Preparation of refractory materials

Claim 2

A process for preparing a refractory material comprising: (a) forming a blank of a precursor composition comprising a thermoformable carbon precursor component; (b) using a gas to apply isostatic pressure to said blank in the absence of a hermetically sealed envelope enveloping said blank; (c) initially heating said blank to a temperature insufficient to initiate pyrolysis thereof but sufficient to permit flow of said precursor composition and holding said blank at said temperature for a period which enables said flow to occur to an extent sufficient to seal said blank whereby said isostatic pressure is effectively transferred to the whole of said blank and then (d) heating said blank to a temperature sufficient to pyrolyze said precursor composition.

Claim 3

A process according to claim 1, wherein the thermoformable carbon precursor component has a viscosity of not more than 100000 Nsm -2 at a temperature at which it is formable and has a viscosity of not less than 1 Nsm -2 at the onset of intractability.

Claim 4

A process according to claim 1, wherein said temperature in step (c) is at least 100° C.

Claim 5

A process according to claim 1, wherein the pyrolysis in step (d) is carried out at an operating temperature of at least 500° C. and the isostatic pressure applied to said blank during step (d) is at least 500 bar.

Claim 6

A process according to claim 1, wherein said blank comprises a fibrous reinforcement which is not deleteriously affected by the processing conditions and which retains a reinforcement function in the resultant refractory material.

Claim 7

A process according to claim 1, wherein said thermoformable carbon precursor component has a viscosity of not more than 10,000 Nsm -2 at a temperature at which it is formable and has a viscosity of not less than 10 Nsm -2 at the onset of intractability.

Claim 8

A process according to claim 1, wherein the temperature in step (c) is at least 200° C.

Claim 9

A process according to claim 1, wherein the pyrolysis in step (d) is carried out at an operating temperature in the range of from 750° C. to 2000° C. and the isostatic pressure applied to said blank in step (d) is in the range of from 750 bar to 2000 bar.

Claim 10

A process according to claim 1, wherein the pyrolysis in step (d) is carried out at an operating temperature in the range of from 750° C. to 1500° C. and the isostatic pressure applied to said blank is in the range of from 750 bar to 1500 bar.

Claim 11

A process according to claim 1, wherein the pyrolysis in step (d) is carried out at an operating temperature in the range of from 1000° C. to 1500° C. and the isostatic pressure applied to said blank is in the range of from 1000 bar to 1500 bar.

Claim 12

A process according to claim 1, wherein said blank comprises a fibrous reinforcement which is not deleteriously affected by the processing conditions and which retains a reinforcement function in the resultant refractory material.

Claim 13

A process for preparing a refractory material comprising: (a) forming a blank of a precursor composition comprising a thermoformable carbon precursor component; (b) using a gas to apply isostatic pressure to said blank in the absence of a hermetically sealed envelope enveloping said blank; (c) initially heating said blank under temperature a temperature of less than 500° C. and a pressure of less than 500 bar, said temperature being insufficient to initiate pyrolysis of said precursor composition but sufficient to permit flow of said precursor composition and holding said blank at said temperature for a period which enables said flow to occur to an extent sufficient to seal said blank whereby said isostatic pressure is effectively transferred to the whole of said blank; and then (d) heating said blank to a temperature of at least 500° C. to pyrolyze said precursor composition, and an isostatic pressure of at least 500 bar.

Claim 14

A process for preparing a refractory material comprising: (a) forming a blank of a precursor composition comprising a thermoformable carbon precursor component; (b) using a gas to apply isostatic pressure to said blank in the absence of a hermetically sealed envelope enveloping said blank; (c) initially heating said blank under temperature a temperature of less than 500° C. and a pressure of less than 500 bar, said temperature being insufficient to initiate pyrolysis of said precursor composition but sufficient to permit flow of said precursor composition and holding said blank at said temperature for a period which enables said flow to occur to an extent sufficient to seal said blank whereby said isostatic pressure is effectively transferred to the whole of said blank; and then (d) heating said blank to a temperature of at least 500° C. to pyrolyze said precursor composition, and an isostatic pressure of at least 500 bar.

Claim 15

A process for preparing a refractory material comprising: (a) selecting a thermoformable carbon precursor component comprising an aromatic polymer having divalent aromatic units containing divalent connecting groups selected from ketone, sulfone, sulfoxide or imide, the units being connected by ether and/or thioether linkages; (b) forming a blank of a precursor composition comprising said thermoformable carbon precursor component; (c) using a gas to apply isostatic pressure to said blank in the absence of a hermetically sealed envelope enveloping said blank; (d) initially heating said blank to a temperature insufficient to initiate pyrolysis thereof but sufficient to permit flow of said precursor composition and holding said blank at said temperature for a period which enables said flow to occur to an extent sufficient to seal said blank whereby said isostatic pressure is effectively transferred to the whole of said blank; and then (e) heating said blank to a temperature sufficient to pyrolyze said precursor composition.

Claim 16

A process for preparing a refractory material comprising: (a) selecting a thermoformable carbon precursor component comprising an aromatic polymer having divalent aromatic units containing divalent connecting groups selected from ketone, sulfone, sulfoxide or imide, the units being connected by ether and/or thioether linkages; (b) forming a blank of a precursor composition comprising said thermoformable carbon precursor component; (c) using a gas to apply isostatic pressure to said blank in the absence of a hermetically sealed envelope enveloping said blank; (d) initially heating said blank to a temperature insufficient to initiate pyrolysis thereof but sufficient to permit flow of said precursor composition and holding said blank at said temperature for a period which enables said flow to occur to an extent sufficient to seal said blank whereby said isostatic pressure is effectively transferred to the whole of said blank; and then (e) heating said blank to a temperature sufficient to pyrolyze said precursor composition.

Claim 17

A process according to claim 13, in which said divalent aromatic units comprise phenylene groups and said divalent connecting groups are selected from the group consisting of ketone, sulfone and/or imide groups, said units being connected by ether linkages.

Claim 18

A process according to claim 13, wherein said thermoformable carbon precusor component comprises continuous reinforcing fibers.