Abstract The present invention relates to a ceramic whisker-containing cutting insert for chipforming machining of steel having improved mechanical, thermal and wearing properties. Besides an oxide-based matrix, the material contains 5-50, preferably 10-40, % by volume of homogeneously distributed whiskers or platelets of nitrides, carbides and/or borides of metals from group IVB (Ti, Zr or Hf) and/or VB (V, Nb or Ta) in the periodic system (or solid solutions thereof) having a linear expansion coefficient being lower than that of Al 2 O 3 , preferably at the most 85% of that for Al 2 O 3 measured at 300-1300 K. The properties of the composite material can be further modified by coating the whisker material with thin layers. The whisker reinforced cutting tool material shows an improved toughness behavior.
Oxide-based ceramic cutting insert for chipforming machining of steel, consisting essentially of a ceramic oxide-based matrix of alumina and less than 20% zirconia and 5-50% by volume, of homogeneously dispersed whiskers or platelets of nitrides, carbides and/or borides of Ta having a linear expansion coefficient measured at 300-1300 K which is at the most 85% of that of Al 2 O 3 .
Claim 2
Dependent Claim
63 words
Oxide-based ceramic cutting insert for chipforming machining of steel, consisting essentially of a ceramic oxide-based matrix of alumina and less than 20% zirconia and 5-50% by volume, of homogeneously dispersed whiskers or platelets of nitrides, carbides and/or borides of Ta having a linear expansion coefficient measured at 300-1300 K which is at the most 85% of that of Al 2 O 3 .
Claim 3
Dependent Claim
20 words
Cutting insert according to claim 1, wherein the oxide-based matrix contains 10-40% by volume of the said whiskers or platelets.
Claim 4
Dependent Claim
34 words
Cutting insert according to claim 1, wherein the whiskers or platelets have a linear expansion coefficient measured at 300-1300 K, which is at the most 70% of that of Al 2 O 3 .
Claim 5
Dependent Claim
20 words
Cutting insert according to claim 1, wherein the oxide-based matrix contains 25-35% by volume of the said whiskers or platelets.