Method for applying a solder resist layer to a printed circuit board
Assignee: Siemens AG
•
Filing: 1990-12-21
•
Granted: 1992-07-28
•
Expires: 2010-12-21
Abstract
Abstract A solder resist and a positively-acting photoresist are successively applied on a surface-wide basis onto a printed circuit board, whereupon the photoresist is selectively exposed and developed in the region of plated-through holes and/or solder pads of a printed conductor pattern carried on the printed circuit board, preferably with the assistance of laser beams. Subsequently, the solder resist is stripped in the regions not protected by the photoresist, i.e. in the regions of plated-through holes and/or solder pads and, as a last step, the remaining photoresist is likewise stripped. The method is particularly suited for the application of a solder resist layer onto three-dimensional printed circuit boards since traditional mask techniques for structuring the solder resist cannot be employed with respect to three-dimensional printed circuit boards.
Inventors
- 👤 Hans-Fr. Schmidt
- 👤 Helmut Hadwiger
- 👤 Milan Prochazka
- 👤 Eddy Roelants
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 02:10
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/26; H; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K2201/00; H05K2201/09; H05K2201/09009; H05K2201/09118; H05K2203/00; H05K2203/05; H05K2203/0562; H05K2203/0585; H05K2203/10; H05K2203/107; H05K2203/11; H05K2203/1105
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
118 words
A method for applying a solder resist layer onto a printed circuit board while leaving solder pads and plated-through holes as solderable elements of a printed conductor pattern carried on the printed circuit board free of the solder resist, comprising the steps of: (a) applying a layer of solder resist onto the printed circuit board to cover the printed conductor pattern; (b) applying a layer of positively-acting photoresist to cover the layer of solder resist; (c) selectively exposing regions of the photoresist layer which lie above the solderable elements with light; (d) removing the exposed regions of the photoresist layer and the solder resist therebelow; and (e) removing the unexposed regions of the photoresist with a stripper solution.
Claim 2
Independent Claim
118 words
A method for applying a solder resist layer onto a printed circuit board while leaving solder pads and plated-through holes as solderable elements of a printed conductor pattern carried on the printed circuit board free of the solder resist, comprising the steps of: (a) applying a layer of solder resist onto the printed circuit board to cover the printed conductor pattern; (b) applying a layer of positively-acting photoresist to cover the layer of solder resist; (c) selectively exposing regions of the photoresist layer which lie above the solderable elements with light; (d) removing the exposed regions of the photoresist layer and the solder resist therebelow; and (e) removing the unexposed regions of the photoresist with a stripper solution.
Claim 3
Dependent Claim
50 words
The method of claim 1, wherein the step (a) of applying a layer of solder resist is further defined as: (a1) applying a layer of thermally-curable solder resist; and further comprising the step of: (f) after the step (e), heating the printed circuit board to cure the remaining solder resist.
Claim 4
Dependent Claim
30 words
The method of claim 2, wherein the step (f) of heating is further defined as: (f1) heating the printed circuit board at a temperature of 120° C. for 30 minutes.
Claim 5
Dependent Claim
34 words
The method of claim 1, wherein the step (a) of applying a layer of solder resist is further defined as: (a1) applying the solder resist to a thickness in the range of 20-30 μm.
Claim 6
Dependent Claim
33 words
The method of claim 1, wherein the step (a) of applying a layer of solder resist is further defined as: (a1) dipping the printed circuit board into a bath of the solder resist.
Claim 7
Dependent Claim
30 words
The method of claim 1, wherein the step (a) of applying a layer of solder resist is further defined as: (a1) spraying the printed circuit board with the solder resist.
Claim 8
Dependent Claim
34 words
The method of claim 1, wherein the step (b) of applying a layer of positively-acting photoresist is further defined as: (b1) dipping the solder-resist covered printed circuit board into a bath of the photoresist.
Claim 9
Dependent Claim
35 words
The method of claim 1, wherein the step (b) of applying a layer of positively-acting photoresist is further defined as: (b1) spraying the printed circuit board with the photoresist to cover the solder resist thereon.
Claim 10
Dependent Claim
25 words
The method of claim 1, wherein the step (c) of selectively exposing is further defined as: (c1) selectively radiating the regions with a laser beam.
Claim 11
Dependent Claim
37 words
The method of claim 1, wherein the step (c) of selectively exposing is further defined as: (c1) operating a laser device in accordance with a predetermined scan program to control tracing and exposure by a laser beam.
Claim 12
Dependent Claim
32 words
The method of claim 1, wherein the step (d) of removing the exposed regions and the solder resist therebelow is further defined as: (d1) applying a developer to remove the exposed regions.
Claim 13
Dependent Claim
52 words
The method of claim 11, wherein the step (d) of removing the exposed regions and the solder resist therebelow is further defined as comprising the step of: (d2) applying a stripper to remove the regions of solder resist uncovered by the removal of the exposed regions of photoresist in the step (d1).
Claim 14
Dependent Claim
54 words
The method of claim 11, wherein the step (d) of removing the exposed regions and the solder resist therebelow is further defined as comprising the step of: (d2) applying an aqueous alkaline solution to remove the regions of solder resist uncovered by the removal of the exposed regions of photoresist in the step (d1).
Claim 15
Dependent Claim
53 words
The method of claim 11, wherein the step (d) of removing the exposed regions and the solder resist therebelow is further defined as comprising the step of: (d2) applying an organic solvent to remove the regions of solder resist uncovered by the removal of the exposed regions of photoresist in the step (d1).
Claim 16
Dependent Claim
51 words
The method of claim 11, wherein the step (d) of removing the exposed regions and the solder resist therebelow is further defined as comprising the step of: (d2) applying butyldiglycol to remove the regions of solder resist undercovered by the removal of the exposed regions of photoresist in the step (d1).
Claim 17
Dependent Claim
38 words
The method of claim 1, wherein the step (d) of removing the exposed regions and the solder resist therebelow is further defined as: (d1) applying an organic solvent to the exposed regions and to the solder resist therebelow.
Claim 18
Dependent Claim
43 words
The method of claim 1, wherein the step (d) of removing is further defined as: (d1) removing the exposed regions and the solder resist therebelow by applying a developing solution which is common to dissolve both the exposed photoresist and the solder resist.
Claim 19
Independent Claim
164 words
A method for applying a solder resist layer onto a printed circuit board while leaving solder pads and plated-through holes as solderable elements of a printed conductor pattern carried on the printed circuit board free of the solder resist, comprising the steps of: (a) applying a layer of solder resist over and to cover a surface of the printed circuit board including the printed conductor pattern and at a thickness in the range of 20-30 μm; (b) applying a layer of positively-acting photoresist to cover the layer of solder resist; (c) operating a laser beam emitting device in accordance with a predetermined scan program to trace and expose the regions of the photoresist which lie above the solderable elements; (d) removing the exposed regions of photoresist by developing the same in an organic developer; (e) stripping the regions of solder resist uncovered by removal of the exposed regions by applying an organic solvent thereto; and (f) removing the unexposed photoresist with a stripper solution.
Claim 20
Independent Claim
164 words
A method for applying a solder resist layer onto a printed circuit board while leaving solder pads and plated-through holes as solderable elements of a printed conductor pattern carried on the printed circuit board free of the solder resist, comprising the steps of: (a) applying a layer of solder resist over and to cover a surface of the printed circuit board including the printed conductor pattern and at a thickness in the range of 20-30 μm; (b) applying a layer of positively-acting photoresist to cover the layer of solder resist; (c) operating a laser beam emitting device in accordance with a predetermined scan program to trace and expose the regions of the photoresist which lie above the solderable elements; (d) removing the exposed regions of photoresist by developing the same in an organic developer; (e) stripping the regions of solder resist uncovered by removal of the exposed regions by applying an organic solvent thereto; and (f) removing the unexposed photoresist with a stripper solution.
Claim 21
Dependent Claim
51 words
The method of claim 18, wherein the step (a) of applying a layer of solder resist is further defined as: (a1) applying a heat-curable solder resist; and further comprising the step of: (g) heating the printed circuit board at a predetermined temperature for a predetermined time to cure the solder resist.
Claim 22
Independent Claim
178 words
A method for applying a solder resist layer onto a printed circuit board while leaving solder pads and plated-through holes as solderable elements of a printed conductor pattern carried on the printed circuit board free of the solder resist, comprising the steps of: (a) applying a layer of solder resist which is soluble in a predetermined developer to cover a surface of the printed circuit board including the printed conductor pattern and at a thickness in the range of 20-30 μm; (b) applying a layer of positively-acting photoresist, which is also soluble when exposed to radiation, in the predetermined developer to cover the layer of solder resist; (c) operating a laser beam emitting device in accordance with a predetermined scan program to trace and expose the regions of the photoresist which lie above the solderable elements to the radiation of the laser beam; (d) removing the exposed regions of photoresist and the uncovered regions of solder resist therebelow by developing the dissolving the same with the predetermined developer; and (e) removing the unexposed photoresist with a stripper solution.
Claim 23
Independent Claim
178 words
A method for applying a solder resist layer onto a printed circuit board while leaving solder pads and plated-through holes as solderable elements of a printed conductor pattern carried on the printed circuit board free of the solder resist, comprising the steps of: (a) applying a layer of solder resist which is soluble in a predetermined developer to cover a surface of the printed circuit board including the printed conductor pattern and at a thickness in the range of 20-30 μm; (b) applying a layer of positively-acting photoresist, which is also soluble when exposed to radiation, in the predetermined developer to cover the layer of solder resist; (c) operating a laser beam emitting device in accordance with a predetermined scan program to trace and expose the regions of the photoresist which lie above the solderable elements to the radiation of the laser beam; (d) removing the exposed regions of photoresist and the uncovered regions of solder resist therebelow by developing the dissolving the same with the predetermined developer; and (e) removing the unexposed photoresist with a stripper solution.
Claim 24
Dependent Claim
51 words
The method of claim 20, wherein the step (a) of applying a layer of solder resist is further defined as: (a1) applying a heat-curable solder resist; and further comprising the step of: (g) heating the printed circuit board at a predetermined temperature for a predetermined time to cure the solder resist.
References Cited (Backward Citations)
US4180604A
Cited
US4459320A
Cited
US4689657A
Cited
US4966827A
Cited
US4608274A
Cited
US4673458A
Cited
US4745045A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-28 | 1996-01-27 | 1996-07-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-28 | 2000-01-27 | 2000-07-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-28 | 2004-01-27 | 2004-07-28 | $7700.00 | Window Closed / Lapsed |