Abstract
Abstract A unique process metallizes a substrate surface using a reducing agent including a borohydride to reduce, in a starved reaction, metal oxide particles (300) substantially uniformly distributed and at a controlled concentration in a particle-filled resin (204) to produce catalytic island areas (301). The catalytic island areas (301) formed have a surface resistivity greater than 10 6 ohms per square. These catalytic island areas (301) are then electrolessly metallized to a predetermined thickness, such that adjacent catalytic island areas (301) are interconnected and form metallic features, such as pads, vias (213), and conductors (210, 211 and 212). The starved reaction limits the reduction of metal oxide particles (300) to catalytic island areas (301) and prevents migration of reduced metal beyond each of the exposed surfaces of particle-filled resin (204) which are to be metallized.
Inventors
- 👤 Vernon L. Brown
- 👤 Julia S. Johnson
- 👤 Yaroslaw A. Magera
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:52
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/51; C04B41/52; C04B41/80; C04B41/81; C04B41/85; C04B41/88; C04B41/89; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28; H; H05; H05K; H05K3/00; H05K3/46; H05K3/4644; H05K3/4661; C04B2111/00; C04B2111/00474; C04B2111/00844; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0206; H05K2201/0236; H05K2201/09; H05K2201/09209; H05K2201/095; H05K2201/09509; H05K2203/00; H05K2203/09; H05K2203/095; H05K2203/11; H05K2203/1157; H05K2203/12; H05K2203/125; H05K3/0011; H05K3/0017; H05K3/0023; H05K3/10; H05K3/18; H05K3/181; H05K3/182; H05K3/184; H05K3/465; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
131 words
A process for metallizing at least a first surface of a substrate, said process comprising the steps of: (a) forming a substrate with at least a first surface by substantially uniformly mixing a resin with a plurality of small metal oxide particles; (b) exposing the small metal oxide particles near the first surface; (c) applying an aqueous reducing agent including a borohydride to the first surface of the substrate for converting the exposed metal oxide particles to non-connected island areas of catalytic film each encompassing one or more metal oxide particles, such that the first surface has a surface resistivity greater than 10 6 ohms per square; and (d) electrolessly metallizing the island areas of the first surface of said substrate to a predetermined thickness, whereby adjacent island areas are interconnected.
Claim 2
Dependent Claim
131 words
A process for metallizing at least a first surface of a substrate, said process comprising the steps of: (a) forming a substrate with at least a first surface by substantially uniformly mixing a resin with a plurality of small metal oxide particles; (b) exposing the small metal oxide particles near the first surface; (c) applying an aqueous reducing agent including a borohydride to the first surface of the substrate for converting the exposed metal oxide particles to non-connected island areas of catalytic film each encompassing one or more metal oxide particles, such that the first surface has a surface resistivity greater than 10 6 ohms per square; and (d) electrolessly metallizing the island areas of the first surface of said substrate to a predetermined thickness, whereby adjacent island areas are interconnected.
Claim 3
Dependent Claim
26 words
The process according to claim 1, wherein said resin is comprised of one or a mixture of a thermoplastic resin, thermoset resin, elastomer, composite, or laminate.
Claim 4
Dependent Claim
29 words
The process according to claim 1, wherein said resin is comprised of one or a mixture of a polyolefin, vinyl, polystyrene, polyamide, acrylic, polyurethane, or saturated polyester thermoplastic resin.
Claim 5
Dependent Claim
26 words
The process according to claim 1, wherein said resin is comprised of one or a mixture of a hardened phenolic, unsaturated polyester, epoxy, or polyimide prepolymer.
Claim 6
Dependent Claim
41 words
The process according to claim 1, wherein said reducing agent is comprised of an unsubstituted alkali metal borohydride or a substituted borohydride wherein up to three of the hydrogen atoms which comprise the borohydride ion have been replaced by inert substituents.
Claim 7
Dependent Claim
19 words
The process according to claim 1, wherein said metal oxide particles are comprised of cuprous oxide or nickel oxide.
Claim 8
Dependent Claim
20 words
The process according to claim 1, wherein said step (d) deposits metallization having a thickness of at least 4 micrometers.
Claim 9
Dependent Claim
26 words
The process according to claim 1, wherein said step (d) deposits metallization comprised of nickel, cobalt, chromium copper, iron, silver, gold, vanadium, cobalt/nickel alloy, or brass.
Claim 10
Dependent Claim
23 words
The process according to claim 1, wherein said metal oxide particles have a diameter ranging at least from 0.05 micrometers to 10 micrometers.
Claim 11
Dependent Claim
35 words
The process according to claim 1, wherein said step (a) further includes the step of reactive ion etching the first surface of said substrate for cleaning the first surface and exposing the metal oxide particles.
Claim 12
Dependent Claim
26 words
The process according to claim 1, wherein said step (a) further includes the step of chemically etching the first surface for exposing said metal oxide particles.
Claim 13
Dependent Claim
23 words
The process according to claim 1, wherein said step (a) comprises the step of controlling the percentage by weight of said metal oxide.
Claim 14
Dependent Claim
20 words
The process according to claim 12, wherein the percentage by weight of said metal oxide is less than ten percent.
Claim 15
Dependent Claim
25 words
The process according to claim 1, wherein said step (c) further includes the step of controlling the concentration of the borohydride in the reducing agent.
Claim 16
Dependent Claim
26 words
The process according to claim 14, wherein the concentration of the borohydride in the reducing agent is at least from 0.01 to 10 moles per liter.
Claim 17
Dependent Claim
22 words
The process according to claim 1, wherein said step (c) further includes the step of controlling the pH of the reducing agent.
Claim 18
Dependent Claim
20 words
The process according to claim 16, wherein the pH of the reducing agent is at least from 9 to 11.5.
Claim 19
Dependent Claim
26 words
The process according to claim 1, wherein said step (c) further includes the step of spraying the reducing agent onto the first surface of the substrate.
Claim 20
Dependent Claim
23 words
The process according to claim 18, further including the step of controlling the flow rate, duration, and pressure of said step of spraying.
Claim 21
Dependent Claim
10 words
The product of the process as defined in claim 1.
Claim 22
Dependent Claim
174 words
A process for selectively metallizing at least a first surface of a substrate comprised of a non-conductive material, said process comprising the steps of: (a) forming a first layer on the first surface by substantially uniformly mixing a resin with a plurality of small metal oxide particles; (b) forming a second layer on the first surface covering said first layer; (c) selectively removing portions of said second layer to reveal corresponding portions of said first layer; (d) exposing the small metal oxide particles near the surface of said portions of the first layer; (e) applying, to said portions of said first layer, an aqueous reducing agent including a borohydride for converting the exposed metal oxide particles to non-connected island areas of catalytic film each encompassing one or more metal oxide particles, such that said portions of said first layer have a surface resistivity greater than 10 6 ohms per square; and (f) electrolessly metallizing the island areas of said portions of said first layer to a predetermined thickness, whereby adjacent island areas are interconnected.
Claim 23
Dependent Claim
174 words
A process for selectively metallizing at least a first surface of a substrate comprised of a non-conductive material, said process comprising the steps of: (a) forming a first layer on the first surface by substantially uniformly mixing a resin with a plurality of small metal oxide particles; (b) forming a second layer on the first surface covering said first layer; (c) selectively removing portions of said second layer to reveal corresponding portions of said first layer; (d) exposing the small metal oxide particles near the surface of said portions of the first layer; (e) applying, to said portions of said first layer, an aqueous reducing agent including a borohydride for converting the exposed metal oxide particles to non-connected island areas of catalytic film each encompassing one or more metal oxide particles, such that said portions of said first layer have a surface resistivity greater than 10 6 ohms per square; and (f) electrolessly metallizing the island areas of said portions of said first layer to a predetermined thickness, whereby adjacent island areas are interconnected.
Claim 24
Dependent Claim
26 words
The process according to claim 21, wherein said resin is comprised of one or a mixture of a thermoplastic resin, thermoset resin, elastomer, composite, or laminate.
Claim 25
Dependent Claim
29 words
The process according to claim 21, wherein said resin is comprised of one or a mixture of a polyolefin, vinyl, polystyrene, polyamide, acrylic, polyurethane, or saturated polyester thermoplastic resin.
Claim 26
Dependent Claim
26 words
The process according to claim 21, wherein said resin is comprised of one or a mixture of a hardened phenolic, unsaturated polyester, epoxy, or polyimide prepolymer.
Claim 27
Dependent Claim
41 words
The process according to claim 21, wherein said reducing agent is comprised of an unsubstituted alkali metal borohydride or a substituted borohydride wherein up to three of the hydrogen atoms which comprise the borohydride ion have been replaced by inert substituents.
Claim 28
Dependent Claim
19 words
The process according to claim 21, wherein said metal oxide particles are comprised of cuprous oxide or nickel oxide.
Claim 29
Dependent Claim
20 words
The process according to claim 21, wherein said step (f) deposits metallization having a thickness of at least 4 micrometers.
Claim 30
Dependent Claim
26 words
The process according to claim 21, wherein said step (f) deposits metallization comprised of nickel, cobalt, chromium copper, iron, silver, gold, vanadium, cobalt/nickel alloy, or brass.
Claim 31
Dependent Claim
23 words
The process according to claim 21, wherein said metal oxide particles have a diameter ranging at least from 0.05 micrometers to 10 micrometers.
Claim 32
Dependent Claim
35 words
The process according to claim 21, wherein said step (a) further includes the step of reactive ion etching the first surface of said substrate for cleaning the first surface and exposing the metal oxide particles.
Claim 33
Dependent Claim
26 words
The process according to claim 21, wherein said step (a) further includes the step of chemically etching the first surface for exposing said metal oxide particles.
Claim 34
Dependent Claim
23 words
The process according to claim 21, wherein said step (a) comprises the step of controlling the percentage by weight of said metal oxide.
Claim 35
Dependent Claim
20 words
The process according to claim 32, wherein the percentage by weight of said metal oxide is less than ten percent.
Claim 36
Dependent Claim
25 words
The process according to claim 21, wherein said step (c) further includes the step of controlling the concentration of the borohydride in the reducing agent.
Claim 37
Dependent Claim
26 words
The process according to claim 34, wherein the concentration of the borohydride in the reducing agent is at least from 0.01 to 10 moles per liter.
Claim 38
Dependent Claim
22 words
The process according to claim 21, wherein said step (c) further includes the step of controlling the pH of the reducing agent.
Claim 39
Dependent Claim
20 words
The process according to claim 36, wherein the pH of the reducing agent is at least from 9 to 11.5.
Claim 40
Dependent Claim
26 words
The process according to claim 21, wherein said step (c) further includes the step of spraying the reducing agent onto the first surface of the substrate.
Claim 41
Dependent Claim
23 words
The process according to claim 38, further including the step of controlling the flow rate, duration, and pressure of said step of spraying.
Claim 42
Dependent Claim
10 words
The product of the process as defined in claim 21.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-11-10 | 1996-05-11 | 1996-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-11-10 | 2000-05-11 | 2000-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-11-10 | 2004-05-11 | 2004-11-10 | $7700.00 | Window Closed / Lapsed |