Phase separated composite materials
Assignee: NAVY United States, REPRESENTED BY SECRETARY OF
•
Filing: 1990-11-15
•
Granted: 1992-10-27
•
Expires: 2010-11-15
Abstract
Abstract A method of forming a phase-separated composite material which utilizes sputtering in a thermal gradient at relatively high sputtering pressures generally above about 0.1 Torr sufficient to produce nanoscale particles which are embedded in a continuous phase matrix produced by normal sputtering. This method avoids the alloying and/or compound formation which prevents preparation of phase-separated composites by conventional co-sputtering, and the invention thus enables particulate composites to be formed from entirely new classes of materials. Microhardness testing shows that the phase-separated composites produced by the present invention have an increased hardness compared to the pure matrix material.
Inventors
- 👤 Ronald L. Holtz
- 👤 Gan-Moog Chow
- 👤 Alan S. Edelstein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 16:33
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/54; C23C14/541; C23C14/06; C23C14/14; C23C14/34; C23C14/35; C23C14/352; C23C14/354; C23C14/355; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/73; Y10S505/731; Y10S505/80; Y10S505/815; Y10S505/816; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12063; Y10T428/12069; Y10T428/12097; Y10T428/12104
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
182 words
A method of producing a composite material comprising the steps of: (a) sputtering a continuous phase layer of a first element from a first sputtering target onto a substrate at a first sputtering pressure which is sufficiently low that a continuous phase layer is deposited; (b) maintaining a thermal gradient between said substrate and a second sputtering target composed of a second element whereby said substrate is at a lower temperature than said second sputtering target, and sputtering a layer of discrete particles of said second element having a particle size from about 1 to about 50 nm from said second sputtering target onto the previously deposited sputtered layer of said first element at a second sputtering pressure higher than said first sputtering pressure, said second sputtering pressure being sufficiently high that a layer of discrete particles is deposited; and (c) sputtering a further continuous phase layer of said first element over said layer of discrete particles at a third sputtering pressure lower than said second sputtering pressure, said third sputtering pressure being sufficiently low that a continuous phase layer is deposited.
Claim 2
Independent Claim
182 words
A method of producing a composite material comprising the steps of: (a) sputtering a continuous phase layer of a first element from a first sputtering target onto a substrate at a first sputtering pressure which is sufficiently low that a continuous phase layer is deposited; (b) maintaining a thermal gradient between said substrate and a second sputtering target composed of a second element whereby said substrate is at a lower temperature than said second sputtering target, and sputtering a layer of discrete particles of said second element having a particle size from about 1 to about 50 nm from said second sputtering target onto the previously deposited sputtered layer of said first element at a second sputtering pressure higher than said first sputtering pressure, said second sputtering pressure being sufficiently high that a layer of discrete particles is deposited; and (c) sputtering a further continuous phase layer of said first element over said layer of discrete particles at a third sputtering pressure lower than said second sputtering pressure, said third sputtering pressure being sufficiently low that a continuous phase layer is deposited.
Claim 3
Dependent Claim
22 words
A method according to claim 1, further comprising repeating steps (b) and (c) until a desired composite material thickness is built up.
Claim 4
Dependent Claim
18 words
A method according to claim 1, wherein said first element is aluminum and said second element is molybdenum.
Claim 5
Dependent Claim
16 words
A method according to claim 1, wherein said thermal gradient is maintained by cooling said substrate.
Claim 6
Dependent Claim
14 words
A method according to claim 4, wherein said substrate is cooled with liquid nitrogen.
Claim 7
Dependent Claim
27 words
A method according to claim 1, wherein the sputtering pressures are maintained by carrying out the sputtering steps in a sputtering chamber containing an inert gas atmosphere.
Claim 8
Dependent Claim
19 words
A method according to claim 6, wherein sputtering is carried out in a sputtering chamber containing an argon atmosphere.
Claim 9
Dependent Claim
21 words
A method according to claim 1, wherein said continuous phase layers are deposited at a sputtering pressure of about 0.001 Torr.
Claim 10
Dependent Claim
28 words
A method according to claim 1, wherein said layer of discrete particles is deposited at a sputtering pressure in the range from about 0.1 to about 10 Torr.
Claim 11
Dependent Claim
28 words
A method according to claim 9, wherein said layer of discrete particles is deposited at a sputtering pressure in the range from about 0.15 to about 1 Torr.
Claim 12
Dependent Claim
28 words
A method according to claim 10, wherein said layer of discrete particles is deposited at a sputtering pressure in the range from about 0.2 to about 0.7 Torr.
Claim 13
Dependent Claim
28 words
A method according to claim 11, wherein said layer of discrete particles is deposited at a sputtering pressure in the range from about 0.3 to about 0.6 Torr.
Claim 14
Dependent Claim
35 words
A method according to claim 1, wherein said substrate is disposed a distance in the range from about 2 to about 20 cm from said second sputtering target during sputtering said layer of discrete particles.
Claim 15
Dependent Claim
35 words
A method according to claim 13, wherein said substrate is disposed a distance in the range from about 5 to about 12 cm from said second sputtering target during sputtering said layer of discrete particles.
Claim 16
Dependent Claim
35 words
A method according to claim 14, wherein said substrate is disposed a distance in the range from about 7 to about 10 cm from said second sputtering target during sputtering said layer of discrete particles.
Claim 17
Dependent Claim
24 words
A method according to claim 1, wherein said discrete particles have a particle size in the range from about 2 to about 20 nm.
Claim 18
Dependent Claim
24 words
A method according to claim 16, wherein said discrete particles have a particle size in the range from about 3 to about 12 nm.
Claim 19
Dependent Claim
18 words
A method according to claim 17, wherein said discrete particles have a particle size of about 7 nm.
Claim 20
Dependent Claim
12 words
A method according to claim 1, wherein said discrete particles are crystalline.
Claim 21
Dependent Claim
18 words
A method according to claim 19, wherein said discrete particles and said continuous phase matrix are each crystalline.
Claim 22
Dependent Claim
35 words
A method according to claim 1, wherein a bimodal size distribution of discrete particles having respective particle sizes of about 20 nm and about 5 nm is produced during sputtering said layer of discrete particles.
Claim 23
Dependent Claim
22 words
A method according to claim 1, wherein said first and second elements are normally miscible with each other to form an alloy.
Claim 24
Dependent Claim
26 words
A method according to claim 1, wherein said first and second elements are normally reactive with each other in the vapor phase to form a compound.
Claim 25
Dependent Claim
35 words
A method according to claim 1, wherein the sputtering pressure during sputtering of said layer of discrete particles is from about 10 to about 1000 times the pressure during sputtering of said continuous phase layers.
Claim 26
Dependent Claim
32 words
A method according to claim 24, wherein the sputtering pressure during sputtering of said layer of discrete particles is at least about 100 times the pressure during sputtering of said continuous layers.
Claim 27
Dependent Claim
27 words
A method according to claim 1, wherein said discrete particles of said second element comprise from about 0.1 vol.-% to about 63 vol.-% of said composite material.
Claim 28
Dependent Claim
27 words
A method according to claim 26, wherein said discrete particles of said second element comprise from about 5 vol.-% to about 20 vol.-% of said composite material.
Claim 29
Dependent Claim
31 words
A method according to claim 1, wherein said continuous phase layers are sputtered at a sputtering power in the range from about 2.5 watts/cm 2 to about 250 watts/cm 2 .
Claim 30
Dependent Claim
23 words
A method according to claim 28, wherein said continuous phase layers are sputtered at a sputtering power of about 50 watts/cm 2 .
Claim 31
Dependent Claim
32 words
A method according to claim 1, wherein said layer of discrete particles is sputtered at a sputtering power in the range from about 6.25 watts/cm 2 to about 25 watts/cm 2 .
Claim 32
Dependent Claim
24 words
A method according to claim 30, wherein said layer of discrete particles is sputtered at a sputtering power of about 18.5 watts/cm 2 .
Claim 33
Dependent Claim
25 words
A method according to claim 2, wherein each repetition of steps (b) and (c) produces an individual sublayer having a thickness of about 25 nm.
Claim 34
Dependent Claim
34 words
A method according to claim 32, wherein steps (b) and (c) are repeated sufficient to produce a composite material having a total thickness in the range from about 100 nm to about 500 nm.
Claim 35
Dependent Claim
29 words
A method according to claim 1, wherein the sputtering pressure is controlled during sputtering of said layer of discrete particles in order to regulate the size of said particles.
Claim 36
Independent Claim
33 words
A method according to claim wherein the sputtering power is controlled during sputtering of said layer of discrete particles in order to regulate the vol.-% of said second element in said composite material.
Claim 37
Dependent Claim
41 words
A method according to claim 1, wherein the temperature difference of said thermal gradient is controlled during sputtering of said layer of discrete particles in order to regulate the velocity at which particles migrate from said second target to said substrate.
Claim 38
Dependent Claim
33 words
A method according to claim 1, wherein at least one of said sputtering steps in carried out in the presence of a reactive gas to deposit a compound reaction product on said substrate.
Claim 39
Dependent Claim
22 words
A method according to claim 37, wherein said reactive gas is selected from the group consisting of oxygen, nitrogen and water vapor.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-27 | 1996-04-27 | 1996-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-27 | 2000-04-27 | 2000-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-27 | 2004-04-27 | 2004-10-27 | $7700.00 | Window Closed / Lapsed |