Abstract
Abstract A method for eliminating carbonaceous contaminants and preventing the hydration/solubilization of the oxide coating of a phosphor is described. The method involves the annealing of the oxide coated phosphor at a temperature and for a period sufficient to preclude adversely affecting the protective oxide coating on the phosphor during subsequent water-based suspension processing without detrimentally altering the phosphor. After annealing the phosphor is cooled and then added to a water-based suspension. The optimum conditions for annealing a manganese activated zinc silicate phosphor or a calcium halophosphate phosphor having a protective aluminum oxide coating are the combination of a temperature between about 700° C. and about 850° C. and for a period of time from about 15 minutes to about 20 hours.
Inventors
- 👤 Thomas E. Peters
- 👤 Roger B. Hunt, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 08:46
CPC Classifications
H; H01; H01J; H01J61/00; H01J61/02; H01J61/38; H01J61/42; H01J61/46; C; C09; C09K; C09K11/00; C09K11/02; C09K11/025; C09K11/08; C09K11/59; C09K11/592; C09K11/595; C09K11/74; C09K11/75; C09K11/76; H01J61/44
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
95 words
A pre-water-based suspension phosphor treatment method comprising the following steps: Step 1--annealing a phosphor having a protective oxide coating at about 700° C. to about 850° C. and for a period of about 15 minutes to about 20 hours to preclude adversely affecting said protective oxide coating on said phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said phosphor to form an annealed phosphor; Step 2--cooling the annealed phosphor from step 1 to form a cooled annealed phosphor; and Step 3--adding the cooled annealed phosphor from step 2 to a water-base suspension.
Claim 2
Dependent Claim
95 words
A pre-water-based suspension phosphor treatment method comprising the following steps: Step 1--annealing a phosphor having a protective oxide coating at about 700° C. to about 850° C. and for a period of about 15 minutes to about 20 hours to preclude adversely affecting said protective oxide coating on said phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said phosphor to form an annealed phosphor; Step 2--cooling the annealed phosphor from step 1 to form a cooled annealed phosphor; and Step 3--adding the cooled annealed phosphor from step 2 to a water-base suspension.
Claim 3
Dependent Claim
107 words
A pre-water-based suspension phosphor treatment method comprising the following steps: Step 1--annealing a manganese activated zinc silicate phosphor having a protective oxide coating at about 700° C. to about 850° C. and for a period of about 15 minutes to about 20 hours to preclude adversely affecting said protective oxide coating on said manganese activated zinc silicate phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said manganese activated zinc silicate phosphor to form an annealed phosphor; Step 2--cooling the annealed phosphor from step 1 to form a cooled annealed phosphor; and Step 3--adding the cooled annealed phosphor from step 2 to a water-based suspension.
Claim 4
Dependent Claim
107 words
A pre-water-based suspension phosphor treatment method comprising the following steps: Step 1--annealing a manganese activated zinc silicate phosphor having a protective oxide coating at about 700° C. to about 850° C. and for a period of about 15 minutes to about 20 hours to preclude adversely affecting said protective oxide coating on said manganese activated zinc silicate phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said manganese activated zinc silicate phosphor to form an annealed phosphor; Step 2--cooling the annealed phosphor from step 1 to form a cooled annealed phosphor; and Step 3--adding the cooled annealed phosphor from step 2 to a water-based suspension.
Claim 5
Dependent Claim
21 words
A pre-water-based suspension phosphor treatment method in accordance with claim 2 wherein said protective oxide coating consists essentially of aluminum oxide.
Claim 6
Dependent Claim
28 words
A pre-water-based suspension phosphor treatment method in accordance with claim 2 wherein said annealing comprises a temperature of about 750° C. for a period of about 4 hours.
Claim 7
Dependent Claim
110 words
A pre-water-based suspension phosphor treatment method comprising the following steps: Step 1--annealing an antimony, manganese activated calcium halophosphate phosphor having a protective oxide coating at about 700° C. to about 850° C. and for a period of about 15 minutes to about 20 hours to preclude adversely affecting said protective oxide coating on said antimony, manganese activated calcium halophosphate phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said antimony, manganese activated calcium halophosphate phosphor to form an annealed phosphor; Step 2--cooling the annealed phosphor from step 1 to form a cooled annealed phosphor; and Step 3--adding the cooled annealed phosphor from step 2 to a water-based suspension.
Claim 8
Dependent Claim
110 words
A pre-water-based suspension phosphor treatment method comprising the following steps: Step 1--annealing an antimony, manganese activated calcium halophosphate phosphor having a protective oxide coating at about 700° C. to about 850° C. and for a period of about 15 minutes to about 20 hours to preclude adversely affecting said protective oxide coating on said antimony, manganese activated calcium halophosphate phosphor during subsequent water-based suspension processing and to preclude detrimentally altering said antimony, manganese activated calcium halophosphate phosphor to form an annealed phosphor; Step 2--cooling the annealed phosphor from step 1 to form a cooled annealed phosphor; and Step 3--adding the cooled annealed phosphor from step 2 to a water-based suspension.
Claim 9
Dependent Claim
21 words
A pre-water-based suspension phosphor treatment method in accordance with claim 5 wherein said protective oxide coating consists essentially of aluminum oxide
Claim 10
Dependent Claim
28 words
A pre-water-based suspension phosphor treatment method in accordance with claim 5 wherein said annealing comprises a temperature of about 750° C. for a period of about 4 hours.
Claim 11
Dependent Claim
28 words
A pre-water-based suspension phosphor treatment method in accordance with claim 5 wherein said annealing comprises a temperature of about 850° C. for a period of about one hour.
Claim 12
Dependent Claim
57 words
A fluorescent lamp comprising a hermetically sealed tubular glass envelope coated with a phosphor, said phosphor prepared in accordance with claim 1, bases at each end of said tubular glass envelope, electrodes, support electrical leads electrically connected to said electrodes, said electrodes coated with an electron-emission promoting material, and a mercury droplet within said tubular glass envelope.
Claim 13
Dependent Claim
57 words
A fluorescent lamp comprising a hermetically sealed tubular glass envelope coated with a phosphor, said phosphor prepared in accordance with claim 2, bases at each end of said tubular glass envelope, electrodes, support electrical leads electrically connected to said electrodes, said electrodes coated with an electron-emission promoting material, and a mercury droplet within said tubular glass envelope.
Claim 14
Dependent Claim
57 words
A fluorescent lamp comprising a hermetically sealed tubular glass envelope coated with a phosphor, said phosphor prepared in accordance with claim 5, bases at each end of said tubular glass envelope, electrodes, support electrical leads electrically connected to said electrodes, said electrodes coated with an electron-emission promoting material, and a mercury droplet within said tubular glass envelope.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-02-07 | 1992-08-08 | 1993-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-02-07 | 1996-08-08 | 1997-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-02-07 | 2000-08-08 | 2001-02-07 | $7700.00 | Window Closed / Lapsed |