Method for packaging electronic parts and adhesive for use in said method
Assignee: Panasonic Holdings Corp
•
Filing: 1990-07-26
•
Granted: 1992-08-11
•
Expires: 2010-07-26
Abstract
Abstract An adhesive composition comprising 10 to 60 parts by weight per 100 parts of the total weight of components (1) to (4) of a monofunctional (meth)acrylic monomer, 0.01 to 10 parts by weight per 100 parts of the total weight of components (1) to (4) of a compound having at least two (meth)acryloyl groups in a molecule, 30 to 80 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a heat resistant epoxy resin, 0.1 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of an imidazole compound, 0.001 to 10 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a photopolymerization initiator, and 0.01 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a thixotropic agent, with which an electronic part can be effectively packaged to a printed board.
Inventors
- 👤 Takashi Akiguchi
- 👤 Yukio Maeda
- 👤 Daisuke Irii
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:05
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/30; H05K3/303; H05K3/305; C; C09; C09J; C09J133/00; C09J133/04; C09J133/06; C09J133/10; C09J133/12; C09D; C09D4/00; C09D4/06; C09J4/00; H05K2201/00; H05K2201/10; H05K2201/10613; H05K2201/10621; H05K2201/10636; Y; Y02; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
252 words
An adhesive composition which comprises: (1) 10 to 60 parts by weight per 100 parts of the total weight of components (1) to (4) of a monofunctional (meth)acrylic monomer of the formula (I): ##STR3## wherein R 1 is a hydrogen atom or a methyl group; R 2 is a methylene group (--CH 2 --), an ethylene group (--C 2 H 4 --) or a propylene group (--C 3 H 6 --); R 3 is an alkyl group, a phenyl group which may be substituted with not more than two alkyl groups or a group of the formula: --CO--HN--R.sup.4 in which R 4 is an alkyl group; and n is 1, 2, or 3, (2) 0.01 to 10 parts weight per 100 parts of the total weight of components (1) to (4) of a compound having at least two (meth)acryloyl groups in a molecule, (3) 30 to 80 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a heat resistant epoxy resin, (4) 0.1 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of an imidazole compound, (5) 0.001 to 10 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of an photopolymerization initiator, and (6) 0.01 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a saturated aliphatic acid amide as a thixotropic agent.
Claim 2
Dependent Claim
252 words
An adhesive composition which comprises: (1) 10 to 60 parts by weight per 100 parts of the total weight of components (1) to (4) of a monofunctional (meth)acrylic monomer of the formula (I): ##STR3## wherein R 1 is a hydrogen atom or a methyl group; R 2 is a methylene group (--CH 2 --), an ethylene group (--C 2 H 4 --) or a propylene group (--C 3 H 6 --); R 3 is an alkyl group, a phenyl group which may be substituted with not more than two alkyl groups or a group of the formula: --CO--HN--R.sup.4 in which R 4 is an alkyl group; and n is 1, 2, or 3, (2) 0.01 to 10 parts weight per 100 parts of the total weight of components (1) to (4) of a compound having at least two (meth)acryloyl groups in a molecule, (3) 30 to 80 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a heat resistant epoxy resin, (4) 0.1 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of an imidazole compound, (5) 0.001 to 10 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of an photopolymerization initiator, and (6) 0.01 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a saturated aliphatic acid amide as a thixotropic agent.
Claim 3
Dependent Claim
56 words
The adhesive composition according to claim 1, wherein said monofunctional (meth)acrylate (1) is at least one compound selected from the group consisting of methoxyethyl (meth)acrylate, methoxypropyl (meth)acrylate, ethoxyethyl (meth)acrylate, ethoxypropyl (meth)acrylate, butoxyethyl (meth)acrylate, butoxypropyl (meth)acrylate, phenoxyethyl (meth)acrylate, phenoxypropyl (meth)acrylate, nonylphenoxyethyl (meth)acrylate, nonylphenoxypropyl (meth)acrylate, ethyl (meth)acrylate butylcarbamate, ethyl (meth)acrylate propylcarbamate, propyl (meth)acrylate butylcarbamate and propyl (meth)acrylate propylcarbamate.
Claim 4
Dependent Claim
42 words
The adhesive composition according to claim 1, wherein said compound having at least two (meth)acrylate group in a molecule is at least one compound selected from the group consisting of polyol poly(meth)acrylate, modified polyol poly(meth)acrylate, polyester (meth)acrylate, epoxy (meth)acrylate and urethane (meth)acrylate.
Claim 5
Dependent Claim
34 words
The adhesive composition according to claim 1, wherein said photopolymerization initiator is at least one initiator selected from the group consisting of benzoinethylether, diethoxyacetophenone, benzildimethylketal, 2-hydroxy-2-methylpropiophenone and 1-hydroxycyclohexyl phenyl ketone, benzil, benzophenone and 2,4-diethylthioxanthone.
Claim 6
Dependent Claim
31 words
The adhesive composition according to claim 1, wherein said heat resistant epoxy resin is an epoxy resin selected from the group consisting of triphenylmethanetriglycidylether, resorcinoldiglycidylether, phenol-novolac type epoxy resin and hydroxyethylisocyanuratetriglycidylether.
Claim 7
Dependent Claim
13 words
The adhesive composite according to claim 1 wherein the thixotropic agent is stearamide.
Claim 8
Dependent Claim
266 words
A photocurable adhesive composition consisting essentially of (1) 10 to 60 parts by weight per 100 parts of the total weight of components (1) to (4) of at least one monofunctional (meth)acrylic monomer selected from the group consisting of methoxyethyl (meth)acrylate, methoxypropyl (meth)acrylate, ethoxyethyl (meth)acrylate, ethoxypropyl (meth)acrylate, butoxyethyl (meth)acrylate, butoxypropyl (meth)acrylate, phenoxyethyl (meth)acrylate, phenoxypropyl (meth)acrylate, nonylphenoxyethyl (meth)acrylate, nonylphenoxypropyl (meth)acrylate, ethyl (meth)acrylate butylcarbamate, ethyl (meth)acrylate propylcarbamate, propyl (meth)acrylate butylcarbamate and propyl (meth)acrylate propylcarbamate, (2) 0.01 to 10 parts by weight per 100 parts of the total weight of components (1) to (4) of at least one compound having at least two (meth)acryloyl groups in the molecule selected from the group consisting of polyol poly(meth)acrylate, modified polyol poly(meth)acrylate, polyester (meth)acrylate, epoxy (meth)acrylate and urethane (meth)acrylate, (3) 30 to 80 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a heat resistant epoxy resin selected from the group consisting of triphenylmethanetriglycidylether, resorcinoldiglycidylether, phenol-novolac type epoxy resin and hydroxyethylisocyanuratetriglycidylether, (4) 0.1 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of an imidazole compound, (5) 0.001 to 10 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of at least one photopolymerization initiator selected from the group consisting of benzoinethylether, diethoxyacetophenone, benzildimethylketal, 2-hydroxy-2-methylpropiophenone and 1-hydroxycyclohexyl phenyl ketone, benzil, benzophenone and 2,4-diethylthioxanthone, and (6) 0.01 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a saturated aliphatic acid amide as a thixotropic agent.
Claim 9
Dependent Claim
266 words
A photocurable adhesive composition consisting essentially of (1) 10 to 60 parts by weight per 100 parts of the total weight of components (1) to (4) of at least one monofunctional (meth)acrylic monomer selected from the group consisting of methoxyethyl (meth)acrylate, methoxypropyl (meth)acrylate, ethoxyethyl (meth)acrylate, ethoxypropyl (meth)acrylate, butoxyethyl (meth)acrylate, butoxypropyl (meth)acrylate, phenoxyethyl (meth)acrylate, phenoxypropyl (meth)acrylate, nonylphenoxyethyl (meth)acrylate, nonylphenoxypropyl (meth)acrylate, ethyl (meth)acrylate butylcarbamate, ethyl (meth)acrylate propylcarbamate, propyl (meth)acrylate butylcarbamate and propyl (meth)acrylate propylcarbamate, (2) 0.01 to 10 parts by weight per 100 parts of the total weight of components (1) to (4) of at least one compound having at least two (meth)acryloyl groups in the molecule selected from the group consisting of polyol poly(meth)acrylate, modified polyol poly(meth)acrylate, polyester (meth)acrylate, epoxy (meth)acrylate and urethane (meth)acrylate, (3) 30 to 80 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a heat resistant epoxy resin selected from the group consisting of triphenylmethanetriglycidylether, resorcinoldiglycidylether, phenol-novolac type epoxy resin and hydroxyethylisocyanuratetriglycidylether, (4) 0.1 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of an imidazole compound, (5) 0.001 to 10 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of at least one photopolymerization initiator selected from the group consisting of benzoinethylether, diethoxyacetophenone, benzildimethylketal, 2-hydroxy-2-methylpropiophenone and 1-hydroxycyclohexyl phenyl ketone, benzil, benzophenone and 2,4-diethylthioxanthone, and (6) 0.01 to 20 parts by weight per 100 parts by weight of the total weight of components (1) to (4) of a saturated aliphatic acid amide as a thixotropic agent.
Claim 10
Dependent Claim
14 words
The photocurable adhesive composite according to claim 7 wherein the thixotropic agent is stearamide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-11 | 1996-02-10 | 1996-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-11 | 2000-02-10 | 2000-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-11 | 2004-02-10 | 2004-08-11 | $7700.00 | Window Closed / Lapsed |