Ceramic compositions for a reduction-reoxidation type semiconducting capacitor
Assignee: Murata Manufacturing Co Ltd
•
Filing: 1984-05-24
•
Granted: 1985-08-13
•
Expires: 2004-05-24
Abstract
Abstract Ceramic compositions having (1) a mixture comprised of barium titanate, zirconium oxide and one or more of cerium oxide, neodymium oxide, lanthanum oxide and an oxide of at least one of lanthanides having atomic numbers 59 to 66 in specific ratios and (2) 0.01 to 0.4% by weight (calculated as Mn based on the weight of the mixture) manganese oxide. Such compositions form reduction-reoxidation type semiconducting capacitors of reduced size and increased capacitance per unit area.
Inventors
- 👤 Yasunobu Yoneda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:00
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1272; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
58 words
A ceramic composition for a reduction-reoxidation type semiconducting capacitor, said composition comprising (1) a mixture of 79.0 to 98.0 mole % barium titanate, 1.0 to 6.0 mole % cerium oxide and 1.0 to 15.0 mole % zirconium oxide and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
Claim 2
Dependent Claim
58 words
A ceramic composition for a reduction-reoxidation type semiconducting capacitor, said composition comprising (1) a mixture of 79.0 to 98.0 mole % barium titanate, 1.0 to 6.0 mole % cerium oxide and 1.0 to 15.0 mole % zirconium oxide and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
Claim 3
Dependent Claim
71 words
A ceramic composition for a reduction-reoxidation type semiconducting capacitor, said composition comprising (1) a mixture of more than 78.5 mole % but less than 98.0 mole % barium titanate, 1.0 to 6.0 mole % cerium oxide, less than 0.5 mole % neodymium oxide and 1.0 to 15.0 mole % zirconium oxide and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
Claim 4
Dependent Claim
71 words
A ceramic composition for a reduction-reoxidation type semiconducting capacitor, said composition comprising (1) a mixture of more than 78.5 mole % but less than 98.0 mole % barium titanate, 1.0 to 6.0 mole % cerium oxide, less than 0.5 mole % neodymium oxide and 1.0 to 15.0 mole % zirconium oxide and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
Claim 5
Dependent Claim
71 words
A ceramic composition for a reduction-oxidation type semiconducting capacitor, said composition comprising (1) a mixture of more than 78.7 mole % but less than 98.0 mole % barium titanate, 1.0 to 6.0 mole % cerium oxide, less than 0.3 mole % lanthanum oxide and 1.0 to 15.0 mole % zirconium oxide and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
Claim 6
Dependent Claim
71 words
A ceramic composition for a reduction-oxidation type semiconducting capacitor, said composition comprising (1) a mixture of more than 78.7 mole % but less than 98.0 mole % barium titanate, 1.0 to 6.0 mole % cerium oxide, less than 0.3 mole % lanthanum oxide and 1.0 to 15.0 mole % zirconium oxide and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
Claim 7
Dependent Claim
73 words
A ceramic composition for a reduction-reoxidation type semiconducting capacitor, said composition comprising (1) a mixture of 79.0 to 99.0 mole % barium titanate, 0.5 to 6.0 mole % of an oxide of at least one lanthanide having an atomic number of from 59 to 66 and 0.5 to 15.0 mole % zirconium oxide, and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
Claim 8
Dependent Claim
73 words
A ceramic composition for a reduction-reoxidation type semiconducting capacitor, said composition comprising (1) a mixture of 79.0 to 99.0 mole % barium titanate, 0.5 to 6.0 mole % of an oxide of at least one lanthanide having an atomic number of from 59 to 66 and 0.5 to 15.0 mole % zirconium oxide, and (2) 0.01 to 0.4% by weight manganese oxide, calculated as Mn based on the weight of said mixture (1).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-08-12 | 1989-02-11 | 1989-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-08-12 | 1993-02-11 | 1993-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-08-12 | 1997-02-11 | 1997-08-13 | $7700.00 | Window Closed / Lapsed |