Heat ray screening glass
Assignee: Nippon Sheet Glass Co Ltd
•
Filing: 1990-06-05
•
Granted: 1992-07-14
•
Expires: 2010-06-05
Abstract
Abstract A heat ray screening glass according to this invention comprises a sheet glass, a first layer covered on the sheet glass and which is 55 nm to 70 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, a second layer covered on the first layer and consisting of a TiO 2 film which is 30 nm to 55 nm thick and has a refractive index of 2.3 to 2.5 at a wavelength of 550 nm, and a third layer covered on the second layer and which is 45 nm to 60 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, wherein the change in color of the light transmitted through and reflected on the sheet ray screening glass is very little, and a comparative high visible light transmittance and a low visible light reflectivity in the glass can be obtained.
Inventors
- 👤 Takashi Muromachi
- 👤 Jun Kawaguchi
- 👤 Hidemi Nakai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:51
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3429; C03C17/3435; C03C17/3417; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
153 words
A heat ray screening glass for automotive window glass consisting of: a sheet glass substrate, a first layer covering the sheet glass and which is 55 nm to 70 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, a second layer covering the first layer and consisting of a TiO 2 film which is 30 nm to 55 nm thick and has a refractive index of 2.3 to 2.5 at a wavelength of 550 nm, and a third layer covering the second layer which is 45 nm to 55 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, wherein the absolute value of each difference in chromaticity coordinates is less than 0.03, the difference being obtained by subtracting the chromaticity coordinates of the sheet glass substrate from the chromaticity coordinates of the heat ray screening glass, respectively.
Claim 2
Dependent Claim
153 words
A heat ray screening glass for automotive window glass consisting of: a sheet glass substrate, a first layer covering the sheet glass and which is 55 nm to 70 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, a second layer covering the first layer and consisting of a TiO 2 film which is 30 nm to 55 nm thick and has a refractive index of 2.3 to 2.5 at a wavelength of 550 nm, and a third layer covering the second layer which is 45 nm to 55 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, wherein the absolute value of each difference in chromaticity coordinates is less than 0.03, the difference being obtained by subtracting the chromaticity coordinates of the sheet glass substrate from the chromaticity coordinates of the heat ray screening glass, respectively.
Claim 3
Dependent Claim
41 words
A heat ray screening glass according to claim 1, further comprising a film, interposed between the second layer and the third layer, and which consists of nitride of Ti, Zr or Hf and has a thickness not greater than 10 nm.
Claim 4
Dependent Claim
59 words
A heat ray screening glass according to claim 1 wherein the first layer consists of an oxide film selected from a group of SnO 2 , ZrO 2 , Al 2 O 3 , Ta 2 O 5 , ZnO and In 2 O 3 , and the third layer consists of an oxide film selected from the group.
Claim 5
Dependent Claim
19 words
A heat ray screening glass according to claim 1 wherein the first, second and third layers are substantially transparent.
Claim 6
Dependent Claim
23 words
A heat ray screening glass according to claim 3, wherein the first layer and the third layer consist of a SnO 2 film.
Claim 7
Dependent Claim
183 words
A heat ray screening glass for automotive window glass consisting of: a sheet glass substrate a first layer covering the sheet glass and which is 55 nm to 70 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, a second layer covering the first layer and consisting of a TiO 2 film which is 30 nm to 55 nm thick and has a refractive index of 2.3 to 2.5 at a wavelength of 550 nm, a third layer covering the second layer which is 45 nm to 55 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, and a film, interposed between the second layer and the third layer, and which consists of nitride of Ti, Zr or Hf and has a thickness not greater than 10 nm, wherein the absolute value of each difference in chromaticity coordinates is less than 0.03, the difference being obtained by subtracting the chromaticity coordinates of the sheet glass substrate from the chromaticity coordinates of the heat ray screening glass, respectively.
Claim 8
Dependent Claim
183 words
A heat ray screening glass for automotive window glass consisting of: a sheet glass substrate a first layer covering the sheet glass and which is 55 nm to 70 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, a second layer covering the first layer and consisting of a TiO 2 film which is 30 nm to 55 nm thick and has a refractive index of 2.3 to 2.5 at a wavelength of 550 nm, a third layer covering the second layer which is 45 nm to 55 nm thick and has a refractive index of 1.8 to 2.1 at a wavelength of 550 nm, and a film, interposed between the second layer and the third layer, and which consists of nitride of Ti, Zr or Hf and has a thickness not greater than 10 nm, wherein the absolute value of each difference in chromaticity coordinates is less than 0.03, the difference being obtained by subtracting the chromaticity coordinates of the sheet glass substrate from the chromaticity coordinates of the heat ray screening glass, respectively.
Claim 9
Dependent Claim
56 words
A heat ray screening glass according to claim 6, wherein the first layer consists of an oxide film selected from a group of SnO 2 , Al 2 O 3 , Al 2 O 5 , ZnO and In 2 O 3 , and the third layer consists of an oxide film selected from the group.
Claim 10
Dependent Claim
19 words
A heat ray screening glass according to claim 6, wherein the first, second and third layers are substantially transparent.
Claim 11
Dependent Claim
23 words
A heat ray screening glass according to claim 7, wherein the first layer and the third layer consist of a SnO 2 film.
References Cited (Backward Citations)
GB1292717A
Cited
US4377613A
Cited
JPS60126601A
Cited
US4690871A
Cited
US4900630A
Cited
JPS645930A
Cited
US4940636A
Cited
DE3902456A1
Cited
US4834857A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-14 | 1996-01-13 | 1996-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-14 | 2000-01-13 | 2000-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-14 | 2004-01-13 | 2004-07-14 | $7700.00 | Window Closed / Lapsed |