Abstract
Abstract A cost-effective process for polishing refractory materials, including natural and synthetic diamond, sapphire, ruby and Si 3 N 4 balls, is disclosed, wherein the surfaces thereof are successively softened to a predetermined depth by ion implantation, followed by mechanical polishing. This cycle of ion-implantation softening, followed by mechanical polishing, is repeated until such time that surface profilometry indicates that a desired surface smoothness has been achieved.
Inventors
- 👤 Piran Sioshansi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:39
CPC Classifications
B; B24; B24B; B24B37/00; B24B37/04; C; C23; C23C; C23C14/00; C23C14/22; C23C14/48; Y; Y10; Y10S; Y10S977/00; Y10S977/84; Y10S977/888; Y10S977/89
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
62 words
A process of polishing refractory materials comprising: (a) providing a refractory material having an operative surface; (b) softening said operative surface to a predetermined depth by forming a soft ion-implanted layer in said surface; (c) polishing said softened layer of said operative surface; and (d) repeating said softening and polishing steps until a desired surface smoothness of said operative surface is achieved.
Claim 2
Dependent Claim
62 words
A process of polishing refractory materials comprising: (a) providing a refractory material having an operative surface; (b) softening said operative surface to a predetermined depth by forming a soft ion-implanted layer in said surface; (c) polishing said softened layer of said operative surface; and (d) repeating said softening and polishing steps until a desired surface smoothness of said operative surface is achieved.
Claim 3
Dependent Claim
29 words
The process of claim 1 wherein said refractory material is one of a group consisting of: natural diamond, synthetic diamond, sapphire, ruby, silicon nitride, SiC, polycrystalline alumina and zirconia.
Claim 4
Dependent Claim
38 words
The process of claim 1 wherein said refractory material is intended for use as polished gems, optical coatings and optical windows, heat sinks, bearing and low friction wear resistant surfaces and as substrates for active electronic device elements.
Claim 5
Dependent Claim
39 words
The process of claim 1 wherein said softening said operative surface by forming said soft ion-implanted layer herein is effected by ion-implantation affecting the crystal lattice structure of said operative surface of said refractory material to said predetermined depth.
Claim 6
Dependent Claim
36 words
The process of claim 4 wherein said affecting the crystal lattice structure by said implantation results in a transformation of said crystal lattice structure to a quasi-amorphous state of said refractory material to said predetermined depth.
Claim 7
Dependent Claim
25 words
The process of claim 5 wherein said transformation to said quasi-amorphous state of said refractory material conditions its said operative surface for said polishing step.
Claim 8
Dependent Claim
45 words
The process of claim 4 wherein said ion-implantation is effected by bombarding said operative surface with at least one of the following ions: nitrogen, oxygen, carbon, boron, all rare gases (He, Ne, Ar, Kr, Xe), aluminum, magnesium, silicon, titanium, yttrium, nickel, flourine and chlorine ions.
Claim 9
Dependent Claim
61 words
The process of claim 7 wherein said ion bombardment is effected with the following operational parameters: a time duration of about 30 to about 60 minutes, a dose of ions from about 1E14 to about 1E18, with energy ranging from about 10 to about 5000 keV, and a current density from about 0.1 uA/cm 2 to about 10 uA/cm 2 .
Claim 10
Dependent Claim
60 words
The process of claim 1 wherein said polishing said softened layer of said operative surface is effected using a cast iron lap and mesh sizes from about 0.01 to about 10 micrometers of one of the following abrasive compounds: natural diamond, corundum, SiC, Al 2 O 3 , ZrO, MgO, Cr 2 O 3 and Fe 2 O 3 .
Claim 11
Dependent Claim
16 words
The process of claim 1 wherein said softening and polishing steps are repeated at least once.
References Cited (Backward Citations)
US3900636A
Cited
US4465524A
Cited
US4568396A
Cited
US4596208A
Cited
US4861407A
Cited
US4693760A
Cited
US4743493A
Cited
US4743308A
Cited
US5032243A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-10-13 | 1996-04-13 | 1996-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-10-13 | 2000-04-13 | 2000-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-10-13 | 2004-04-13 | 2004-10-13 | $7700.00 | Window Closed / Lapsed |