Abstract A method for eliminating carbonaceous contaminants and preventing the hydration/solubilization of the alumina protective coating of a phosphor is described. The method involves the heating a fluidized alumina coated phosphor in a fluidized bed at a temperature and for a period of time sufficient to preclude adversely affecting the protective oxide coating on the phosphor during subsequent water-based suspension processing without detrimentally altering the phosphor. After heating the fluidized phosphor is cooled and then added to a water-based suspension. The conditions for treating a manganese activated zinc silicate phosphor having a protective alumina coating are heating the fluidized phosphor at a temperature between about 700° C. and about 850° C. for a period of time from about 15 minutes to about 20 hours. A fluorescent lamp containing the phosphor prepared by the above described method is also described.
An alumina coated phosphor treatment process comprising the following steps: step 1--fluidizing a manganese activated zinc silicate phosphor having an alumina protective coating and having a particle size of about 10-12 microns in an isothermal fluidized bed to form a fluidized phosphor powder, the alumina coating having been applied through chemical vapor deposition; step 2--heating said fluidized phosphor powder to form an annealed phosphor powder, wherein said heating is carried out at a temperature from about 200° C. to about 850° C. and for a period of time sufficient to preclude adversely affecting said alumina protective coating of said phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said phosphor; step 3--cooling said annealed phosphor powder from step 2 to form a cooled annealed phosphor powder; and step 4--adding said cooled annealed phosphor powder from step 3 to a water-base suspension.
Claim 2
Dependent Claim
143 words
An alumina coated phosphor treatment process comprising the following steps: step 1--fluidizing a manganese activated zinc silicate phosphor having an alumina protective coating and having a particle size of about 10-12 microns in an isothermal fluidized bed to form a fluidized phosphor powder, the alumina coating having been applied through chemical vapor deposition; step 2--heating said fluidized phosphor powder to form an annealed phosphor powder, wherein said heating is carried out at a temperature from about 200° C. to about 850° C. and for a period of time sufficient to preclude adversely affecting said alumina protective coating of said phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said phosphor; step 3--cooling said annealed phosphor powder from step 2 to form a cooled annealed phosphor powder; and step 4--adding said cooled annealed phosphor powder from step 3 to a water-base suspension.
Claim 3
Dependent Claim
25 words
An alumina coated phosphor treatment process in accordance with claim 1 wherein said period of time being from about 15 minutes to about 20 hours.
Claim 4
Dependent Claim
40 words
An alumina coated phosphor treatment process in accordance with claim 1 wherein said temperature in Step 2 being from about 750° C. to about 770° C. and said period of time being from about 1 hour to about 4 hours.