Apparatus and method of fabricating a monolithic solid oxide fuel cell

Claim 3

The method of claim 1, wherein said attaching step is further characterized by: roll milling said anode tape, said electrolyte tape, and said cathode tape within a two roll mill to bond the respective contacting surfaces together.

Claim 4

The method of claim 1, wherein said mixing step is further characterized by: selecting a cermet of cobalt or nickel metal with stabilized zirconia for said anode, strontium-doped lanthanum manganite for said cathode, yttria-stabilized zirconia for said electrolyte, and doped lanthanum chromite for said interconnect; and selecting said binder system for compatibility with said anode, cathode, electrolyte, and interconnect materials, said binder system including a binder and a plasticizer.

Claim 5

The method of claim 1, wherein said steps of forming said thin tapes and shaping said trilayer electrolyte tapes is further characterized by: fabricating said materials by a process selected from the methods consisting of roll milling, extruding, pressing and tape casting.

Claim 6

The method of claim 1, wherein said steps of forming said thin tapes and said step of attaching said anode and cathode tapes to said electrolyte are further characterized by: tape casting said electrolyte onto one of said anode and cathode tapes; and tape casting said other of said cathode and anode onto an opposite side of said electrolyte tape.

Claim 7

The method of claim 1, wherein said attaching step is further characterized by: wetting adjacent surfaces of said anode, electrolyte, and cathode tapes with a solution capable of at least partially dissolving said binder system of said tapes.

Claim 8

The method of claim 1, wherein said step of shaping said trilayer electrolyte tape to form said fuel and oxidant flow pathways is further characterized by: deforming the respective surfaces of said anode layer and said cathode layer of said trilayer electrolyte tape by displacing contiguous portions of said surfaces from the plane of the pre existing flat surface, leaving raised surface portions to form a ribbed, finned, or pillared anode and cathode surface configuration.

Claim 9

The method of claim 7, wherein said step of shaping said pathways is further characterized by: deforming said surfaces of said anode and cathode by a process selected from the group consisting of pressing, rolling, and cutting.

Claim 10

The method of claim 1, wherein said heating step is further characterized by: raising the temperature of said respective trilayer electrolyte elements and said interconnect elements by any one or a combination of heating processes selected from the group consisting of radiant, convective, and microwave heating.

Claim 11

The method of claim 1, wherein said heating step is further characterized by: raising the temperature of said trilayer electrolyte elements and said interconnect elements to a temperature sufficient to sinter the respective ceramic materials to at least 25% of the total material shrinkage resulting from sintering the ceramic materials to a desired final density.

Claim 12

The method of claim 1, wherein said heating step is further characterized by: raising the temperature of said trilayer electrolyte elements and said interconnect elements to a temperature sufficient to sinter the respective ceramic materials to at least 80% of the total material shrinkage resulting from sintering the ceramic materials to a desired final density.

Claim 13

The method of claim 1, wherein said heating step is further characterized by: raising the temperature of said trilayer electrolyte elements and said interconnect elements to a temperature sufficient to sinter the respective ceramic materials to a percentage of the desired final density for said respective materials such that subsequent heating and sintering of said stacked array will result in compatible shrinkage of all ceramic materials in said stacked array.

Claim 14

The method of claim 1, wherein said stacking step is further characterized by: wetting adjacent surfaces of said interconnect elements and said anode of said trilayer electrolyte elements with an anode bonding agent; and wetting adjacent surfaces of said interconnect elements and said cathode of said trilayer electrolyte elements with a cathode bonding agent.

Claim 15

The method of claim 13, wherein said anode and cathode bonding agents utilized in said stacking step are further characterized by: mixing powders of said anode ceramic material for said anode bonding agent, and said cathode ceramic material for said cathode bonding agent respectively, with a bonding material.

Claim 16

The method of claim 14, wherein said heating step is further characterized by: raising the temperature of said interconnect elements to a temperature sufficient to sinter the ceramic material to a percentage of the desired final density for said material such that said interconnect ceramic material will not diffuse into adjacent layers of said stacked array during subsequent heating and sintering of said stacked array.

Claim 17

The method of claim 14 wherein said bonding material further comprises: a binder selected from the group consisting of synthetic rubber, plastics, polyvinyl alcohol, polyvinyl butyryl resin, cellulose, and polymer systems which thermally decompose without cross linking; a plasticizer selected from the group consisting of butyl benzyl phthalate and solvents of the phthalate group; and a solvent, said ceramic materials, said binder, said plasticizer, and said solvent mixed together to form a viscous slurry.

Claim 18

The method of claim 14 wherein said bonding material further comprises: a ceramic paste material including at least one of the materials selected from the group consisting of ceramic cements, glass ceramics, an organo-metallic sol gel material, and zirconium oxide.

Claim 19

The method of claim 14 wherein said bonding material of said bonding agents further comprise: a binder, a plasticizer, and platinum.

Claim 20

The method of claim 1, wherein said processing step is further characterized by: raising the temperature of said stacked array by any one or a combination of heating processes selected from the group consisting of radiant, convective, and microwave heating.

Claim 21

The method of claim 1, wherein said processing step is further characterized by: raising the temperature of said stacked array to a temperature sufficient to sinter the respective ceramic materials to their desired final density.

Claim 22

The method of claim 1, wherein said step of shaping said pathways is further characterized by: deforming said trilayer electrolyte elements to a corrugated or backfolded configuration.

Claim 23

The method of constructing a fuel cell according to claim 1, further comprising the steps of: attaching sections of said anode tape onto one side of said interconnect tape; attaching sections of said cathode tape on an opposite side of said interconnect tape to form a trilayer interconnect tape; cutting said trilayer interconnect tape to form a plurality of trilayer interconnect elements; shaping sections of said trilayer electrolyte or interconnect elements into a desired configuration selected from the group consisting of corrugated and backfolded configurations; and stacking said shaped trilayer elements on the other of said trilayer elements prior to initially heating said stacked trilayer elements.

Claim 24

The method of claim 22, wherein said step of stacking said shaped trilayer element on the other of said trilayer elements is repeated to form a stack of up to ten pairs of trilayer elements.

Claim 27

The method of claim 24, wherein said mixing step is further characterized by: selecting a cermet of cobalt or nickel metal with stabilized zirconia for said anode, strontium-doped lanthanum manganite for said cathode, yttria-stabilized zirconia for said electrolyte, and lanthanum chromite doped with a compound selected from the group consisting of magnesium, calcium cobalt, and strontium, for said interconnect; and selecting said binder system for compatibility with said anode, cathode, electrolyte, and interconnect materials, said binder system including a binder selected from the group consisting of synthetic rubber, thermosetting plastics, polyvinyl alcohol, polyvinyl butyryl resin, and polymer systems which thermally decompose without cross linking, and a plasticizer selected from the group consisting of butyl benzyl phthalate and solvents of the phthalate group.

Claim 28

The method of claim 25, wherein said heating step and said processing step are further characterized by: raising the temperature of said ceramic materials by any one or a combination of heating processes selected from the group consisting of radiant, convective, and microwave heating.

Claim 31

The method of claim 27, further characterized by: selecting a cermet of cobalt or nickel metal with stabilized zirconia for said anode, strontium-doped lanthanum manganite for said cathode, yttria-stabilized zirconia for said electrolyte, and doped lanthanum chromite for said interconnect; selecting said binder system materials of said anode bonding agent and said cathode bonding agent for compatibility with said anode, cathode, electrolyte, and interconnect materials, said binder system materials including a binder selected from the group consisting of synthetic rubber, plastics, polyvinyl alcohol, polyvinyl butyryl resin, and polymer systems which thermally decompose without cross linking, and a plasticizer selected from the group consisting of butyl benzyl phthalate and solvents of the phthalate group; and selecting isopropyl alcohol for said solvent of said anode bonding agent and said cathode bonding agent.

Claim 32

The method of claim 27, further characterized by: configuring said plurality of trilayer electrolyte elements and said plurality of interconnect elements to include aligned integral fuel inlet, fuel outlet, oxidant inlet, and oxidant outlet manifolds at spaced apart locations; enclosing said fuel pathway extending along said anode of said plurality of electrolyte layers such that said fuel pathways extend from said fuel inlet manifold to said fuel outlet manifold; and enclosing said oxidant pathways extending along said cathode of said plurality of electrolyte layers such that said oxidant pathways extend from said oxidant inlet manifold to said oxidant outlet manifold.

Claim 35

The method according to claim 30 wherein said electrolyte trilayer elements are bonded to said interconnect trilayer elements sandwiching anode ceramic material between said electrolyte ceramic material and said interconnect ceramic material, said stacking step further comprising: wetting exposed cathode surfaces of said cell elements with a cathode bonding agent, said cathode bonding agent including powders of said cathode ceramic material, a binder system materials, and a solvent mixed into a viscous slurry.

Claim 36

The method according to claim 30 wherein said electrolyte trilayer elements are bonded to said interconnect trilayer elements sandwiching cathode ceramic material between said electrolyte ceramic material and said interconnect ceramic material, said stacking step further comprising: wetting exposed anode surface of said cell elements with an anode bonding agent, said anode bonding agent including powders of said anode ceramic material, a binder system materials, and a solvent mixed into a viscous slurry.

Claim 37

The method of claim 30, further characterized by: configuring said plurality of electrolyte trilayer elements and said plurality of interconnect trilayer elements to include aligned integral fuel inlet, fuel outlet, oxidant inlet, and oxidant outlet manifolds at spaced apart locations; forming a plurality of fuel passageways extending through said anode ceramic material from said fuel inlet manifold to said fuel outlet manifold; and forming a plurality of oxidant passageways extending through said cathode ceramic material from said oxidant inlet manifold to said oxidant outlet manifold.

Claim 38

The method of claim 30, further characterized by: selecting a cermet of cobalt or nickel metal with stabilized zirconia for said anode, strontium-doped lanthanum manganite for said cathode, yttria-stabilized zirconia for said electrolyte, and doped lanthanum chromite for said interconnect.

Claim 41

The apparatus of claim 35 wherein said bonding agent means further comprises: an anode bonding agent including powders of said anode ceramic material, a binder system material, and a solvent mixed into a viscous slurry for bonding one surface of said interconnect elements to said anode of said electrolyte elements; and a cathode bonding agent including powders of said cathode ceramic material, said binder system material, and a solvent mixed into a viscous slurry for bonding the opposite surface of said interconnect elements to said cathode of said electrolyte elements.

Claim 42

The apparatus of claim 36, wherein said anode bonding agent and said cathode bonding agent each further include interconnect ceramic materials mixed into said respective viscous slurries.

Claim 43

The apparatus of claim 37, wherein said ceramic materials further comprise: a cermet of cobalt or nickel metal with stabilized zirconia for said anode; strontium-doped lanthanum manganite for said cathode; yttria-stabilized zirconia for said electrolyte; and lanthanum chromite doped with a compound selected from the group consisting of magnesium, calcium cobalt, and strontium, for said interconnect.

Claim 44

The apparatus of claim 38, wherein said binder system material of said bonding agent means further comprises: a binder selected from the group consisting of synthetic rubber, plastics, polyvinyl alcohol, polyvinyl butyryl resin, and polymer systems which thermally decompose without cross linking; and a plasticizer selected from the group consisting of butyl benzyl phthalate and solvents of the phthalate group.

Claim 45

The apparatus of claim 36, wherein said anode bonding agent and said cathode bonding agent each further include powdered platinum mixed into said respective viscous slurries.

Claim 46

The apparatus of claim 35 wherein said bonding agent means further comprises: a ceramic paste material including at least one of the materials selected from the group consisting of ceramic cements, glass ceramics, an organo-metallic sol gel material, and zirconium oxide.

Claim 47

A bonding agent for use in bonding the contacting surfaces of ceramic elements of a monolithic solid oxide fuel cell which ceramic elements are at least partially but not completely sintered, said bonding agent comprising: ceramic materials selected from the group consisting of anode ceramics, cathode ceramics, and interconnect ceramics; a binder selected from the group consisting of synthetic rubber, plastics, polyvinyl alcohol, polyvinyl butyryl resin, and polymer systems which thermally decompose without cross linking; a plasticizer selected from the group consisting of butyl benzyl phthalate and solvents of the phthalate group; and a solvent, said ceramic material, said binder, said plasticizer, and said solvent mixed together to form a viscous slurry.

Claim 48

A bonding agent for use in bonding the contacting surfaces of ceramic elements of a monolithic solid oxide fuel cell which ceramic elements are at least partially but not completely sintered, said bonding agent comprising: ceramic materials selected from the group consisting of anode ceramics, cathode ceramics, and interconnect ceramics; a binder selected from the group consisting of synthetic rubber, plastics, polyvinyl alcohol, polyvinyl butyryl resin, and polymer systems which thermally decompose without cross linking; a plasticizer selected from the group consisting of butyl benzyl phthalate and solvents of the phthalate group; and a solvent, said ceramic material, said binder, said plasticizer, and said solvent mixed together to form a viscous slurry.

Claim 49

The bonding agent of claim 42, wherein said ceramic materials further comprise: a cermet of cobalt or nickel metal with stabilized zirconia for said anode ceramic; strontium-doped lanthanum manganite for said cathode ceramic; yttria-stabilized zirconia for said electrolyte ceramic; and doped lanthanum chromite for said interconnect ceramic.

Claim 50

The bonding agent of claim 42, further comprising powdered platinum mixed into said viscous slurries.

Claim 51

A monolithic solid oxide fuel cell constructed according to the process steps of: mixing ceramic powders required to make an anode, a cathode, an electrolyte, and an interconnect each individually with a binder system to form a batch of each of said materials; forming thin tapes of each of said material batches; attaching said anode tape onto said electrolyte tape and said cathode tape on an opposite side of said electrolyte tape to form a trilayer electrolyte tape; shaping said trilayer electrolyte tape to form fuel flow pathways extending along said anode, and oxidant flow pathways extending along said cathode of said trilayer electrolyte tape; cutting said trilayer electrolyte tape to form a plurality of trilayer electrolyte elements having a desired gross net shape; cutting said interconnect tape to form a plurality of interconnect elements having a desired gross net shape; heating said trilayer electrolyte elements and said interconnect elements to a temperature sufficient to cause removal of the binder system and initiate sintering of the respective ceramic materials to a partially sintered condition; stacking a plurality of said partially sintered trilayer electrolyte elements alternately with a plurality of said partially sintered interconnect elements, subsequent to said heating step, to form a stacked array; and processing said stacked array to bond contacting surfaces of said alternately stacked trilayer electrolyte and interconnect elements.

Claim 52

A monolithic solid oxide fuel cell constructed according to the process steps of: mixing ceramic powders required to make an anode, a cathode, an electrolyte, and an interconnect each individually with a binder system to form a batch of each of said materials; forming thin tapes of each of said material batches; attaching said anode tape onto said electrolyte tape and said cathode tape on an opposite side of said electrolyte tape to form a trilayer electrolyte tape; shaping said trilayer electrolyte tape to form fuel flow pathways extending along said anode, and oxidant flow pathways extending along said cathode of said trilayer electrolyte tape; cutting said trilayer electrolyte tape to form a plurality of trilayer electrolyte elements having a desired gross net shape; cutting said interconnect tape to form a plurality of interconnect elements having a desired gross net shape; heating said trilayer electrolyte elements and said interconnect elements to a temperature sufficient to cause removal of the binder system and initiate sintering of the respective ceramic materials to a partially sintered condition; stacking a plurality of said partially sintered trilayer electrolyte elements alternately with a plurality of said partially sintered interconnect elements, subsequent to said heating step, to form a stacked array; and processing said stacked array to bond contacting surfaces of said alternately stacked trilayer electrolyte and interconnect elements.

Claim 53

A monolithic solid oxide fuel cell constructed according to the process steps of: mixing ceramic powders required to make an anode, a cathode, an electrolyte, and an interconnect each individually with a binder system to form a batch of each of said materials; forming thin tapes of each of said materials; attaching said anode tape onto said electrolyte tape and said cathode tape on an opposite side of said electrolyte tape to form a trilayer electrolyte tape; forming a plurality of parallel fuel and oxidant passageways extending along said anode and said cathode respectively; cutting said trilayer electrolyte tape to form a plurality of trilayer electrolyte elements having a desired gross net shape; cutting said interconnect tape to form a plurality of interconnect elements having a desired gross net shape; heating said trilayer electrolyte elements and said interconnect elements to a temperature and for a duration sufficient to cause removal of the binder system and to partially sinter the respective ceramic materials to a percentage of the desired final density for said respective materials such that subsequent heating and sintering will result in a compatible shrinkage of all of said ceramic materials; cooling said at least partially sintered trilayer electrolyte and interconnect elements; wetting one surface of said interconnect elements and a surface of said anode of said trilayer electrolyte elements with an anode bonding agent, said anode bonding agent including powders of said anode ceramic material, interconnect ceramic materials, binder system materials, and a solvent mixed into a viscous slurry; wetting the opposite surface of said interconnect elements and the surface of said cathode of said trilayer electrolyte elements with a cathode bonding agent, said cathode bonding agent including powders of said cathode ceramic material, interconnect ceramic materials, binder system materials, and a solvent mixed into a viscous slurry; stacking a plurality of said at least partially sintered trilayer electrolyte elements alternately with a plurality of said partially sintered interconnect elements to form a stacked array; and processing said stacked array to bond the contacting surfaces of said alternately stacked trilayer electrolyte and interconnect elements.

Claim 54

A monolithic solid oxide fuel cell constructed according to the process steps of: mixing ceramic powders required to make an anode, a cathode, an electrolyte, and an interconnect each individually with a binder system to form a batch of each of said materials; forming thin tapes of each of said materials; attaching said anode tape onto said electrolyte tape and said cathode tape on an opposite side of said electrolyte tape to form a trilayer electrolyte tape; forming a plurality of parallel fuel and oxidant passageways extending along said anode and said cathode respectively; cutting said trilayer electrolyte tape to form a plurality of trilayer electrolyte elements having a desired gross net shape; cutting said interconnect tape to form a plurality of interconnect elements having a desired gross net shape; heating said trilayer electrolyte elements and said interconnect elements to a temperature and for a duration sufficient to cause removal of the binder system and to partially sinter the respective ceramic materials to a percentage of the desired final density for said respective materials such that subsequent heating and sintering will result in a compatible shrinkage of all of said ceramic materials; cooling said at least partially sintered trilayer electrolyte and interconnect elements; wetting one surface of said interconnect elements and a surface of said anode of said trilayer electrolyte elements with an anode bonding agent, said anode bonding agent including powders of said anode ceramic material, interconnect ceramic materials, binder system materials, and a solvent mixed into a viscous slurry; wetting the opposite surface of said interconnect elements and the surface of said cathode of said trilayer electrolyte elements with a cathode bonding agent, said cathode bonding agent including powders of said cathode ceramic material, interconnect ceramic materials, binder system materials, and a solvent mixed into a viscous slurry; stacking a plurality of said at least partially sintered trilayer electrolyte elements alternately with a plurality of said partially sintered interconnect elements to form a stacked array; and processing said stacked array to bond the contacting surfaces of said alternately stacked trilayer electrolyte and interconnect elements.

Claim 55

A monolithic solid oxide fuel cell having a plurality of stacked cells, each cell including a cathode, an electrolyte, and an anode, said cells being separated from one another by an interconnect, constructed according to the process steps of: assembling a plurality of trilayer electrolyte elements each including respective layers of at least partially but not completely sintered cathode ceramic materials, electrolyte ceramic materials, and anode ceramic materials, said trilayer electrolyte elements including fuel and oxidant flow pathways formed into the respective surfaces of said anode layer and said cathode layer by displacing contiguous portions of said surfaces from the plane of the pre-existing flat surface leaving raised surface portions, said trilayer electrolyte elements having a desired configuration; forming a plurality of interconnect elements each including at least partially but not completely sintered interconnect ceramic materials in a desired configuration; wetting one surface of said interconnect elements and the surface of said anode of said trilayer electrolyte elements with an anode bonding agent, said anode bonding agent including powders of said anode ceramic material, said interconnect ceramic materials, a binder system materials, and a solvent mixed into a viscous slurry; wetting the opposite surface of said interconnect elements and the surface of said cathode of said trilayer electrolyte elements with a cathode bonding agent, said cathode bonding agent including powders of said cathode ceramic material, said interconnect ceramic material, said binder system materials, and a solvent mixed into a viscous slurry; stacking a plurality of said at least partially sintered trilayer electrolyte elements alternately with a plurality of said interconnect elements to form a stacked array; and processing said stacked array to bond the contacting surfaces of said alternately stacked trilayer electrolyte and interconnect elements.

Claim 56

A monolithic solid oxide fuel cell having a plurality of stacked cells, each cell including a cathode, an electrolyte, and an anode, said cells being separated from one another by an interconnect, constructed according to the process steps of: assembling a plurality of trilayer electrolyte elements each including respective layers of at least partially but not completely sintered cathode ceramic materials, electrolyte ceramic materials, and anode ceramic materials, said trilayer electrolyte elements including fuel and oxidant flow pathways formed into the respective surfaces of said anode layer and said cathode layer by displacing contiguous portions of said surfaces from the plane of the pre-existing flat surface leaving raised surface portions, said trilayer electrolyte elements having a desired configuration; forming a plurality of interconnect elements each including at least partially but not completely sintered interconnect ceramic materials in a desired configuration; wetting one surface of said interconnect elements and the surface of said anode of said trilayer electrolyte elements with an anode bonding agent, said anode bonding agent including powders of said anode ceramic material, said interconnect ceramic materials, a binder system materials, and a solvent mixed into a viscous slurry; wetting the opposite surface of said interconnect elements and the surface of said cathode of said trilayer electrolyte elements with a cathode bonding agent, said cathode bonding agent including powders of said cathode ceramic material, said interconnect ceramic material, said binder system materials, and a solvent mixed into a viscous slurry; stacking a plurality of said at least partially sintered trilayer electrolyte elements alternately with a plurality of said interconnect elements to form a stacked array; and processing said stacked array to bond the contacting surfaces of said alternately stacked trilayer electrolyte and interconnect elements.