US5147490A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the production of a heat-mode recording material
Assignee: Agfa Gevaert NV
•
Filing: 1990-02-15
•
Granted: 1992-09-15
•
Expires: 2010-02-15
Abstract
Abstract A process for the production of a heat-mode recording material by coating in a sealed zone maintained under vacuum conditions a web support with a heat-mode recording layer of vapor depositable material and within the sealed zone laminating a protective organic resin layer in web form by means of an adhesive layer onto the supported heat-mode recording layer. The web support moves within the sealed zone from a delivery reel to a take-up roll with the recording layer deposited thereon in a region between the rolls and the protective layer is laminated over the recording layer before the coated web support is collected on the take-up rolls.
Inventors
- 👤 Luc H. Leenders
- 👤 Luciaan F. Voet
- 👤 Dirk M. D'hont
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:43
CPC Classifications
B; B32; B32B; B32B7/00; B32B7/04; B32B7/12; B32B27/00; B32B27/06; B32B27/08; B32B37/00; B32B37/10; B41; B41M; B41M5/00; B41M5/26; C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/20; G; G11; G11B; G11B7/00; G11B7/24; G11B7/241; G11B7/252; G11B7/254; G11B7/2542; B32B2309/00; B32B2309/60; B32B2309/68; G11B7/242; G11B7/243; G11B2007/24302; G11B2007/24314; G11B7/256
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
76 words
In a process for the production of a heat-mode recording material having "direct read after write" (DRAW) capabilities wherein a web support is coated within a sealed zone maintained under vacuum conditions with a heat-mode recording layer, the improvement of laminating a protective organic resin layer in web form onto said supported recording layer by means of an adhesive layer while said supported recording layer remains within said sealed zone and while maintaining said vacuum conditions.
Claim 2
Dependent Claim
76 words
In a process for the production of a heat-mode recording material having "direct read after write" (DRAW) capabilities wherein a web support is coated within a sealed zone maintained under vacuum conditions with a heat-mode recording layer, the improvement of laminating a protective organic resin layer in web form onto said supported recording layer by means of an adhesive layer while said supported recording layer remains within said sealed zone and while maintaining said vacuum conditions.
Claim 3
Dependent Claim
76 words
The method of claim 1, wherein said web support is unwound from a delivery reel and collected onto a take-up reel both contained within said sealed zone and said recording layer is coated onto said web support in a region intermediate said reels and which further comprises laminating said protective resin layer onto said recording layer after the same is coated onto said web support but before the coated web support is collected onto said reel.
Claim 4
Dependent Claim
32 words
A process according to claim 1, wherein the lamination of a protective layer to the heat-mode recording layer proceeds by means of a transparent or opaque pressure-sensitive or heat-sensitive adhesive resin layer.
Claim 5
Dependent Claim
15 words
A process according to claim 1, wherein said adhesive resin layer is heat-curable or UV-curable.
Claim 6
Dependent Claim
21 words
A process according to claim 1, wherein the adhesive layer has a thickness in the range of 0.1 to 15 μm.
Claim 7
Dependent Claim
23 words
A process according to claim 1, wherein said protective layer comprises a hard protective resin layer covered with a transparent adhesive resin layer.
Claim 8
Dependent Claim
23 words
A process according to claim 1, wherein said protective organic resin layer has a thickness in the range of 2 to 200 μm.
Claim 9
Dependent Claim
58 words
A process according to claim 1, wherein the heat-mode recording layer is deposited on a transparent web resin support having a thickness in the range of 50 to 200 μm and a transparent protective resin layer having a thickness in the range of 2 to 15 μm is laminated by said adhesive layer onto the heat-mode recording layer.
Claim 10
Dependent Claim
60 words
A process according to claim 1, wherein the heat-mode recording layer is coated on a transparent web resin support having a thickness in the range of 2 to 20 μm and a transparent or opaque protective resin layer having a thickness in the range of 50 to 200 μm is laminated by said adhesive layer to the heat-mode recording layer.
Claim 11
Dependent Claim
16 words
A process according to claim 1, wherein the heat-mode recording layer is a vacuum-deposited bismuth layer.
Claim 12
Dependent Claim
54 words
A process according to claim 1, wherein the adhesive layer is a pressure-sensitive adhesive layer containing at least one adhesive selected from the group of a polyterpene resin, low density polyethylene, a copoly(ethylene/vinyl acetate), a poly(C1-C16)alkyl acrylate, a mixture of poly(C1-C16)alkyl acrylate with polyvinyl acetate, and a copoly(vinyl acetate/acrylate) being tacky at 20° C.
Claim 13
Dependent Claim
38 words
A process according to claim 1, wherein said protective layer is made of a resin selected from the group consisting of a polyester, a polycarbonate, a polyamide, a styrene polymer or copolymer and a (meth)acrylate polymer or copolymer.
Claim 14
Dependent Claim
63 words
A process according to claim 1, wherein said protective organic resin layer is applied from a laminating web comprising a peelable temporary resin support having a thickness in the range of 20 to 200 μm and serving temporarily as a backing for said adhesive layer and adhered to said adhesive layer a transparent permanent resin support serving as said protective organic resin layer.
Claim 15
Dependent Claim
70 words
A process according to claim 13, wherein said laminating web is unwound from an unwinding roller before undergoing the lamination and said temporary support is peeled apart from the adhesive resin layer and is turned over 360° along the curvature of its unwinding roller and affixed on top of said permanent resin support to be carried along with the latter to effect peeling separation of the temporary support during unwinding.
Claim 16
Dependent Claim
40 words
A process according to claim 14, wherein after completion of the lamination the laminated material is removed from the sealed zone whereupon both said temporary and permanent supports are separated and said temporary support is wound on a take-up roll.
References Cited (Backward Citations)
US3279966A
Cited
US3329549A
Cited
US4267261A
Cited
US3767500A
Cited
US3837952A
Cited
US4422159A
Cited
US4818852A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-09-15 | 1996-03-16 | 1996-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-09-15 | 2000-03-16 | 2000-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-09-15 | 2004-03-16 | 2004-09-15 | $7700.00 | Window Closed / Lapsed |