Dielectric ceramic compositions and manufacturing method of dielectric ceramics
Assignee: Murata Manufacturing Co Ltd
•
Filing: 1991-07-09
•
Granted: 1992-07-14
•
Expires: 2011-07-09
Abstract
Abstract The dielectric ceramic composite according to the invention contains at least one kind of lanthanum oxide, cerium oxide, neodymium oxide, praseodymium oxide and samarium oxide at an amount of 2.5-5.0 mol % and zirconium oxide, tin oxide and titanium oxide at an amount of 0.5-8.5 mol% in a formula (Zr 1-a-b Sn a Ti b ) O 3 (where a>0, b≧0, 0<a+b≦1.0) to barium titanate of 100 mol % containing alkali metal oxide less than 0.03% by weight as an impurity. Barium zirconate and barium stannate at an amount of 0.5-5.0 mol % in a formula Ba (Zr 1-a Sn a ) O 3 (where 0<a≦1.0) and titanium oxide at an amount of 1.5-6.0 mol % may be added instead of zirconium oxide, tin oxide, titanium oxide. The manufacturing method of dielectric ceramic according to the invention is a method which comprises a process of firing, in an atmosphere of 60% or more oxygen concentration, moldings of a composition containing at least one kind of a lanthanum compound, cerium compound, neodymium compound, praseodymium compound, and a samarium compound and further containing a zirconium compound, tin compound, and a titanium compound to a barium titanate base material.
Inventors
- 👤 Harunobu Sano
- 👤 Nobuyuki Wada
- 👤 Yoshiaki Kohno
- 👤 Yukio Sakabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 16:33
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; H; H01; H01B; H01B3/00; H01B3/02; H01B3/12; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1236; H01G4/1245
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
85 words
A dielectric ceramic composition containing at least one compound selected from the group consisting of lanthanum oxide, cerium oxide, neodymium oxide, praseodymium oxide and samarium oxide in an amount of 2.5-5.0 mol %, zirconium oxide, tin oxide and titanium oxide in an amount of 0.5-8.5 mol % according to a formula (Zr 1-a-b Sn a Ti b )O 2 (where a>0, b≧0, 0<a+b≦1.0), and barium titanate in an amount of 86.5-97.0 mol %, containing alkali metal oxide less than 0.03% by weight as an impurity.
Claim 2
Dependent Claim
85 words
A dielectric ceramic composition containing at least one compound selected from the group consisting of lanthanum oxide, cerium oxide, neodymium oxide, praseodymium oxide and samarium oxide in an amount of 2.5-5.0 mol %, zirconium oxide, tin oxide and titanium oxide in an amount of 0.5-8.5 mol % according to a formula (Zr 1-a-b Sn a Ti b )O 2 (where a>0, b≧0, 0<a+b≦1.0), and barium titanate in an amount of 86.5-97.0 mol %, containing alkali metal oxide less than 0.03% by weight as an impurity.
Claim 3
Dependent Claim
88 words
A dielectric ceramic composition containing at least one compound selected from the group consisting of lanthanum oxide, cerium oxide, neodymium oxide, praseodymium oxide and samarium oxide in an amount of 2.5-5.0 mol %, barium zirconate and barium stannate in an amount of 0.5-5.0 mol % according to a formula Ba(Zr 1-a Sn a )O 3 (where 0<a≦1.0), titanium oxide in an amount of 1.5-6.0 mol %, and barium titanate in an amount of 86.5-95.5 mol %, containing alkali metal oxide less than 0.03% by weight as an impurity.
Claim 4
Dependent Claim
88 words
A dielectric ceramic composition containing at least one compound selected from the group consisting of lanthanum oxide, cerium oxide, neodymium oxide, praseodymium oxide and samarium oxide in an amount of 2.5-5.0 mol %, barium zirconate and barium stannate in an amount of 0.5-5.0 mol % according to a formula Ba(Zr 1-a Sn a )O 3 (where 0<a≦1.0), titanium oxide in an amount of 1.5-6.0 mol %, and barium titanate in an amount of 86.5-95.5 mol %, containing alkali metal oxide less than 0.03% by weight as an impurity.
Claim 5
Independent Claim
99 words
A method of manufacturing a dielectric ceramic composition comprising the steps of: preparing a molded composition containing at least one compound selected from the group consisting of lanthanum oxide, cerium oxide, neodymium oxide, praseodymium oxide, and samarium oxide in an amount of 2.5-5.0 mol %; zirconium oxide, tin oxide and titanium oxide in an amount of 0.5-8.5 mol % according to a formula (Zr 1-a-b Sn a Ti b )O 2 (where a>0, b≧0, 0<a+b≦1.0); and barium titanate in an amount of 86.5-97.0 mol % and firing said molded composition in an atmosphere of 60% or more oxygen concentration.
Claim 6
Independent Claim
99 words
A method of manufacturing a dielectric ceramic composition comprising the steps of: preparing a molded composition containing at least one compound selected from the group consisting of lanthanum oxide, cerium oxide, neodymium oxide, praseodymium oxide, and samarium oxide in an amount of 2.5-5.0 mol %; zirconium oxide, tin oxide and titanium oxide in an amount of 0.5-8.5 mol % according to a formula (Zr 1-a-b Sn a Ti b )O 2 (where a>0, b≧0, 0<a+b≦1.0); and barium titanate in an amount of 86.5-97.0 mol % and firing said molded composition in an atmosphere of 60% or more oxygen concentration.
Claim 7
Dependent Claim
23 words
A method as in claim 3, wherein said barium titanate contains less than 0.03% by weight of alkali metal oxide as an impurity.
Claim 8
Independent Claim
104 words
A method of manufacturing a dielectric ceramic composition comprising the steps of: preparing a molded composition containing at least one compound selected from the group consisting of a lanthanum compound, a cerium compound, a neodymium compound, a praseodymium compound, and samarium compound in an amount of 2.5-5.0 mol %; zirconium compound, a tin compound and a titanium compound in an amount of 0.5-8.5 mol % according to a formula (Zr 1-a-b Sn a Ti b ) (where a>0, b≧0, 0<a+b≦1.0); and barium titanate in an amount of 86.5-97.0 mol % and firing said molded composition, in an atmosphere of 60% or more oxygen concentration.
Claim 9
Independent Claim
104 words
A method of manufacturing a dielectric ceramic composition comprising the steps of: preparing a molded composition containing at least one compound selected from the group consisting of a lanthanum compound, a cerium compound, a neodymium compound, a praseodymium compound, and samarium compound in an amount of 2.5-5.0 mol %; zirconium compound, a tin compound and a titanium compound in an amount of 0.5-8.5 mol % according to a formula (Zr 1-a-b Sn a Ti b ) (where a>0, b≧0, 0<a+b≦1.0); and barium titanate in an amount of 86.5-97.0 mol % and firing said molded composition, in an atmosphere of 60% or more oxygen concentration.
Claim 10
Dependent Claim
137 words
A method in claim 5, wherein said compounds are selected from the group consisting of La 2 CO 3 , La(NO 3 ) 2 , La(C 2 O 4 ) 3 , CeCO 3 , Ce(NO 3 ) 3 , Ce(OH) 4 , Nd(OH) 3 , Nd(NO 3 ) 3 , Nd 2 (CO 3 ) 3 , Nd 2 (C 2 O 4 ) 3 , Pr 2 (CO 3 ) 3 , Pr(NO 3 ) 3 , Sm 2 (C 2 O 4 ) 3 , Sm(NO 3 ) 3 , BaZrO 3 , CaZrO 3 , ZrCl 4 , ZrO(NO 3 ) 2 , ZrO(CH 3 COO) 2 , BaSnO 3 , CaSnO 3 , Sn(OCH 3 ) 4 , BaTiO 3 , CaTiO 3 , TiCl 4 and Ti(OCH 3 ) 4 .
Claim 11
Dependent Claim
23 words
A method as in claim 5, wherein said barium titanate contains less than 0.03% by weight of alkali metal oxide as an impurity.
References Cited (Backward Citations)
JPS508800A
Cited
JPS5054900A
Cited
JPS5067500A
Cited
DE2637762A1
Cited
US4535064A
Cited
US4764494A
Cited
US4767732A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-14 | 1996-01-13 | 1996-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-14 | 2000-01-13 | 2000-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-14 | 2004-01-13 | 2004-07-14 | $7700.00 | Window Closed / Lapsed |