ones of said trenches, the width of said first ones leaving a substantial amount of the bottom of said first ones not covered by said sidewall spacers after said step of etching said coating; said first layer having a top surface after said patterning being at about the level of the top surface of said conformal coating at said active areas; reflowing said first layer of photoresist to fill any gaps at edges of said photoresist and to planarize the surface of said first layer of photoresist; depositing a second layer of photoresist over said face over said first layer of photoresist and over said conformal coating; etching said second layer of photoresist to said conformal coating to leave photoresist in said other ones of said trenches where said first layer is not present; depositing a third layer of photoresist on said face; etching said first, second and third layers of photoresist and said conformal coating down to the level of tops of said active areas to leave a substantially planar surface for formation of devices in said active areas.
Claim 11
Independent Claim
276 words
A method of planarizing a face of a semiconductor body, comprising the steps of: etching trenches of various widths in said face to leave active areas of said face; forming a conformal coating of silicon oxide on said face, coating the sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; depositing a first layer of photoresist on said face over said conformal coating and patterning said first layer to leave said layer only in first ones of said trenches, said first ones being wider than other ones of said trenches, the width of said first ones leaving a substantial amount of the bottom of said first ones not covered by said sidewall spacers after said step of etching said coating; said first layer having a top surface after said patterning being at about the level of the top surface of said conformal coating at said active areas; reflowing said first layer of photoresist to fill any gaps at edges of said photoresist and to planarize the surface of said first layer of photoresist; depositing a second layer of photoresist over said face over said first layer of photoresist and over said conformal coating; etching said second layer of photoresist to said conformal coating to leave photoresist in said other ones of said trenches where said first layer is not present; depositing a third layer of photoresist on said face; etching said first, second and third layers of photoresist and said conformal coating down to the level of tops of said active areas to leave a substantially planar surface for formation of devices in said active areas.
Claim 12
Dependent Claim
12 words
A method according to claim 8 wherein said semiconductor body is silicon.
Claim 13
Dependent Claim
53 words
A method according to claim 9 wherein said step of etching trenches includes forming an etch mask of silicon nitride on said face in a pattern to define said trenches, and wherein said step of etching said first, second and third layers of photoresist includes stopping on said etch mask of silicon nitride.
Claim 14
Independent Claim
310 words
A method of planarizing a face of a semiconductor body, comprising the steps of: etching trenches of various widths in said face to leave active areas of said face; said trenches including first ones of a width which is wider than other ones of said trenches; forming a conformal coating of insulator on said face, coating the sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; etching said conformal coating to leave sidewall spacers at the edges of said trenches; the width of said first ones leaving a substantial amount of the bottom of said first ones not covered by said sidewall spacers after said step of etching said coating; forming a second conformal coating of insulator on said face, coating the spacers at said sidewalls of said trenches as well as any flat surfaces of the face in the trenches and between the trenches; depositing a first layer of photoresist on said face over said second conformal coating and patterning said first layer to leave said layer only in said first ones of said trenches; said first layer of photoresist having a top surface after said patterning being at about the level of the top surface of said second conformal coating at said active areas; depositing a second layer of photoresist over said face over said first layer of photoresist and over said conformal coating; etching said second layer of photoresist to said second conformal coating to leave photoresist in narrower ones of said trenches where said first layer is not present; depositing a third layer of photoresist on said face; etching said first, second and third layers of photoresist and said second conformal coating down to the level of tops of said active areas to leave a substantially planar surface for formation of devices in said active areas.
Claim 15
Independent Claim
310 words
A method of planarizing a face of a semiconductor body, comprising the steps of: etching trenches of various widths in said face to leave active areas of said face; said trenches including first ones of a width which is wider than other ones of said trenches; forming a conformal coating of insulator on said face, coating the sidewalls of said trenches as well as flat surfaces of the face in the trenches and between the trenches; etching said conformal coating to leave sidewall spacers at the edges of said trenches; the width of said first ones leaving a substantial amount of the bottom of said first ones not covered by said sidewall spacers after said step of etching said coating; forming a second conformal coating of insulator on said face, coating the spacers at said sidewalls of said trenches as well as any flat surfaces of the face in the trenches and between the trenches; depositing a first layer of photoresist on said face over said second conformal coating and patterning said first layer to leave said layer only in said first ones of said trenches; said first layer of photoresist having a top surface after said patterning being at about the level of the top surface of said second conformal coating at said active areas; depositing a second layer of photoresist over said face over said first layer of photoresist and over said conformal coating; etching said second layer of photoresist to said second conformal coating to leave photoresist in narrower ones of said trenches where said first layer is not present; depositing a third layer of photoresist on said face; etching said first, second and third layers of photoresist and said second conformal coating down to the level of tops of said active areas to leave a substantially planar surface for formation of devices in said active areas.
Claim 16
Dependent Claim
18 words
A method according to claim 11 wherein said semiconductor body is silicon, and said insulator is silicon oxide.
Claim 17
Dependent Claim
53 words
A method according to claim 12 wherein said step of etching trenches includes forming an etch mask of silicon nitride on said face in a pattern to define said trenches, and wherein said step of etching said first, second and third layers of photoresist includes stopping on said etch mask of silicon nitride.
Claim 18
Dependent Claim
36 words
A method according to claim 11 including the step of reflowing said first layer of photoresist to fill any gaps at edges of said photoresist and to planarize the surface of said first layer of photoresist.
References Cited (Backward Citations)
JPS57187951A
Cited
JPS58143548A
Cited
US4505025A
Cited
JPS6155939A
Cited
JPS63281441A
Cited
JPS6413727A
Cited
JPS6425433A
Cited
US5077234A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-12-29 | 1996-06-29 | 1996-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-12-29 | 2000-06-29 | 2000-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-12-29 | 2004-06-29 | 2004-12-29 | $7700.00 | Window Closed / Lapsed |