Removable adhesive comprising acrylic microballs, acrylic copolymer and cross-linker
Assignee: Nichiban Co Ltd
•
Filing: 1990-05-14
•
Granted: 1992-07-07
•
Expires: 2010-05-14
Abstract
Abstract A removable adhesive composition comprising (i) 100 parts by weight of a copolymer (A) which is tacky at ordinary temperature, synthesized of 90 to 99.9% by weight of a nonfunctional vinyl type monomer (a) mainly composed of an acrylate or methacrylate ester having an alkyl group having 2 to 12 carbon atoms and 0.1 to 10% by weight of a functional vinyl type monomer (b) having one or more of a carboxyl group, a hydroxyl group, an amino group or an epoxy group in its molecule; (ii) 20 to 1,000 parts by weight of a copolymer (B) whose glass transition point is 10° C. or less and also having a mean particle diameter of 0.5 to 300 μm, synthesized of 90 to 99.9% by weight of a nonfunctional vinyl type monomer (a) mainly composed of acrylate or methacrylate ester having an alkyl group having 2 to 12 carbon atoms and 0.1 to 10% by weight of an α-monoolefinic carboxylic acid (c); and (iii) 0.01 to 5 parts by weight of a polyfunctional cross-linking agent (C) which is capable of reacting with the functional groups of said components (b) and (c), and the surfaces of said copolymer (B) being entirely covered with the copolymer (A). The removable adhesive composition of this invention has excellent primary tack, adhesiveness and removability, and which, in particular, can be readily removed from an adherend without leaving any remanent adhesive composition on the adherend and also has excellent adhesiveness.
Inventors
- 👤 Hiroyasu Miyasaka
- 👤 Yasuaki Kitazaki
- 👤 Tetsuaki Matsuda
- 👤 Junichi Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 21:03
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/30; C08F8/14; C09; C09J; C09J133/00; C09J133/04; C09J133/06; C09J133/062; C08F2810/00; C08F2810/20; C08L; C08L2205/00; C08L2205/02; C08L2205/14; C08L2205/18; C08L2666/00; C08L2666/02; C08L2666/04; C08L33/00; C08L33/04; C08L33/06; C09J2301/00; C09J2301/30; C09J2301/302
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
260 words
A removable adhesive composition comprising: about 100 parts by weight of a copolymer (A) which is tacky at ordinary temperature, and comprises: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which comprises an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of a functional vinyl monomer (b) having at least one of a carboxyl group, a hydroxyl group, an amino group and an epoxy group; from about 20 to about 1,000 parts by weight of a copolymer (B) having a glass transition point of at most about 10° C. and being in the form of microballs having a mean particle diameter of from about 0.5 to about 300 μm, and comprising: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which comprises an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of an α-monoolefinic carboxylic acid (c); and from about 0.01 to about 5 parts by weight of a polyfunctional cross-linking agent (C) which is capable of reacting with the functional groups of said components (b) and (c), wherein the surfaces of said copolymer (B) are substantially covered by said copolymer (A), and wherein the adhesive composition may be readily adhered to an adherend with a slight pressure and removed therefrom without damaging the surface of the adherend or leaving adhesive on the surface of the adherend.
Claim 2
Dependent Claim
260 words
A removable adhesive composition comprising: about 100 parts by weight of a copolymer (A) which is tacky at ordinary temperature, and comprises: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which comprises an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of a functional vinyl monomer (b) having at least one of a carboxyl group, a hydroxyl group, an amino group and an epoxy group; from about 20 to about 1,000 parts by weight of a copolymer (B) having a glass transition point of at most about 10° C. and being in the form of microballs having a mean particle diameter of from about 0.5 to about 300 μm, and comprising: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which comprises an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of an α-monoolefinic carboxylic acid (c); and from about 0.01 to about 5 parts by weight of a polyfunctional cross-linking agent (C) which is capable of reacting with the functional groups of said components (b) and (c), wherein the surfaces of said copolymer (B) are substantially covered by said copolymer (A), and wherein the adhesive composition may be readily adhered to an adherend with a slight pressure and removed therefrom without damaging the surface of the adherend or leaving adhesive on the surface of the adherend.
Claim 3
Dependent Claim
58 words
The removable adhesive composition according to claim 1, wherein said nonfunctional vinyl monomer (a) is a member selected from the group consisting of ethyl acrylate, propyl acrylate, n-butyl acrylate, isobutyl acrylate, n-octyl acrylate, isooctyl acrylate, 2-ethylhexyl acrylate, nonyl acrylate, isononyl acrylate, lauryl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, 2-ethylhexyl methacrylate, isononyl methacrylate and lauryl methacrylate.
Claim 4
Dependent Claim
23 words
The removable adhesive composition according to claim 1, comprising from about 95 to about 99.5% by weight of said nonfunctional vinyl monomer (a).
Claim 5
Dependent Claim
53 words
The removable adhesive composition according to claim 1, wherein said functional vinyl monomer (b) is a member selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, crotonic acid, maleic acid, 2-hydroxyethyl methacrylate, hydroxypropyl methacrylate, 2-hydroxyethyl acrylate, hydroxypropyl acrylate, N-methylolacryl amide and N-methylolmethacryl amide, acryl amide, glycidyl methacrylate and allyl-glycidyl ether.
Claim 6
Dependent Claim
27 words
The removable adhesive composition according to claim 1, wherein said copolymer (A) comprises from about 0.5 to about 5% by weight of said functional vinyl monomer (b).
Claim 7
Dependent Claim
20 words
The removable adhesive composition according to claim 1, wherein said polymer (A) is prepared by emulsion polymerization or solution polymerization.
Claim 8
Dependent Claim
19 words
The removable adhesive composition according to claim 6, wherein said copolymer (A) is prepared by a solution polymerization method.
Claim 9
Dependent Claim
25 words
The removable adhesive composition according to claim 1, wherein said copolymer (B) comprises from about 95 to about 99.5% by weight of said component (a).
Claim 10
Dependent Claim
25 words
The removable adhesive composition according to claim 1, wherein said copolymer (B) comprises from about 0.5 to about 5% by weight of said component (c).
Claim 11
Dependent Claim
25 words
The removable adhesive composition according to claim 1, wherein the mean particle diameter of the copolymer (B) is from about 1 to about 100 μm.
Claim 12
Dependent Claim
34 words
The removable adhesive composition according to claim 1, wherein polyfunctional cross-linking agent is a member selected from the group consisting of a polyisocyanate (C) compound, polyepoxy series compound and a polyfunctional aziridine series compound.
Claim 13
Dependent Claim
50 words
The removable adhesive composition according to claim 1, wherein said composition comprises from about 20 to about 1,000 parts by weight of said copolymer (B) and from about 0.01 to about 5 parts by weight of said cross-linking agent relative to 100 parts by weight of said copolymer (A), respectively.
Claim 14
Dependent Claim
50 words
The removable adhesive composition according to claim 12, wherein said composition comprises from about 20 to about 500 parts by weight of said copolymer (B), and from about 0.5 to about 3 parts by weight of said cross-linking agent, relative to 100 parts by weight of said copolymer (A), respectively.
Claim 15
Dependent Claim
255 words
A removable adhesive composition consisting essentially of: about 100 parts by weight of a copolymer (A) which is tacky at ordinary temperature, consisting essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of a functional vinyl monomer (b) having at least one of carboxyl group, a hydroxyl group, an amino group and an epoxy group; from about 20 to about 1,000 parts by weight of a copolymer (B) having a glass transition point of at most about 10° C. and having a mean particle diameter of from about 0.5 to about 300 μm, and comprising essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of an α-monoolefinic carboxylic acid (c); and from about 0.01 to about 5 parts by weight of a polyfunctional cross-linking agent (C) which is capable of reacting with the functional groups of said components (b) and (c), wherein the surfaces of said copolymer (A), and wherein the adhesive composition may be readily adhered to an adherend with a slight pressure and removed therefrom without damaging the surface of the adherend or leaving adhesive on the surface of the adherend.
Claim 16
Dependent Claim
255 words
A removable adhesive composition consisting essentially of: about 100 parts by weight of a copolymer (A) which is tacky at ordinary temperature, consisting essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of a functional vinyl monomer (b) having at least one of carboxyl group, a hydroxyl group, an amino group and an epoxy group; from about 20 to about 1,000 parts by weight of a copolymer (B) having a glass transition point of at most about 10° C. and having a mean particle diameter of from about 0.5 to about 300 μm, and comprising essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 10% by weight of an α-monoolefinic carboxylic acid (c); and from about 0.01 to about 5 parts by weight of a polyfunctional cross-linking agent (C) which is capable of reacting with the functional groups of said components (b) and (c), wherein the surfaces of said copolymer (A), and wherein the adhesive composition may be readily adhered to an adherend with a slight pressure and removed therefrom without damaging the surface of the adherend or leaving adhesive on the surface of the adherend.
Claim 17
Dependent Claim
269 words
A removable adhesive composition consisting essentially of: about 100 parts by weight of a copolymer (A) which is tacky at ordinary temperature, consisting essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 5% by weight of a functional vinyl monomer (b) having at least one of a carboxyl group, a hydroxyl group, an amino group and an epoxy group; from about 20 to about 500 parts by weight of a copolymer (B) having a glass transition point of at most about 10° C. and being in the form of microballs having a mean particle diameter of from about 0.5 to about 300 μm, and consisting essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.5 to about 5% by weight of an α-monoolefinic carboxylic acid (c); and from about 0.05 to about 3 parts by weight of a polyfunctional cross-linking agent (C) which is capable of reacting with the functional groups of said components (b) and (c), wherein the surfaces of said copolymer (B) are substantially covered by said copolymer (A), and wherein the adhesive composition may be readily adhered to an adherend with a slight pressure and removed therefrom without damaging the surface of the adherend or leaving adhesive on the surface of the adherend.
Claim 18
Dependent Claim
269 words
A removable adhesive composition consisting essentially of: about 100 parts by weight of a copolymer (A) which is tacky at ordinary temperature, consisting essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.1 to about 5% by weight of a functional vinyl monomer (b) having at least one of a carboxyl group, a hydroxyl group, an amino group and an epoxy group; from about 20 to about 500 parts by weight of a copolymer (B) having a glass transition point of at most about 10° C. and being in the form of microballs having a mean particle diameter of from about 0.5 to about 300 μm, and consisting essentially of: from about 90 to about 99.9% by weight of a nonfunctional vinyl monomer (a) which consists essentially of an acrylate or methacrylate ester having an alkyl group having from 2 to 12 carbon atoms, and from about 0.5 to about 5% by weight of an α-monoolefinic carboxylic acid (c); and from about 0.05 to about 3 parts by weight of a polyfunctional cross-linking agent (C) which is capable of reacting with the functional groups of said components (b) and (c), wherein the surfaces of said copolymer (B) are substantially covered by said copolymer (A), and wherein the adhesive composition may be readily adhered to an adherend with a slight pressure and removed therefrom without damaging the surface of the adherend or leaving adhesive on the surface of the adherend.
References Cited (Backward Citations)
US3691140A
Cited
US3773710A
Cited
US4098945A
Cited
US4415697A
Cited
JPS57182373A
Cited
US4468493A
Cited
US4565730A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-07-07 | 1996-01-06 | 1996-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-07-07 | 2000-01-06 | 2000-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-07-07 | 2004-01-06 | 2004-07-07 | $7700.00 | Window Closed / Lapsed |