Method of producing parts and molds using composite ceramic powders
Assignee: The University of Texas System
•
Filing: 1991-02-19
•
Granted: 1992-09-15
•
Expires: 2011-02-19
Abstract
Abstract A method and apparatus for selectively sintering a layer of powder to produce a part comprising a plurality of sintered layers. The apparatus includes a computer controlling a laser to direct the laser energy onto the powder to produce a sintered mass. The computer either determines or is programmed with the boundaries of the desired cross-sectional regions of the part. For each cross-section, the aim of the laser beam is scanned over a layer of powder and the beam is switched on to sinter only the powder within the boundaries of the cross-section. Powder is applied and successive layers sintered until a completed part is formed. Preferably, the powder comprises a plurality of materials having different dissociation or bonding temperatures. The powder preferably comprises blended or coated materials, including precursor materials which are formed into a mass at the irradiated locations, and which either react due to the laser thermal energy or in a later heat treatment to form a compound with properties different than the precursors. Examples are disclosed wherein a compound is formed which has a significantly higher melting point than that of one or more of the precursor powders. A ceramic part, such as a mold for investment casting, may be formed according to the method, where a first material (e.g., ammonium dihydrogen phosphate) has a melting point sufficiently low that it is melted so as to bind the second material (e.g., alumina). Subsequent heat treatment enables chemical reaction of the two materials to form a ceramic (e.g., aluminum phosphate) capable of withstanding high temperatures.
Inventors
- 👤 Harris L. Marcus
- 👤 Udaykumar Lakshminarayan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:45
CPC Classifications
G; G05; G05B; G05B19/00; G05B19/02; G05B19/18; G05B19/41; B; B05; B05C; B05C19/00; B05C19/008; B22; B22F; B22F10/00; B22F10/20; B22F10/28; B22F10/30; B22F10/38; B22F10/50; B22F3/00; B22F3/004; B22F3/10; B22F3/105; B22F7/00; B22F7/02; B23; B23K; B23K26/00; B23K26/08; B23K26/082; B23K26/34; B29; B29C; B29C41/00; B29C41/02; B29C41/12; B29C41/34; B29C41/46; B29C64/00; B29C64/10; B29C64/141; B29C64/153; B33; B33Y; B33Y10/00; B33Y70/00; B33Y70/10; C; C23; C23C; C23C24/00; C23C24/08; C23C24/10; C23C26/00; C23C26/02; B22F10/36; B22F10/366; B22F12/00; B22F12/40; B22F12/41; B22F12/44; B22F12/49; B22F2003/1052; B22F2998/00; B22F2998/10; B29C35/00; B29C35/02; B29C35/04; B29C35/045; G05B2219/00; G05B2219/30; G05B2219/49; G05B2219/49013; G05B2219/49018; Y; Y02; Y02P; Y02P10/00; Y02P10/25; Y02P90/00; Y02P90/02
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
82 words
A method of producing a part, comprising: depositing a powder onto a target surface, said powder comprising first and second materials; heating a selected portion of said powder above the melting point of said first material so that said first material binds said second material in said selected portion to define a cross-sectional region of the part; and reacting the first and second materials in said cross-sectional region of the part to form a chemical compound of said first and second materials.
Claim 2
Independent Claim
82 words
A method of producing a part, comprising: depositing a powder onto a target surface, said powder comprising first and second materials; heating a selected portion of said powder above the melting point of said first material so that said first material binds said second material in said selected portion to define a cross-sectional region of the part; and reacting the first and second materials in said cross-sectional region of the part to form a chemical compound of said first and second materials.
Claim 3
Dependent Claim
47 words
The method of claim 1, further comprising: depositing a second layer of said powder after said heating step and before said reacting step; and before said reacting step, heating a selected portion of said second layer of powder to define a second cross-sectional region of the part.
Claim 4
Dependent Claim
46 words
The method of claim 2, wherein said reacting step comprises: removing portions of the powder not within the defined cross-section of the part, after said step of heating said second layer of powder; and heating the part after said removing step to cause a chemical reaction.
Claim 5
Dependent Claim
20 words
The method of claim 1, wherein said heating step comprises: directing a laser beam at selected portions of said powder.
Claim 6
Dependent Claim
27 words
The method of claim 1, wherein said reacting step comprises: decomposing said first material into an intermediate material; and reacting said intermediate material with said second material.
Claim 7
Dependent Claim
21 words
The method of claim 1, wherein said first material comprises ammonium dihydrogen phosphate, and wherein said second material comprises aluminum oxide.
Claim 8
Dependent Claim
45 words
The method of claim 1, wherein said reacting step causes a gas to be driven off from said part; and wherein the temperature/time sequence of said reacting step is selected in such a manner as to control shrinkage of the part during said reacting step.
Claim 9
Dependent Claim
27 words
The method of claim 1, wherein said reacting step comprises: heating the part to a temperature which reduces the chemical compound of said first and second materials.
Claim 10
Dependent Claim
44 words
The method of claim 8, wherein a gas is driven off from said part during said reacting step; and wherein the temperature/time sequence of said heating step is selected in such a manner as to control shrinkage of the part during said reacting step.
Claim 11
Independent Claim
103 words
A method of investment casting a part, comprising: depositing a layer of a powder onto a target surface, said powder comprising first and second materials; heating a selected portion of said powder above the melting point of said first material so that said first material binds said second material in said selected portion to define a cross-sectional region of a mold; repeating said depositing and heating steps for additional layers of said powder, to form said mold; reacting the first and second materials in said mold to form a chemical compound of said first and second materials; casting a part in said mold.
Claim 12
Independent Claim
103 words
A method of investment casting a part, comprising: depositing a layer of a powder onto a target surface, said powder comprising first and second materials; heating a selected portion of said powder above the melting point of said first material so that said first material binds said second material in said selected portion to define a cross-sectional region of a mold; repeating said depositing and heating steps for additional layers of said powder, to form said mold; reacting the first and second materials in said mold to form a chemical compound of said first and second materials; casting a part in said mold.
Claim 13
Dependent Claim
21 words
The method of claim 10, wherein said first material comprises ammonium dihydrogen phosphate, and wherein said second material comprises aluminum oxide.
Claim 14
Dependent Claim
36 words
The method of claim 10, wherein said reacting step comprises: removing portions of the powder not within the defined cross-section of the mold; and heating the mold after said removing step to cause a chemical reaction.
Claim 15
Dependent Claim
50 words
The method of claim 12, wherein the step of heating the mold drives a gas from said part; and wherein the temperature/time sequence of the step of heating the mold is selected in such a manner as to control shrinkage of the mold during the step of heating the mold.
Claim 16
Dependent Claim
20 words
The method of claim 10, wherein said heating step comprises: directing an energy beam at selected portions of said powder.
Claim 17
Dependent Claim
27 words
The method of claim 10, wherein said reacting step comprises: decomposing said first material into an intermediate material; and reacting said intermediate material with said second material.
Claim 18
Dependent Claim
27 words
The method of claim 10, wherein said reacting step is performed at a sufficiently high temperature to reduce the chemical compound of said first and second materials.
Claim 19
Dependent Claim
52 words
The method of claim 16, wherein a gas is driven from said part during the reduction of the chemical compound of said first and second materials; and wherein the temperature/time sequence of the reacting step is selected in such a manner as to control shrinkage of the mold during said reacting step.
Claim 20
Dependent Claim
85 words
A part produced by the method comprising the steps of: depositing a powder onto a target surface, said powder comprising first and second materials; heating a selected portion of said powder above the melting point of said first material so that said first material binds said second material in said selected portion to define a cross-sectional region of the part; and reacting the first and second materials in said cross-sectional region of the part to form a chemical compound of said first and second materials.
Claim 21
Dependent Claim
85 words
A part produced by the method comprising the steps of: depositing a powder onto a target surface, said powder comprising first and second materials; heating a selected portion of said powder above the melting point of said first material so that said first material binds said second material in said selected portion to define a cross-sectional region of the part; and reacting the first and second materials in said cross-sectional region of the part to form a chemical compound of said first and second materials.
Claim 22
Dependent Claim
40 words
The part of claim 18, wherein said reacting step comprises: decomposing said first material into an intermediate material; and reacting said intermediate material with said second material, so that the compound is of said intermediate material and said second material.
Claim 23
Dependent Claim
27 words
The part of claim 19, wherein said part comprises particles of said second material bound by said chemical compound of said intermediate material and said second material.
Claim 24
Dependent Claim
14 words
The part of claim 20, wherein the part is a mold for investment casting.
Claim 25
Dependent Claim
21 words
The part of claim 18, wherein said first material comprises ammonium dihydrogen phosphate, and wherein said second material comprises aluminum oxide.
Claim 26
Dependent Claim
41 words
The part of claim 18, wherein the method further comprises: depositing a second layer of said powder after said heating step; and heating a selected portion of said second layer of powder to define a second cross-sectional region of the part.
Claim 27
Dependent Claim
46 words
The part of claim 23, wherein said reacting step comprises: removing portions of the powder not within the defined cross-section of the part, after said step of heating said second layer of powder; and heating the part after said removing step to cause a chemical reaction.
Claim 28
Dependent Claim
53 words
The part of claim 24, wherein a gas is driven from said part during the step of heating the part after said removing step; and wherein the temperature/time sequence of the step of heating the part after said removing step is selected in such a manner as to control shrinkage of the part.
Claim 29
Dependent Claim
31 words
The part of claim 24, wherein the step of heating the part after said removing step is at a temperature which reduces the chemical compound of said first and second materials.
Claim 30
Dependent Claim
54 words
The part of claim 26, wherein a gas is driven off from said part during the step of heating the part after said removing step; and wherein the temperature/time sequence of the step of heating the part after said removing step is selected in such a manner as to control shrinkage of the part.
Claim 31
Dependent Claim
44 words
The part of claim 24, wherein said heating step in said reacting step comprises: decomposing said first material into an intermediate material; and reacting said intermediate material with said second material, so that the compound is of said intermediate material and said second material.
References Cited (Backward Citations)
US4117302A
Cited
US4300474A
Cited
US4323756A
Cited
US4474861A
Cited
US4575330B1
Cited
US4575330A
Cited
JPS61296976A
Cited
EP0221276A1
Cited
US4938816A
Cited
US4863538A
Cited
WO1988002677A2
Cited
US4944817A
Cited
US5076869A
Cited
US4818562A
Cited
EP0283003A2
Cited
US5053090A
Cited
US5017317A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-15 | 1996-03-16 | 1996-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-15 | 2000-03-16 | 2000-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-15 | 2004-03-16 | 2004-09-15 | $7700.00 | Window Closed / Lapsed |