Method of making hydroxamic acid polymers from primary amide polymers
Assignee: Massachusetts Institute of Technology
•
Filing: 1988-12-13
•
Granted: 1992-07-07
•
Expires: 2008-12-13
Abstract
Abstract A method for preparing hydroxamic acid polymers from primary amide polymers wherein polyvinyl monomers such as polyacrylamide are reacted with hydroxyl amine in aqueous solution at room temperature. The low reaction temperature is crucial to producing a high yield (70%) of polymer with hydroxamic acid groups and having a low carboxylic acid content (less than 15%, preferably less than 3%). The polymers display high metal affinity over a broad pH range. The polymers are particularly useful for biomedical applications due to the low carboxylic acid content and for the removal and purification of metals due to the high binding constants and rapid reaction rates.
Inventors
- 👤 Abraham J. Domb
- 👤 Robert S. Langer
- 👤 Ernest G. Cravalho
- 👤 Gershon Golomb
- 👤 Edith Mathiowitz
- 👤 Cato T. Laurencin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 09:35
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/30; C08F8/32; C08F2800/00; C08F2800/10; C08F2810/00; C08F2810/20
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
33 words
A method for synthesizing hydroxamic polymers comprising: reacting a primary amide polymer with a compound selected from the group consisting of hydroxylamine or a derivative thereof at a pH greater than about 10.
Claim 2
Independent Claim
33 words
A method for synthesizing hydroxamic polymers comprising: reacting a primary amide polymer with a compound selected from the group consisting of hydroxylamine or a derivative thereof at a pH greater than about 10.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein the reaction is conducted at a temperature of between about 20° C. and 30° C.
Claim 4
Dependent Claim
20 words
The method of claim 1 further comprising stirring the primary amides-hydroxylamine mixture for approximately thirty minutes before adjusting the pH.
Claim 5
Dependent Claim
25 words
The method of claim 1 further comprising selecting the primary amide polymer from the group consisting of acrylamide and linear, branched, and crosslinked derivatives thereof.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein the reaction is continued until approximately 70% of the functional groups on the polymer are hydroxamic acid groups.
Claim 7
Dependent Claim
28 words
The method of claim 1 wherein the reaction is continued until the carboxylic acid groups constitute less than about 15% of the total functional groups on the polymer.
References Cited (Backward Citations)
US2959574A
Cited
US4536296A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-07 | 1996-01-06 | 1996-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-07 | 2000-01-06 | 2000-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-07 | 2004-01-06 | 2004-07-07 | $7700.00 | Window Closed / Lapsed |