Longitudinal magnetic recording media and magnetic memory units
Assignee: HGST Japan Ltd
•
Filing: 1989-09-26
•
Granted: 1992-09-15
•
Expires: 2009-09-26
Abstract
Abstract Disclosed are longitudinal recording media comprising a composite magnetic film formed on a nonmagnetic substrate directly or through a nonmagnetic underlayer, in which all of magnetic thin films constituting the composite magnetic film are magnetically connected, the composite magnetic film has a single in-plane coercivity, and the in-plane coercivity is greater than the in-plane coercivity of a longitudinal magnetically anisotropic magnetic thin film constituting a magnetic thin film nearest to an information recording side among the magnetic thin films constituting the composite film.
Inventors
- 👤 Yoshihiro Shiroishi
- 👤 Takeo Yamashita
- 👤 Sadao Hishiyama
- 👤 Noriyuki Kumasaka
- 👤 Yoshibumi Matsuda
- 👤 Hiroyuki Suzuki
- 👤 Kazumasa Takagi
- 👤 Norikazu Tsumita
- 👤 Masaki Ohura
- 👤 Tomoyuki Ohno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:06
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/64; G11B5/66; G11B5/672; G11B11/00; G11B11/10; G11B11/105; G11B11/10582; G11B11/10586; G11B11/10589; G11B11/10593; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10S428/922; Y10S428/9265; Y10S428/928; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
86 words
A longitudinal magnetic recording medium comprising a composite magnetic film formed on a nonmagnetic substrate directly or through a nonmagnetic underlayer, in which all of the magnetic thin metal films constituting the composite magnetic film are magnetically coupled so as to have a single in-plane coercivity, and the in-plane coercivity is greater than the in-plane coercivity of a longitudinal magnetically anisotropic magnetic thin film constituting a magnetic thin metal film nearest to an information recording side among the magnetic thin metal films constituting the composite film.
Claim 2
Dependent Claim
86 words
A longitudinal magnetic recording medium comprising a composite magnetic film formed on a nonmagnetic substrate directly or through a nonmagnetic underlayer, in which all of the magnetic thin metal films constituting the composite magnetic film are magnetically coupled so as to have a single in-plane coercivity, and the in-plane coercivity is greater than the in-plane coercivity of a longitudinal magnetically anisotropic magnetic thin film constituting a magnetic thin metal film nearest to an information recording side among the magnetic thin metal films constituting the composite film.
Claim 3
Dependent Claim
59 words
A longitudinal magnetic recording medium according to claim 1 wherein the magnetic thin metal film nearest to the information recording side has a coercivity of not less than 50 Oe and not more than 200 Oe and the magnetic thin metal film adjacent to said magnetic thin film nearest to the information recording side individually has perpendicular magnetic anisotropy.
Claim 4
Dependent Claim
33 words
A longitudinal magnetic recording medium according to claim 1 wherein the magnetic thin metal film adjacent to the magnetic thin metal film nearest to the information recording side individually has longitudinal magnetic anisotropy.
Claim 5
Dependent Claim
24 words
A longitudinal magnetic recording medium according to claim 1 wherein the composite magnetic film has an in-plane coercivity of not less than 1,000 Oe.
Claim 6
Dependent Claim
24 words
A longitudinal magnetic recording medium according to claim 1 wherein the composite magnetic film has an in-plane coercivity of not less than 1,500 Oe.
Claim 7
Dependent Claim
37 words
A longitudinal magnetic recording medium according to claim 1 wherein the magnetic thin metal film nearest to the information recording side has a higher saturation magnetization than the magnetic thin metal film nearest to the substrate side.
Claim 8
Dependent Claim
36 words
A longitudinal magnetic recording medium according to claim 6 wherein the magnetic thin metal film nearest to the substrate side has the highest in-plane coercivity among the magnetic thin metal films constituting the composite magnetic film.
Claim 9
Dependent Claim
73 words
A longitudinal magnetic recording medium according to claim 7 wherein the saturation magnetization consecutively decreases in the direction from the magnetic thin metal film nearest to the information recording side to the magnetic thin metal film nearest to the substrate side, and the in-plane coercivity consecutively increases in the direction from the magnetic thin metal film nearest to the information recording side to the magnetic thin metal film nearest to the substrate side.
Claim 10
Dependent Claim
233 words
A longitudinal magnetic recording medium having a composite magnetic film comprising at least two magnetic thin metal films formed on a nonmagnetic substrate directly or through a nonmagnetic underlayer, in which the magnetic thin metal film nearest to an information recording side is a longitudinal magnetically anisotropic magnetic thin metal film containing, as a main component, an alloy containing at least one element selected from a first group consisting of Co and Fe, and at least one element selected from a second group consisting of N, Tb, Mo, W, Gd, Y, Sm, Nd, Pr, Pm, Ce, Dy, La, Pt, Ir, Ti, Zr, Hf, V, Nb, Ta, Ru, Os, Rh, Pd, Al and Si, and/or Ni, the magnetic thin metal film nearest to the substrate side differs from the magnetic thin metal film nearest to the information recording side in components or composition and contains, as a main component an alloy containing at least one element selected from the above first group and at least one element selected from a third group consisting of Cu, Cr, Mo, W, Tb, Gd, Sm, Nd, Pm, Pr, Ce, Dy, Pt and Ir, and/or Ni, all of the magnetic thin metal films constituting the composite magnetic film are magnetically coupled so as to have a single in-plane coercivity of not less than 250 Oe in magnetization reversal of the composite magnetic film to a longitudinal head magnetic field.
Claim 11
Dependent Claim
233 words
A longitudinal magnetic recording medium having a composite magnetic film comprising at least two magnetic thin metal films formed on a nonmagnetic substrate directly or through a nonmagnetic underlayer, in which the magnetic thin metal film nearest to an information recording side is a longitudinal magnetically anisotropic magnetic thin metal film containing, as a main component, an alloy containing at least one element selected from a first group consisting of Co and Fe, and at least one element selected from a second group consisting of N, Tb, Mo, W, Gd, Y, Sm, Nd, Pr, Pm, Ce, Dy, La, Pt, Ir, Ti, Zr, Hf, V, Nb, Ta, Ru, Os, Rh, Pd, Al and Si, and/or Ni, the magnetic thin metal film nearest to the substrate side differs from the magnetic thin metal film nearest to the information recording side in components or composition and contains, as a main component an alloy containing at least one element selected from the above first group and at least one element selected from a third group consisting of Cu, Cr, Mo, W, Tb, Gd, Sm, Nd, Pm, Pr, Ce, Dy, Pt and Ir, and/or Ni, all of the magnetic thin metal films constituting the composite magnetic film are magnetically coupled so as to have a single in-plane coercivity of not less than 250 Oe in magnetization reversal of the composite magnetic film to a longitudinal head magnetic field.
Claim 12
Dependent Claim
67 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the information recording side contains at least element(s) from the above second group, and the total amount of element(s) from the above second group is not less than 0.1 at % and not more than 30 at % based on the total amount of element(s) from the above first group.
Claim 13
Dependent Claim
56 words
A longitudinal magnetic recording medium according to claim 10 wherein the magnetic thin metal film nearest to the information recording side contains at least Ni, and the amount of Ni is not less than 10 at % and not more than 60 at % based on the total amount of element(s) from the above first group.
Claim 14
Dependent Claim
65 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the substrate side contains at least element(s) from the above third group and the amount of the element(s) from the third group is not less tan 0.1 at % and not more than 30 at % based on the total amount of element(s) from the above first group.
Claim 15
Dependent Claim
55 words
A longitudinal magnetic recording medium according to claim 12 wherein the magnetic thin metal film nearest to the substrate side contains at least Ni, and the amount of Ni is not less than 10 at % and not more than 60 at % based on the total amount of element(s) from the above first group.
Claim 16
Dependent Claim
75 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the substrate side further contains not less than 0.1 at % and not more than 20 at %, based on the total amount of element(s) from the above first group, of at least one element selected from a four group consisting of Ti, Zr, Hf, Nb, Ta, Ru, Os, Rh, Pd, Al and Si, and is predominantly crystalline.
Claim 17
Dependent Claim
48 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the information recording side is a CoNi-based three-element or four-element alloy, and the magnetic thin metal film nearest to the substrate side is a CoCr-based or CoSm-based three-element or four-element alloy.
Claim 18
Dependent Claim
29 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the information recording side contains at least one of Fe and Bi.
Claim 19
Dependent Claim
44 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the information recording side has a thickness not more than 2 times as large as that of the magnetic thin metal film nearest to the substrate side.
Claim 20
Dependent Claim
35 words
A longitudinal magnetic recording medium according to claim 17 wherein the magnetic thin metal film nearest to the information recording side has a thickness not more than 5 nm and not more than 100 nm.
Claim 21
Dependent Claim
37 words
A longitudinal magnetic recording medium according to claim 17 wherein the magnetic thin metal film nearest to the information recording side has a higher saturation magnetization than the magnetic thin metal film nearest to the substrate side.
Claim 22
Dependent Claim
42 words
A longitudinal magnetic recording medium according to claim 19 wherein the magnetic thin metal film nearest to the substrate side has the highest in-plane coercivity when the coercivities of the magnetic thin metal films constituting the composite magnetic film are measured individually.
Claim 23
Dependent Claim
73 words
A longitudinal magnetic recording medium according to claim 20 wherein the saturation magnetization consecutively decreases in the direction from the magnetic thin metal film nearest to the information recording side to the magnetic thin metal film nearest to the substrate side, and the in-plane coercivity consecutively increases in the direction from the magnetic thin metal film nearest to the information recording side to the magnetic thin metal film nearest to the substrate side.
Claim 24
Dependent Claim
24 words
A longitudinal magnetic recording medium according to claim 9 wherein the composite magnetic film comprises at least three kinds of magnetic thin metal films.
Claim 25
Dependent Claim
60 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the information recording side has a coercivity of not less than 50 Oe and not more than 200 Oe and the magnetic thin metal film adjacent to the magnetic thin metal film nearest to the information recording side individually has perpendicular magnetic anisotropy.
Claim 26
Dependent Claim
33 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film adjacent to the magnetic thin metal film nearest to the information recording side individually has longitudinal magnetic anisotropy.
Claim 27
Dependent Claim
24 words
A longitudinal magnetic recording medium according to claim 8 wherein the composite magnetic film has an in-plane coercivity of not less than 1,000 Oe.
Claim 28
Dependent Claim
24 words
A longitudinal magnetic recording medium according to claim 25 wherein the composite magnetic film has an in-plane coercivity of not less than 1,500 Oe.
Claim 29
Dependent Claim
32 words
A longitudinal magnetic recording medium according to claim 9 wherein the nonmagnetic underlayer is composed of Cr, Mo, W, Ti, C, Ge or a nonmagnetic material containing these as a main component.
Claim 30
Dependent Claim
45 words
A longitudinal magnetic recording medium according to claim 9 wherein the magnetic thin metal film nearest to the information recording side further has, formed thereon, a nonmagnetic protective coating layer having a thickness of not less than 10 nm and not more than 40 nm.
Claim 31
Dependent Claim
84 words
A longitudinal magnetic recording medium comprising a composite magnetic film formed on a nonmagnetic substrate directly or through a nonmagnetic underlayer, in which the composite magnetic film is made of magnetic thin metal films and has a single in-plane coercivity and the in-plane coercivity is not less than 1,000 Oe, said in-plane coercivity being greater than the in-plane coercivity of a longitudinal anisotropic magnetic thin metal film which is nearest to an information recording side among the magnetic thin films constituting the composite film.
Claim 32
Dependent Claim
84 words
A longitudinal magnetic recording medium comprising a composite magnetic film formed on a nonmagnetic substrate directly or through a nonmagnetic underlayer, in which the composite magnetic film is made of magnetic thin metal films and has a single in-plane coercivity and the in-plane coercivity is not less than 1,000 Oe, said in-plane coercivity being greater than the in-plane coercivity of a longitudinal anisotropic magnetic thin metal film which is nearest to an information recording side among the magnetic thin films constituting the composite film.
Claim 33
Dependent Claim
20 words
A longitudinal magnetic recording medium according to claim 29 wherein the above in-plane coercivity is not less than 1,500 Oe.
Claim 34
Dependent Claim
76 words
A magnetic memory unit comprising a longitudinal magnetic recording medium having a composite magnetic film made of a plurality of magnetic thin metal films on a non-magnetic substrate and having a longitudinal recording density of not less than 100 Mb/in 2 said in plane coercivity being greater than the in-plane coercivity of a longitudinal anisotropic magnetic thin metal film which is nearest to an information recording side among the magnetic thin films constituting the composite film.
Claim 35
Dependent Claim
76 words
A magnetic memory unit comprising a longitudinal magnetic recording medium having a composite magnetic film made of a plurality of magnetic thin metal films on a non-magnetic substrate and having a longitudinal recording density of not less than 100 Mb/in 2 said in plane coercivity being greater than the in-plane coercivity of a longitudinal anisotropic magnetic thin metal film which is nearest to an information recording side among the magnetic thin films constituting the composite film.
Claim 36
Dependent Claim
21 words
A magnetic memory unit according to claim 31 wherein the longitudinal recording density is not less than 150 Mb/in 2 .
Claim 37
Dependent Claim
49 words
A magnetic memory unit comprising the longitudinal magnetic recording medium recited in claim 1 and a ring type magnetic head for reading and writing of which the magnetic core is at least partially formed of a ferromagnetic core is at least partially formed of a ferromagnetic metal thin film.
Claim 38
Dependent Claim
19 words
A magnetic memory unit comprising the magnetic recording medium recited in claim 1 and an optical head for reading.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-15 | 1996-03-16 | 1996-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-15 | 2000-03-16 | 2000-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-15 | 2004-03-16 | 2004-09-15 | $7700.00 | Window Closed / Lapsed |