Method for making zinc electrodes for alkaline-zinc batteries
Assignee: Teck Metals Ltd
•
Filing: 1990-07-16
•
Granted: 1992-06-23
•
Expires: 2010-07-16
Abstract
Abstract A method for making zinc electrodes for alkaline-zinc batteries comprising the steps of: mixing an amount of a zinc-magnesium binder alloy with an amount of a material chosen from zinc and a second zinc-magnesium alloy to form a mechanical mixture. The melting temperature of the material is at least 15 Celsius degrees higher than the melting temperature of the binder alloy. The mixture is applied to a current collector and the current collector with applied mixture is heated to a temperature at which incipient melting of the binder alloy causes sintering of the mixture with the formation of a coherent layer solidly bonded to the current collector. The compositions and the amount of the binder alloy and the second alloy are selected such that the active material in the layer of the electrode contains no more than about 15% magnesium, preferably no more than about 10% magnesium. In various embodiments, a binder alloy containing 45% to 55% Mg is eutectically sintered with zinc or a second alloy containing from >0% to about 10% Mg, a binder alloy containing about 3% to 4% Mg is eutectically sintered with a second alloy containing either about 20% to 43% Mg is eutectically sintered with a second alloy containing either about 20% to 43% Mg or about 52% to 80% Mg, and a binder alloy containing either about 41% to 50% Mg or containing about 1.5% to 3% is eutectically sintered with zinc.
Inventors
- 👤 Jack Sklarchuck
- 👤 Hans Rensing
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:26
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/04; H; H01; H01M; H01M4/00; H01M4/02; H01M4/24; H01M4/26; H01M4/36; H01M4/38; H01M4/42; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
173 words
A method for making zinc electrodes for alkaline zinc batteries, said electrodes having a layer of active material, said method comprising the steps of: mixing an amount of a zinc-magnesium binder alloy in particulate form with an amount of a material in particulate form chosen from the group consisting of zinc and a second zinc-magnesium alloy to form a mechanical mixture, the melting temperature of said material being at least 15 Celsius degrees higher than the melting temperature of said binder alloy, applying said mixture to a current collector; heating said current collector with applied mixture to a temperature at which incipient melting of said binder alloy causes sintering of said mixture with the formation of a coherent layer solidly bonded to said current collector, said layer containing active material; and selecting the composition of said binder alloy and the composition of said material and selecting said amount of said binder alloy and said amount of said material such that said active material in said layer contains no more than about 15% magnesium.
Claim 2
Independent Claim
173 words
A method for making zinc electrodes for alkaline zinc batteries, said electrodes having a layer of active material, said method comprising the steps of: mixing an amount of a zinc-magnesium binder alloy in particulate form with an amount of a material in particulate form chosen from the group consisting of zinc and a second zinc-magnesium alloy to form a mechanical mixture, the melting temperature of said material being at least 15 Celsius degrees higher than the melting temperature of said binder alloy, applying said mixture to a current collector; heating said current collector with applied mixture to a temperature at which incipient melting of said binder alloy causes sintering of said mixture with the formation of a coherent layer solidly bonded to said current collector, said layer containing active material; and selecting the composition of said binder alloy and the composition of said material and selecting said amount of said binder alloy and said amount of said material such that said active material in said layer contains no more than about 15% magnesium.
Claim 3
Dependent Claim
21 words
A method as claimed in claim 1, wherein said active material in said layer contains no more than about 10% magnesium.
Claim 4
Dependent Claim
30 words
A method as claimed in claim 2, wherein the melting temperature of said material is at least about 20 Celsius degrees higher than the melting temperature of said binder alloy.
Claim 5
Dependent Claim
33 words
A method as claimed in claim 2, wherein said heating is carried out in an inert or a reducing atmosphere for a period of time sufficient for the formation of said coherent layer.
Claim 6
Dependent Claim
170 words
A method as claimed in claim 2, wherein said material is a second zinc-magnesium alloy, said binder alloy has a composition that contains magnesium in an amount in the range of about 45% to about 55%, said binder alloy has a melting temperature in the range of about 330° C. to about 360° C., said second alloy has a composition that contains magnesium in an amount in the range of from >0% to about 10%, said second alloy has a melting temperature in the range of about 363° C. to about 575° C., choosing the composition of said binder alloy and the composition of said second alloy such that the melting temperature of said second alloy is at least about 15 Celsius degrees higher than the melting temperature of said binder alloy, and said mechanical mixture contains an amount of said binder alloy and an amount of said second alloy in a weight ratio of binder alloy to second alloy in the range of from about 1:1 to about 1:9.
Claim 7
Dependent Claim
19 words
A method as claimed in claim 5, wherein said binder alloy contains magnesium in an amount of about 50%.
Claim 8
Dependent Claim
44 words
A method as claimed in claim 5, wherein said second alloy contains magnesium in an amount in the range of about 3.5% to about 10%, and said second alloy has a melting temperature in the range of about 380° C. to about 575° C.
Claim 9
Dependent Claim
14 words
A method as claimed in claim 5, wherein said weight ratio is about 1:4.
Claim 10
Dependent Claim
170 words
A method as claimed in claim 2, wherein said material is a second zinc-magnesium alloy, said binder alloy has a composition that contains magnesium in an amount in the range of about 3% to about 4%, said binder alloy has a melting temperature in the range of about 363° C. to about 415° C., said second alloy has a composition that contains magnesium in an amount in the range of about 20% to about 43%, said second alloy has a melting temperature in the range of about 378° C. to about 580° C., choosing the composition of said binder alloy and the composition of said second alloy such that the melting temperature of said second alloy is at least about 15 Celsius degrees higher than the melting temperature of said binder alloy, and said mechanical mixture contains an amount of said binder alloy and an amount of said second alloy in a weight ratio of binder alloy to second alloy in the range of from about 1:1 to about 9:1.
Claim 11
Dependent Claim
19 words
A method as claimed in claim 9, wherein said binder alloy contains magnesium in an amount of about 3%.
Claim 12
Dependent Claim
14 words
A method as claimed in claim 9, wherein said weight ratio is about 4:1.
Claim 13
Dependent Claim
170 words
A method as claimed in claim 1, wherein said material is a second zinc-magnesium alloy, said binder alloy has a composition that contains magnesium in an amount in the range of about 3% to about 4%, said binder alloy has a melting temperature in the range of about 363° C. to about 415° C., said second alloy has a composition that contains magnesium in an amount in the range of about 52% to about 80%, said second alloy has a melting temperature in the range of about 378° C. to about 570° C., choosing the composition of said binder alloy and the composition of said second alloy such that the melting temperature of said second alloy is at least about 15 Celsius degrees higher than the melting temperature of said binder alloy, and said mechanical mixture contains an amount of said binder alloy and an amount of said second alloy in a weight ratio of binder alloy to second alloy in the range of from about 1:1 to about 9:1.
Claim 14
Dependent Claim
19 words
A method as claimed in claim 12, wherein said binder alloy contains magnesium in an amount of about 3%.
Claim 15
Dependent Claim
14 words
A method as claimed in claim 12, wherein said weight ratio is about 4:1.
Claim 16
Dependent Claim
116 words
A method as claimed in claim 2, wherein said material is zinc, said binder alloy has a composition that contains magnesium in an amount in the range of about 41% to about 50%, said binder alloy has a melting temperature in the range of about 330° C. to about 404° C., choosing the composition of said binder alloy such that the melting temperature of zinc is at least about 15 Celsius degrees higher than the melting temperature of said binder alloy, and said mechanical mixture contains an amount of said binder alloy and an amount of zinc in a weight ratio of binder alloy to zinc in the range of from about 1:1 to about 1:9.
Claim 17
Dependent Claim
19 words
A method as claimed in claim 15, wherein said binder alloy contains magnesium in an amount of about 50%.
Claim 18
Dependent Claim
14 words
A method as claimed in claim 15, wherein said weight ratio is about 1:4.
Claim 19
Dependent Claim
116 words
A method as claimed in claim 2, wherein said material is zinc, said binder alloy has a composition that contains magnesium in an amount in the range of about 1.5% to about 3%, said binder alloy has a melting temperature in the range of about 336° C. to about 404° C., choosing the composition of said binder alloy such that the melting temperature of zinc is at least about 15 Celsius degrees higher than the melting temperature of said binder alloy, and said mechanical mixture contains an amount of said binder alloy and an amount of zinc in a weight ratio of binder alloy to zinc in the range of from about 1:1 to about 1:9.
Claim 20
Dependent Claim
19 words
A method as claimed in claim 18, wherein said binder alloy contains magnesium in an amount of about 3%.
Claim 21
Dependent Claim
14 words
A method as claimed in claim 18, wherein said weight ratio is about 1:4.
Claim 22
Dependent Claim
25 words
A method as claimed in claim 1, wherein said composition of said binder alloy is chosen from about the eutectic compositions between zinc and magnesium.
References Cited (Backward Citations)
US1223322A
Cited
US1342801A
Cited
US2254549A
Cited
US3348976A
Cited
US3325282A
Cited
US3650736A
Cited
US3655447A
Cited
US3663297A
Cited
US4011077A
Cited
US4155754A
Cited
US4591480A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-23 | 1995-12-23 | 1996-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-23 | 1999-12-23 | 2000-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-23 | 2003-12-23 | 2004-06-23 | $7700.00 | Window Closed / Lapsed |