Continuous preparation of linear high molecular weight polyamides having regulated amino and carboxyl end group content
Assignee: BASF SE
•
Filing: 1991-07-10
•
Granted: 1992-08-18
•
Expires: 2011-07-10
Abstract
Abstract Linear high molecular weight polyamides containing a regulated level of amino and carboxyl end groups are prepared in a continuous process by reacting polyamides in the melt with polyamide-forming diamines or dicarboxylic acids by continuous mixing for a residence time of ≦10 minutes, granulating the polyamide, and further condensing the polyamide granules thus obtained in solid phase in the presence of inert gases until the viscosity has reached the desired level.
Inventors
- 👤 Gunter Pipper
- 👤 Peter Hildenbrand
- 👤 Wolfgang F. Mueller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:58
CPC Classifications
C; C08; C08G; C08G69/00; C08G69/02; C08G69/26; C08G69/28
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
151 words
A process for the continuous preparation of a linear polyamide having a regulated amino and carboxyl end group content, comprising the steps of a) reacting a polyamide having a relative viscosity of 2.0 to 7.0 measured in a 1% by weight solution of the polyamide in 96% by weight of sulfuric acid at a temperature of 25° C. with a polyamide-forming diamine in the melt at a temperature not more tan 50° C. above the melting point of the polyamide by continuous mixing over a residence time of ≦10 min, b) converting the resulting polyamide into a solid granular product, and c) further condensing the resulting polyamide granules in the solid phase and in the presence of an inert gas at a temperature of rom 130° C. to 20° C. below the melting point of the particular polyamide until the viscosity and the end group content have reached the desired levels.
Claim 2
Dependent Claim
151 words
A process for the continuous preparation of a linear polyamide having a regulated amino and carboxyl end group content, comprising the steps of a) reacting a polyamide having a relative viscosity of 2.0 to 7.0 measured in a 1% by weight solution of the polyamide in 96% by weight of sulfuric acid at a temperature of 25° C. with a polyamide-forming diamine in the melt at a temperature not more tan 50° C. above the melting point of the polyamide by continuous mixing over a residence time of ≦10 min, b) converting the resulting polyamide into a solid granular product, and c) further condensing the resulting polyamide granules in the solid phase and in the presence of an inert gas at a temperature of rom 130° C. to 20° C. below the melting point of the particular polyamide until the viscosity and the end group content have reached the desired levels.
Claim 3
Dependent Claim
152 words
A process for the continuous preparation of a linear polyamide having a regulated amino and carboxyl end group content, comprising the steps of a) reacting a polyamide having a relative viscosity of 2.0 to 7.0 measured in a 1% by weight solution of the polyamide in 96% by weight of sulfuric acid at a temperature of 25° C. with a polyamide-forming dicarboxylic acid in the melt at a temperature not more than 50° C. above the melting point of the polyamide by continuous mixing over a residence time of ≦10 min, b) converting the resulting polyamide into a solid granular product, and c) further condensing the resulting polyamide granules in the solid phase and in the presence of an inert gas at a temperature of from 130° C. to 20° C. below the melting point of the particular polyamide until the viscosity and the end group content have reached the desired levels.
Claim 4
Dependent Claim
152 words
A process for the continuous preparation of a linear polyamide having a regulated amino and carboxyl end group content, comprising the steps of a) reacting a polyamide having a relative viscosity of 2.0 to 7.0 measured in a 1% by weight solution of the polyamide in 96% by weight of sulfuric acid at a temperature of 25° C. with a polyamide-forming dicarboxylic acid in the melt at a temperature not more than 50° C. above the melting point of the polyamide by continuous mixing over a residence time of ≦10 min, b) converting the resulting polyamide into a solid granular product, and c) further condensing the resulting polyamide granules in the solid phase and in the presence of an inert gas at a temperature of from 130° C. to 20° C. below the melting point of the particular polyamide until the viscosity and the end group content have reached the desired levels.
Claim 5
Dependent Claim
20 words
A process as claimed in claim 1, wherein the amino end group content is adjusted with hexamethylene-diamine,. 2,2-(4,4'-diamino)dicyclohexylpropane or 4,4'-diaminodicyclohexylmethane.
Claim 6
Dependent Claim
25 words
A process as claimed in claim 2, wherein the carboxyl end group content is adjusted with adipic acid, sebacic acid, terephthalic acid or isophthalic acid.
Claim 7
Dependent Claim
23 words
The process of claim 1, wherein a diamine is added in an amount of from 0.1 to 2% by weight, based on polyamide.
Claim 8
Dependent Claim
24 words
The process of claim 1, wherein a dicarboxylic acid is added in an amount of from 0.1 to 2% by weight, based on polyamide.
Claim 9
Dependent Claim
17 words
The process of claim 1, wherein stage a comprises a residence time of 0.5 to 2 min.
Claim 10
Dependent Claim
17 words
The process of claim 2, wherein stage a comprises a residence time of 0.5 to 2 min.
Claim 11
Dependent Claim
16 words
The process of claim 7, wherein the condensation in solid phase comprises countercurrent with superheated steam.
Claim 12
Dependent Claim
16 words
The process of claim 2, wherein the condensation in solid phase comprises countercurrent with superheated steam.
References Cited (Backward Citations)
US2174527A
Cited
US5079307A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-18 | 1996-02-17 | 1996-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-18 | 2000-02-17 | 2000-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-18 | 2004-02-17 | 2004-08-18 | $7700.00 | Window Closed / Lapsed |