Assignee: SRI International Inc
•
Filing: 1989-06-14
•
Granted: 1992-07-28
•
Expires: 2009-06-14
Abstract
Abstract The present invention relates to solid materials for use as electrolyte for a fuel cell, or for a sensor, or as a catalyst. Representative structures include lanthanum fluoride, lead potassium fluoride, lead bismuth fluoride, lanthanum strontium fluoride, lanthan strontium lithium fluoride, calcium uranium, cesium fluoride, PbSnFy, KSn2F4, SrCl2.KCl, LaOF2, PbSnF8.PbSnO, lanthanum oxyfluoride, oxide, calcium fluoride, SmNdFO, and the like. In another aspect, the present invention relates to a composite and a process to obtain it of the formula: A1-yByQO3 having a perovskite or a perovskite-type structure as an electrode catalyst in combination with: AyB1-yF2+y as a discontinuous surface coating solid electrolyte solid electrolyte wherein A is independently selected from lanthanum, cerium, neodymium, praseodymium, and scandium, B is independently selected from strontium, calcium barium or magnesium, Q is independently selected from nickel, cobalt, iron or manganese, and y is between about 0.0001 and 1, which process comprises: (a) obtaining a particulate of: A1-yByQO3 wherein A, B and y are defined hereinabove having an average size distribution of between about 50 and 200 Angstroms in diameter; (b) reacting the particle of step (a) with a vapor comprising: AyB1-yF2+y wherein A, B and y are defined hereinabove, at about ambient pressure at between about 0 DEG and 1000 DEG C.: for between about 10 and 30 hr. obtain a composite of between about 25 to 1000 microns in thickness; (c) recovering the composite of step (b) having multiple interfaces between the electrode and electrolyte. In another aspect the invention relates to the heating of these solid materials with oxygen and water to obtain higher ionic conductivity. In another aspect the invention relates to the electrochemical doping of oxide ions present by treatment of the electrode-lanthanum fluoride interface at between about 0 DEG and 400 DEG C. in an oxygen environment at between about 10-3 and 10-6 amperes per square centimeter for between about 1 and 60 minutes. The invention also includes the use of the fuel cells disclosed to generate electricity.
Inventors
- 👤 Marc J. Madou
- 👤 Takaaki Otagawa
- 👤 Arden Sher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:44
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4073; B; B01; B01J; B01J23/00; B01J23/002; B01J27/00; B01J27/06; B01J27/08; B01J27/12; B01J37/00; B01J37/02; B01J37/024; H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M8/00; H01M8/10; H01M8/12; H01M8/124; B01J2523/00; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
213 words
The use of a solid material as an electrolyte for a fuel cell or for use as a catalyst, each solid material having a polycrystal or single crystal structure, comprising: (d) a structure of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A is independently selected from lanthanum, cerium, neodymium, praseodymium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; (e) a structure of the formula: A.sub.y B.sub.1-y-z LiF.sub.i+y+z wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; (f) a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; (j) a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3, wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof.
Claim 2
Dependent Claim
213 words
The use of a solid material as an electrolyte for a fuel cell or for use as a catalyst, each solid material having a polycrystal or single crystal structure, comprising: (d) a structure of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A is independently selected from lanthanum, cerium, neodymium, praseodymium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; (e) a structure of the formula: A.sub.y B.sub.1-y-z LiF.sub.i+y+z wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; (f) a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; (j) a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3, wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof.
Claim 3
Dependent Claim
32 words
The use of a solid material as an electrolyte for a fuel cell of claim 1 wherein the fuel cell has a useful operational temperature range of between 0° and 1000° C.
Claim 4
Dependent Claim
229 words
A process for the pretreatment of an electrolyte for a fuel cell, which process comprises: reacting a structure of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A is independently selected from lanthanum, cerium, neodynium, praseodymium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; a structure of the formula: A.sub.y B.sub.1-y-z LiF.sub.2+y+z wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; or a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3 wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof in an atmosphere comprising a mixture of oxygen and water is present in between about 1 and 99% by weight at between 100° and 1000° C. for between about 10 and 50 hrs.
Claim 5
Dependent Claim
229 words
A process for the pretreatment of an electrolyte for a fuel cell, which process comprises: reacting a structure of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A is independently selected from lanthanum, cerium, neodynium, praseodymium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; a structure of the formula: A.sub.y B.sub.1-y-z LiF.sub.2+y+z wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; or a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3 wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof in an atmosphere comprising a mixture of oxygen and water is present in between about 1 and 99% by weight at between 100° and 1000° C. for between about 10 and 50 hrs.
Claim 6
Dependent Claim
205 words
A process for preparing a composite comprising: A.sub.1-y B.sub.y QO.sub.3 having a perovskite or a perovskite-type structure as an electrode catalyst in combination with A.sub.y B.sub.1-y F.sub.2+y as a discontinuous surface coating solid electrolyte wherein A is independently selected from lanthanum, cerium, neodymium, praseodymium, or scandium, B is independently selected from strontium, calcium, barium, or magnesium, Q is independently selected from nickel, cobalt, iron or manganese, and y is between about 0.0001 and 1, which process comprises: (a) obtaining a particulate of: A.sub.1-y B.sub.y QO.sub.3 wherein A, B, Q and y are defined hereinabove having an average size distribution of between about 50 and 200 Angstroms in diameter; (b) contacting the particles of step (a) with a vapor comprising: A.sub.y B.sub.1-y F.sub.2+y wherein A, B and y are defined hereinabove, at about ambient pressure at between about 0° and 1000° C., for between about 10 and 30 hr to obtain a composite of between about 25 to 1000 microns in thickness; (c) recovering the composite of step (b) having multiple interfaces between: A.sub.1-y B.sub.y QO.sub.3 and A.sub.y B.sub.1-y F.sub.2+y said composite having a pore size of between about 25 and 200 Angstroms and a surface area of between about 10 and 100 meters 2 /gram.
Claim 7
Dependent Claim
205 words
A process for preparing a composite comprising: A.sub.1-y B.sub.y QO.sub.3 having a perovskite or a perovskite-type structure as an electrode catalyst in combination with A.sub.y B.sub.1-y F.sub.2+y as a discontinuous surface coating solid electrolyte wherein A is independently selected from lanthanum, cerium, neodymium, praseodymium, or scandium, B is independently selected from strontium, calcium, barium, or magnesium, Q is independently selected from nickel, cobalt, iron or manganese, and y is between about 0.0001 and 1, which process comprises: (a) obtaining a particulate of: A.sub.1-y B.sub.y QO.sub.3 wherein A, B, Q and y are defined hereinabove having an average size distribution of between about 50 and 200 Angstroms in diameter; (b) contacting the particles of step (a) with a vapor comprising: A.sub.y B.sub.1-y F.sub.2+y wherein A, B and y are defined hereinabove, at about ambient pressure at between about 0° and 1000° C., for between about 10 and 30 hr to obtain a composite of between about 25 to 1000 microns in thickness; (c) recovering the composite of step (b) having multiple interfaces between: A.sub.1-y B.sub.y QO.sub.3 and A.sub.y B.sub.1-y F.sub.2+y said composite having a pore size of between about 25 and 200 Angstroms and a surface area of between about 10 and 100 meters 2 /gram.
Claim 8
Dependent Claim
16 words
The process of claim 4 wherein A is lanthanum, B is strontium, and Q is cobalt.
Claim 9
Dependent Claim
10 words
The process of claim 5 wherein y is about 0.3.
Claim 10
Dependent Claim
36 words
The process of claim 4 wherein A is selected from cerium or scandium, B is selected from strontium or magnesium, Q is selected from nickel, cobalt or manganese and y is between about 0.2 and 0.4.
Claim 11
Dependent Claim
9 words
The composite obtained by the process of claim 4.
Claim 12
Dependent Claim
9 words
The composite obtained by the process of claim 5.
Claim 13
Dependent Claim
9 words
The composite obtained by the process of claim 6.
Claim 14
Dependent Claim
9 words
The composite obtained by the process of claim 7.
Claim 15
Dependent Claim
160 words
The use of a composite as a solid electrolyte or as a catalyst said composite consisting essentially of A.sub.1-y B.sub.y QO.sub.3 having a perovskite or a perovskite-type structure as a solid electrode catalyst in combination with: A.sub.y B.sub.1-y F.sub.2+y as a discontinuous surface coating solid electrolyte on the perovskite wherein A is independently selected from lanthanum, cerium, neodymium, praseodymium, or scandium, B is independently selected from strontium, calcium, barium or magnesium, Q is independently selected from nickel, cobalt, iron or manganese, and y is between about 0.0001 and 1, wherein the perovskite or perovskite-type structure has an average size and distribution of between about 50 and 200 Angstroms in diameter; and the composite layer of between about 25 and 1000 microns in thickness; said composite having multiple interfaces between: A.sub.1-y B.sub.y QO.sub.3 and A.sub.y B.sub.1-y F.sub.2+y and a pore size of between about 20 and 200 Angstroms and a surface area of between about 10 and 100 meters 2 /gram.
Claim 16
Dependent Claim
160 words
The use of a composite as a solid electrolyte or as a catalyst said composite consisting essentially of A.sub.1-y B.sub.y QO.sub.3 having a perovskite or a perovskite-type structure as a solid electrode catalyst in combination with: A.sub.y B.sub.1-y F.sub.2+y as a discontinuous surface coating solid electrolyte on the perovskite wherein A is independently selected from lanthanum, cerium, neodymium, praseodymium, or scandium, B is independently selected from strontium, calcium, barium or magnesium, Q is independently selected from nickel, cobalt, iron or manganese, and y is between about 0.0001 and 1, wherein the perovskite or perovskite-type structure has an average size and distribution of between about 50 and 200 Angstroms in diameter; and the composite layer of between about 25 and 1000 microns in thickness; said composite having multiple interfaces between: A.sub.1-y B.sub.y QO.sub.3 and A.sub.y B.sub.1-y F.sub.2+y and a pore size of between about 20 and 200 Angstroms and a surface area of between about 10 and 100 meters 2 /gram.
Claim 17
Dependent Claim
14 words
The use of the composite of claim 12 which further includes an inorganic support.
Claim 18
Dependent Claim
226 words
A process for the generation of electricity, which process comprises: contacting one side of the solid material of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A independently selected from lanthanum, cerium, neodynium, praseodymium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; a structure of the formula: A.sub.y B.sub.1-y-2 LiF.sub.2+y+2 wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; or a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3 wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof and a first electrode with a fuel at between about 0° and 1000° C., and contacting the second side of the solid electrolyte and second electrode with air, oxygen, or mixtures thereof.
Claim 19
Dependent Claim
226 words
A process for the generation of electricity, which process comprises: contacting one side of the solid material of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A independently selected from lanthanum, cerium, neodynium, praseodymium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; a structure of the formula: A.sub.y B.sub.1-y-2 LiF.sub.2+y+2 wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; or a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3 wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof and a first electrode with a fuel at between about 0° and 1000° C., and contacting the second side of the solid electrolyte and second electrode with air, oxygen, or mixtures thereof.
Claim 20
Dependent Claim
43 words
The process of claim 14 wherein the fuel for the fuel cell is selected from hydrogen, hydrazine, ammonia, fossil fuels, separate components of fossil fuels, or mixtures thereof, wherein all fuels have a boiling point at ambient pressure of 250° C. or less.
Claim 21
Dependent Claim
16 words
The process of claim 15 wherein the operating temperature is between about 10° and 30° C.
Claim 22
Dependent Claim
257 words
A process for the pretreatment of an electrolyte for a fuel cell which process comprises: subjecting the equivalent of about one gram of a solid material of a structure of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A is independently selected from lanthanum, cerium, neodynium, praseodynium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; a structure of the formula: A.sub.y B.sub.1-y-z LiF.sub.2+y+z wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; or a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3 wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal, which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof to a current of about 10 -3 amperes per square centimeter for a time sufficient to transmit a certain amount of coulombs equivalent to a product of one Faraday (coulombs/mole) times X where X is between about 0.001 and 1 at a temperature of between about 0° and 400° C.
Claim 23
Dependent Claim
257 words
A process for the pretreatment of an electrolyte for a fuel cell which process comprises: subjecting the equivalent of about one gram of a solid material of a structure of the formula: A.sub.y B.sub.1-y F.sub.2+y wherein: A is independently selected from lanthanum, cerium, neodynium, praseodynium, scandium or mixtures thereof, B is independently selected from strontium, calcium, barium or magnesium, and y is between about 0.0001 and 1; a structure of the formula: A.sub.y B.sub.1-y-z LiF.sub.2+y+z wherein A, B and y are as defined hereinabove, z is between about 0.0001 and 0.10; a structure of the formula: N.sub.1-n-m U.sub.n Ce.sub.m F.sub.2+2n+m wherein N is independently selected from calcium, strontium or barium, n is between about 0.0001 and 0.05, and m is between about 0.0001 and 0.35; or a structure of the formula: LaO.sub.1-p F.sub.1+2p wherein p is between about 0.1 and 0.3 wherein the solid material as an electrolyte for a fuel cell is a thin layer having one side coated with a noble metal, which is in contact with a gaseous fuel for a fuel cell and the other side of the thin solid material for the electrolyte is also coated with a noble metal which is in contact with gaseous oxygen, or air or mixtures thereof to a current of about 10 -3 amperes per square centimeter for a time sufficient to transmit a certain amount of coulombs equivalent to a product of one Faraday (coulombs/mole) times X where X is between about 0.001 and 1 at a temperature of between about 0° and 400° C.
References Cited (Backward Citations)
DE1442686A1
Cited
FR2330127A1
Cited
GB2002739A
Cited
FR2403652A2
Cited
US4402924A
Cited
DE3112739A1
Cited
JPS61132855A
Cited
EP0194380A2
Cited
US4851303A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-28 | 1996-01-27 | 1996-07-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-28 | 2000-01-27 | 2000-07-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-28 | 2004-01-27 | 2004-07-28 | $7700.00 | Window Closed / Lapsed |