Method of application of a conforming mask to a printed circuit board
Assignee: Eternal Technology Corp
•
Filing: 1991-11-19
•
Granted: 1992-11-17
•
Expires: 2011-11-19
Abstract
Abstract A dry film for forming a solder mask includes a cover sheet, a photoimageable composition layer which is curable to form a solder mask and a top coat interposed between the cover sheet and the photoimageable composition layer which is selectively adherent to the photoimageable composition layer. The dry film is applied to a surface of a printed circuit board. With heat, vacuum and mechanical pressure, the photoimageable composition layer is laminated to the irregular surface of the printed circuit board, partially conforming the photoimageable composition layer to the contours thereof. Within about 60 seconds and with the photoimageable composition layer still heated, the cover sheet is peeled away, leaving the top coat as a protective covering over the photoimageable composition layer. Removal of the cover sheet allows the photoimageable composition layer to fully conform to the contours of the printed circuit board. Immediately thereafter, the circuit board is cooled to about ambient temperature or below. The photoimageable composition layer is exposed to patterned actinic radiation, developed, and cured to form a hard, permanent solder mask.
Inventors
- 👤 James J. Briguglio
- 👤 Leo Roos
- 👤 Clancy P. Crooks
- 👤 Samuel W. Shoemaker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:08
CPC Classifications
B; B32; B32B; B32B37/00; B32B37/02; B32B37/10; B32B37/1018; G; G03; G03F; G03F7/00; G03F7/004; G03F7/09; G03F7/092; G03F7/16; G03F7/161; H; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K3/281; B32B2457/00; B32B2457/08; H05K2203/00; H05K2203/06; H05K2203/066; H05K2203/068; H05K2203/08; H05K2203/085; H05K2203/11; H05K2203/1105; H05K3/0073; H05K3/0079
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
235 words
A method of forming a solder mask on the surface of a printed circuit board, said surface having raised areas, the method comprising: (A) providing a dry film comprising (1) a cover sheet, (2) a top coat on said cover sheet, (3) a layer of photoimageable composition on said top coat, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printer circuit board; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) applying said photoimageable composition layer to the surfaced of said printed circuit board; (C) laminating said photoimageable composition layer to the surface of said printed circuit board using heat, vacuum and mechanical pressure; (D) within about 60 seconds of completion of step (C), with said photoimageable composition layer still at elevated temperature, removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to the surface of said circuit board with said top coat covering and protecting the same; (E) exposing said photoimageable composition layer to patterned actinic radiation; (F) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (G) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 2
Independent Claim
235 words
A method of forming a solder mask on the surface of a printed circuit board, said surface having raised areas, the method comprising: (A) providing a dry film comprising (1) a cover sheet, (2) a top coat on said cover sheet, (3) a layer of photoimageable composition on said top coat, which photoimageable composition is curable after exposure and development to provide a hard, permanent solder mask overlying the printer circuit board; said top coat being selectively adherent to said photoimageable composition relative to its adherence to said cover sheet; (B) applying said photoimageable composition layer to the surfaced of said printed circuit board; (C) laminating said photoimageable composition layer to the surface of said printed circuit board using heat, vacuum and mechanical pressure; (D) within about 60 seconds of completion of step (C), with said photoimageable composition layer still at elevated temperature, removing said cover sheet from said top coat, leaving said photoimageable composition layer tacked to the surface of said circuit board with said top coat covering and protecting the same; (E) exposing said photoimageable composition layer to patterned actinic radiation; (F) developing said photoimageable composition to remove either exposed or unexposed portions from said printed circuit board, leaving either unexposed or exposed portions remaining on said printed circuit board; and (G) curing said remaining portions of said photoimageable composition layer to form a hard, permanent solder mask protecting said printed circuit board.
Claim 3
Dependent Claim
24 words
A method according to claim 1 wherein said lamination (C) is conducted at a temperature of between about 40° C. and about 100° C.
Claim 4
Dependent Claim
25 words
A method according to claim 1 wherein said lamination (C) is conducted at a temperature range of between about 55° C. and about 80° C.
Claim 5
Dependent Claim
38 words
A method according to claim 1 wherein immediately subsequent to step (D) and prior to step (E), said circuit board and said overlying photoimageable composition layer and said top coat are rapidly cooled to ambient temperature or below.
Claim 6
Dependent Claim
27 words
A method according to claim 4 wherein said photoimageable composition layer is cooled to about ambient temperatures or below within about 60 seconds after cover sheet removal.
Claim 7
Dependent Claim
23 words
A method according to claim 4 wherein immediately subsequent to said rapid cooling, said photoimageable composition layer is pressed with heated roll means.
Claim 8
Dependent Claim
21 words
A method according to claim 6 wherein said heated roll means are heated to between about 55° and about 75° C.
Claim 9
Dependent Claim
27 words
A method according to claim 1 wherein in step (D) said cover sheet is removed from said top coat within about 30 seconds subsequent to vacuum lamination.
Claim 10
Dependent Claim
31 words
A method according to claim 1 wherein in step (D) said cover sheet is removed from said top coat before said photoimageable composition layer has cooled more than about 10° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-17 | 1996-05-18 | 1996-11-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-17 | 2000-05-18 | 2000-11-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-17 | 2004-05-18 | 2004-11-17 | $7700.00 | Window Closed / Lapsed |