Erasable optical disk media and method of recording/erasing the same
Assignee: Panasonic Holdings Corp
•
Filing: 1990-04-12
•
Granted: 1992-06-02
•
Expires: 2010-04-12
Abstract
Abstract Erasable optical disk media basically comprise a double layer structure composed of a thermal expansion layer formed of an organic dye and a binder, and a retention layer of metal. In the recording process, the thermal expansion layer is heated to form a dome-like pit in the retention layer. The reproducing process is performed by reading differences in reflectivity from the pit and an area surrounding the pit. In the erasing process, the retention layer including the pit is heated to flatten the same under the tensile stress (residual stress) acting on the thermal expansion layer. The pit size is kept in a stable condition during the recording and reproducing processes, while the erasing can be performed completely without leaving partly erased traces. The erasable optical disk media of the foregoing construction are highly durable and resistant to heat.
Inventors
- 👤 Osamu Yamamoto
- 👤 Katsuji Hattori
- 👤 Hirotoshi Niguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:59
CPC Classifications
G; G11; G11B; G11B7/00; G11B7/004; G11B7/0055; G11B7/00557; G11B7/0045; G11B7/00452; G11B7/24; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10S428/914; Y10S430/00; Y10S430/146; Y10T; Y10T428/00; Y10T428/23; Y10T428/239; Y10T428/31504; Y10T428/31507
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
130 words
An erasable optical disk medium, comprising: a transparent substrate; a thermal expansion layer disposed on said transparent substrate and composed of an organic dye and a binder, said thermal expansion layer having a light absorption band having a peak wavelength larger than the wavelength of a laser beam used in a recording process of said erasable optical disk medium, said peak wavelength ranging between 600 and 900 nm, said thermal expansion layer being formed of a viscoelastic material having a linear thermal expansion coefficient greater than 5×10 -1 kcal/mh°C.; and a retention layer of metal disposed on said thermal expansion layer and having a breaking elongation over 15%, said metal having a melting point greater than a temperature at which said thermal expansion layer softens and less than 600° C.
Claim 2
Dependent Claim
130 words
An erasable optical disk medium, comprising: a transparent substrate; a thermal expansion layer disposed on said transparent substrate and composed of an organic dye and a binder, said thermal expansion layer having a light absorption band having a peak wavelength larger than the wavelength of a laser beam used in a recording process of said erasable optical disk medium, said peak wavelength ranging between 600 and 900 nm, said thermal expansion layer being formed of a viscoelastic material having a linear thermal expansion coefficient greater than 5×10 -1 kcal/mh°C.; and a retention layer of metal disposed on said thermal expansion layer and having a breaking elongation over 15%, said metal having a melting point greater than a temperature at which said thermal expansion layer softens and less than 600° C.
Claim 3
Dependent Claim
28 words
An erasable optical disk medium as claimed in claim 1, wherein said viscoelastic material has a thermal conductivity greater than 2×10 -1 kcal/mh°C. less than 4×10 -1 kcal/mh°C.
Claim 4
Dependent Claim
44 words
An erasable optical disk medium as claimed in claim 1, further including a thermal diffusion layer disposed between said transparent substrate and said thermal expansion layer, said thermal diffusion layer having a thermal conductivity greater than 1.0 kcal/mh°C. and less than 2×10 2 kcal/mh°C.
Claim 5
Dependent Claim
59 words
An erasable optical disk medium as claimed in claim 3, wherein said thermal diffusion layer is formed a material selected from the group consisting of SiO 2 , SiN, Al 2 O 3 and diamond-like carbon said diamond-like carbon further comprising a thin film formed by sputtering carbon and having a thermal conductivity of from 6 to 50 kcal/mh°C.
Claim 6
Independent Claim
145 words
A method of recording/erasing an erasable optical disk medium having a double layer structure composed of a thermal expansion layer and a retention layer of metal, said method comprising the steps of: heating the thermal expansion layer of the erasable optical disk medium by directing a source of energy at a portion of said thermal expansion layer to thermally expand the same for causing the metal retention layer to plastically deform to form a bump, thereby performing the recording process; reading changes in reflectivity of the bump and an area surrounding the bump, thereby performing reproducing process; and heating the metal retention layer by directing a source of energy at a portion of said metal retention layer for softening said metal retention layer and causing the bump to be flattened by a tensile stress stored in the thermal expansion layer, thereby performing the erasing process.
Claim 7
Independent Claim
145 words
A method of recording/erasing an erasable optical disk medium having a double layer structure composed of a thermal expansion layer and a retention layer of metal, said method comprising the steps of: heating the thermal expansion layer of the erasable optical disk medium by directing a source of energy at a portion of said thermal expansion layer to thermally expand the same for causing the metal retention layer to plastically deform to form a bump, thereby performing the recording process; reading changes in reflectivity of the bump and an area surrounding the bump, thereby performing reproducing process; and heating the metal retention layer by directing a source of energy at a portion of said metal retention layer for softening said metal retention layer and causing the bump to be flattened by a tensile stress stored in the thermal expansion layer, thereby performing the erasing process.
Claim 8
Dependent Claim
183 words
A method as claimed in claim 5, wherein said heating in the recording process is achieved by directing a laser beam of an intermediate power to the backside of the transparent substrate for heating the thermal expansion layer to expand the same in such a manner as to plastically deform the metal retention layer to form a dome-like bump constituting a pit in the metal retention layer, thus recording a signal, said reading in the reproducing process is performed with a low power laser beam that is detected, as a signal, by differences in reflectivity from the pit and an area surrounding the pit while the pit is kept stable against deformation, and said heating in the erasing process is achieved by directing a laser beam of not less than said intermediate power to an area of the metal retention layer including the pit so as to heat the area to a temperature above the softening temperature of the metal retention layer for flattening the dome-like bump by the use of residual stress acting on the thermal expansion layer, thereby erasing the pit.
Claim 9
Dependent Claim
101 words
A method as claimed in claim 6, wherein said laser beams are irradiated from the backside of the transparent substrate, and said reproducing, recording and erasing processes comprise activating first, second and third semiconductor lasers provided exclusively for the reproducing, recording and erasing processes, respectively, said first semiconductor laser is capable of generating a laser beam having a wavelength shorter than the wavelength of a laser beam generated by said second semiconductor laser, said third semiconductor laser is capable of generating a laser beam having a wavelength longer than the wavelength of the laser beam generated by said second semiconductor laser.
Claim 10
Dependent Claim
95 words
A method as claimed in claim 6, wherein said laser beams are irradiated from the backside of the transparent substrate, said reproducing comprises activating a first semiconductor laser, and said recording and erasing comprise activating a second semiconductor laser, said first semiconductor laser being capable of generating a laser beam having a wavelength shorter than the wavelength of a laser beam generated by said second semiconductor laser, said second semiconductor laser comprising a power dependent semiconductor laser capable of generating a laser beam of a varying wavelength which increases with an increase in input power.
Claim 11
Dependent Claim
129 words
A method as claimed in claim 6, wherein the laser beams are irradiated from the backside of the transparent substrate, said recording, reproducing and erasing processes comprising activating a power dependent semiconductor laser capable of producing a laser beam having a varying wavelength which increases with an increase in input power, the wavelength of the laser beam generated in the erasing process being longer than the wavelength of the laser beam generated in the recording process, said wavelength of the leaser beam generated int he recording process being longer than the wavelength generated in the reproducing process, said laser beam generated in the recording process being substantially focused on the thermal expansion layer, said laser beam generated in the erasing process being substantially focused on the metal retention layer.
Claim 12
Dependent Claim
49 words
A method as claimed in claim 5, wherein said recording process includes irradiating a laser beam from the backside of the transparent substrate to the thermal expansion layer, and said erasing process includes irradiating a laser beam to the retention layer from an opposite side to the transparent substrate.
Claim 13
Dependent Claim
84 words
A method as claimed in claim 5, wherein said recording process comprises irradiating a laser beam of an intermediate power from the backside of the transparent substrate to the thermal expansion layer to form a dome-like bump for recording a signal, and said erasing process comprises irradiating the entire surface of the retention layer with one of a flashing light beam and a continuous light beam applied thereto from an opposite side to the transparent substrate for erasing a number of recorded signals simultaneously.
Claim 14
Dependent Claim
71 words
A method as claimed in claim 5, wherein said recording process comprises irradiating a laser beam of an intermediate power from the backside of the transparent substrate to the thermal expansion layer to form a dome-like bump for recording a signal, and said erasing process comprises applying a microwave to the transparent substrate to heat the metal retention layer for softening the same, thereby erasing a number of recorded signals simultaneously.
Claim 15
Dependent Claim
27 words
A method as claimed in claim 9, wherein said erasing process includes de-activating a focus servo, and said recording and reproducing processes include activating the focus servo.
Claim 16
Dependent Claim
28 words
A method as claimed in claim 13, wherein the focal point is previously offset slightly in the direction of the transparent substrate when the focus servo is activated.
References Cited (Backward Citations)
JPS56124136A
Cited
US4371954A
Cited
JPS6069846A
Cited
JPS60253035A
Cited
US4825430A
Cited
JPS63276724A
Cited
US4896314A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-02 | 1995-12-02 | 1996-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-02 | 1999-12-02 | 2000-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-02 | 2003-12-02 | 2004-06-02 | $7700.00 | Window Closed / Lapsed |