Claim 1

Independent Claim 151 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization, not requiring the use of a nucleating agent, said method comprising: a) impregnating the fibrous reinforcement with a sol in a sol-gel process, the sol impregnating the fibrous reinforcement and wherein premature crystallization of the matrix obtained from the sol is hindered by the addition to the sol of an amount of a crystallization retarding agent which is sufficient for maintaining the sol in a vitreous state during the step of densification of the fibrous reinforcement and of the matrix, resulting in a product with low residual porosity when said densification is carried out at a temperature lower than 1100° C.; and b) hot pressing the fibrous reinforcement and matrix at a temperature lower than 1100° C., for carrying out the densification of said fibrous reinforcement and matrix.

Claim 2

Independent Claim 151 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization, not requiring the use of a nucleating agent, said method comprising: a) impregnating the fibrous reinforcement with a sol in a sol-gel process, the sol impregnating the fibrous reinforcement and wherein premature crystallization of the matrix obtained from the sol is hindered by the addition to the sol of an amount of a crystallization retarding agent which is sufficient for maintaining the sol in a vitreous state during the step of densification of the fibrous reinforcement and of the matrix, resulting in a product with low residual porosity when said densification is carried out at a temperature lower than 1100° C.; and b) hot pressing the fibrous reinforcement and matrix at a temperature lower than 1100° C., for carrying out the densification of said fibrous reinforcement and matrix.

Claim 3

Dependent Claim 15 words

The method as claimed in claim 1, wherein said crystallization retarding agent is boric anhydride.

Claim 4

Dependent Claim 27 words

The method as claimed in claim 2, wherein the boric anhydride content of the sol is between 10 and 30% by weight with respect to the silica.

Claim 5

Dependent Claim 41 words

The method as claimed in claim 1, wherein the reinforcement is made up of ceramic fibers selected from the group consisting of carbon, silicon carbide, alumina and alumino-silica fibers, the fiber volume fraction in the composite being from 20% to 70%.

Claim 6

Dependent Claim 27 words

The method as claimed in claim 1, wherein the fibers are unidirectional and continuous, or in the form of fabrics, non woven mats or other multidirectional preforms.

Claim 7

Dependent Claim 66 words

The method as claimed in claim 1 wherein the fibers of the reinforcement, before impregnation by the sol, undergo a surface treatment for weakening the fiber/matrix bond so as to increase the toughness of the composite or to protect the fibers against the agressiveness of the matrix or to increase the toughness of the composite and to protect the fibers against the agressiveness of the matrix.

Claim 8

Dependent Claim 16 words

The method as claimed in claim 6, wherein the surface treatment consists of a pyrocarbon deposition.

Claim 9

Dependent Claim 29 words

The method as claimed in claim 1, wherein the hot pressing is carried out at a temperature between 600° and 900° C. at a pressure less than 50 MPa.

Claim 10

Independent Claim 172 words

A method for manufacturing a composite material formed of fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization, and not requiring the use of a nucleating agent, said method comprising: a) impregnating a fibrous reinforcement with a sol prepared from an aqueous silica suspension, a solution of metal salts and a solution containing an amount of a crystallization retarding agent, which is sufficient for maintaining the sol in a vitreous state during densification of the fibrous reinforcement and of the matrix, resulting in a product with low residual porosity when densification is carried out at a temperature lower than 1100° C., b) drying the thus impregnated fibrous reinforcement, c) repeating the impregnating-drying steps until a prepreg is obtained having the desired fiber volume fraction, d) pyrolysing the prepreg for a sufficiently long time for removing the gases formed by chemical reaction, and, e) hot pressing said prepreg at a temperature lower than 1100° C. for carrying out its densification and cooling it without pressure down to ambient temperature.

Claim 11

Independent Claim 172 words

A method for manufacturing a composite material formed of fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization, and not requiring the use of a nucleating agent, said method comprising: a) impregnating a fibrous reinforcement with a sol prepared from an aqueous silica suspension, a solution of metal salts and a solution containing an amount of a crystallization retarding agent, which is sufficient for maintaining the sol in a vitreous state during densification of the fibrous reinforcement and of the matrix, resulting in a product with low residual porosity when densification is carried out at a temperature lower than 1100° C., b) drying the thus impregnated fibrous reinforcement, c) repeating the impregnating-drying steps until a prepreg is obtained having the desired fiber volume fraction, d) pyrolysing the prepreg for a sufficiently long time for removing the gases formed by chemical reaction, and, e) hot pressing said prepreg at a temperature lower than 1100° C. for carrying out its densification and cooling it without pressure down to ambient temperature.

Claim 12

Dependent Claim 23 words

The method as claimed in claim 9, wherein the metal salts are selected from the group consisting of aluminum salts and lithium salts.

Claim 13

Dependent Claim 14 words

The method as claimed in claim 10, wherein the aluminum salt is aluminum nitrate.

Claim 14

Dependent Claim 14 words

The method as claimed in claim 10, wherein the lithium salt is lithium nitrate.

Claim 15

Dependent Claim 42 words

The method as claimed in claim 9, wherein step a) is carried out only once by the impregnation of said fibrous reinforcement by said sol, followed by in situ gelling of said sol induced by increasing the temperature or modifying the pH.

Claim 16

Dependent Claim 23 words

The method as claimed in claim 9, wherein pyrolysis of the prepreg is carried out at a temperature from 200° to 600° C.

Claim 17

Dependent Claim 16 words

The method as claimed in claim 9, wherein step e) is completed by a ceramization posttreatment.

Claim 18

Dependent Claim 19 words

The method as claimed in claim 15, wherein the ceramization treatment is carried out after relaxation of the pressure.

Claim 19

Dependent Claim 54 words

The method as claimed in claim 9, wherein step e) comprises heating without pressure up to the glass transition temperature of the matrix obtained by pyrolysis of the prepreg, pressing at the glass transition temperature of the matrix and raising of this temperature under pressure up to a value between 800° and 1000° C.

Claim 20

Independent Claim 114 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization comprising: impregnating the fibrous reinforcement with a sol of a sol-gel process, the sol impregnating the fibrous material and wherein premature crystallization of the matrix obtained from the sol is hindered by addition to the sol of a crystallization retarding agent and hot pressing the fibrous reinforcement and matrix, the hot pressing being carried out at temperature lower than 1100° C. and the crystallization retarding agent being boric anhydride which is added to the sol in the form of a precursor selected from the group consisting of boric acid or borate.

Claim 21

Independent Claim 114 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization comprising: impregnating the fibrous reinforcement with a sol of a sol-gel process, the sol impregnating the fibrous material and wherein premature crystallization of the matrix obtained from the sol is hindered by addition to the sol of a crystallization retarding agent and hot pressing the fibrous reinforcement and matrix, the hot pressing being carried out at temperature lower than 1100° C. and the crystallization retarding agent being boric anhydride which is added to the sol in the form of a precursor selected from the group consisting of boric acid or borate.

Claim 22

Dependent Claim 13 words

The method as claimed in claim 18, wherein the borate is ammonium tetraborate.

Claim 23

Independent Claim 104 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization comprising: impregnating the fibrous reinforcement with a sol of a sol-gel process, the sol impregnating the fibrous material and wherein premature crystallization of the matrix obtained from the sol is hindered by addition to the sol of a crystallization retarding agent and hot pressing the fibrous reinforcement and matrix, the hot pressing being carried out at a temperature lower than 1100° C. and the overall concentration of the sol in oxide equivalent being increased by raising the temperature of the sol.

Claim 24

Independent Claim 104 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization comprising: impregnating the fibrous reinforcement with a sol of a sol-gel process, the sol impregnating the fibrous material and wherein premature crystallization of the matrix obtained from the sol is hindered by addition to the sol of a crystallization retarding agent and hot pressing the fibrous reinforcement and matrix, the hot pressing being carried out at a temperature lower than 1100° C. and the overall concentration of the sol in oxide equivalent being increased by raising the temperature of the sol.

Claim 25

Independent Claim 99 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization comprising: impregnating the fibrous reinforcement with a sol of a sol-gel process, the sol impregnating the fibrous material and wherein premature crystallization of the matrix obtained from the sol is hindered by addition to the sol of a crystallization retarding agent and hot pressing the fibrous reinforcement and matrix, the hot pressing being carried out at temperature lower than 1100° C., and wherein fillers are incorporated in the sol in the form of whiskers or particles.

Claim 26

Independent Claim 99 words

A method for manufacturing a composite material formed of a fibrous reinforcement and a silica based ceramic or vitro-ceramic matrix formed by crystallization comprising: impregnating the fibrous reinforcement with a sol of a sol-gel process, the sol impregnating the fibrous material and wherein premature crystallization of the matrix obtained from the sol is hindered by addition to the sol of a crystallization retarding agent and hot pressing the fibrous reinforcement and matrix, the hot pressing being carried out at temperature lower than 1100° C., and wherein fillers are incorporated in the sol in the form of whiskers or particles.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1995-06-30	1995-12-30	1996-06-30	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1999-06-30	1999-12-30	2000-06-30	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2003-06-30	2003-12-30	2004-06-30	$7700.00	Window Closed / Lapsed

Method of manufacturing a composite material with vitroceramic or ceramic matrix using a sol-gel process

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag