Method of forming a solder layer on pads of a circuit board and method of mounting an electronic part on a circuit board
Assignee: Furukawa Electric Co Ltd
•
Filing: 1990-11-26
•
Granted: 1992-06-02
•
Expires: 2010-11-26
Abstract
Abstract A paste-like composition containing a lead salt of an organic acid and tin powder is applied on a pad array portion of a circuit board. Then, the paste-like compsition is heated so as to cause precipitation, thereby forming a solder layer formed of a Sn-Pb alloy substantially only on the pads. This precipitation is performed in a state that a liquid pool is formed on the pad array portion when the paste-like composition is liquefied by heating, and the tin powder is settled in the liquid pool. When an electronic part is mounted on the pads, first, preparatory solder layers are formed on the pads by the above-mentioned precipitation process. After a paste-like composition is applied on the preparatory solder layers, the electronic part is put on the paste-like composition. Then, the paste-like composition is heated, thereby soldering leads of the electronic part to the pads.
Inventors
- 👤 Kenichi Fuse
- 👤 Takao Fukunaga
- 👤 Masanao Kohno
- 👤 Hisao Irie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 05:29
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/34; H; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3485; H05K2201/00; H05K2201/10; H05K2201/10613; H05K2201/10954; H05K2201/10992; H05K2203/00; H05K2203/04; H05K2203/043; H05K2203/12; H05K2203/125; H05K3/3473
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
83 words
A method of forming a solder layer on pads of a circuit board, comprising the steps of: applying a paste-like composition comprising a lead salt of an organic acid and tin powder on a pad array portion on the circuit board; and heating the composition to cause a solder alloy being performed in a state that a liquid pool is formed the pad array portion when the paste-like composition is liquefied by heating, and the tin powder is settled in the liquid pool.
Claim 2
Independent Claim
83 words
A method of forming a solder layer on pads of a circuit board, comprising the steps of: applying a paste-like composition comprising a lead salt of an organic acid and tin powder on a pad array portion on the circuit board; and heating the composition to cause a solder alloy being performed in a state that a liquid pool is formed the pad array portion when the paste-like composition is liquefied by heating, and the tin powder is settled in the liquid pool.
Claim 3
Dependent Claim
30 words
The method of forming a solder layer on pads of a circuit board according to claim 1, wherein said solder layers comprise a Sn-Pb alloy having a Pb rich composition.
Claim 4
Independent Claim
88 words
A method of mounting electronic parts on a circuit board, comprising the steps of: forming preparatory solder layers formed of a Sn-Palloy substantially only on pads of a pad array portion on the circuit board; applying a paste-like composition containing a lead salt of an organic acid and tin powder on the preparation solder layers; putting an electronic part having leads on the paste-like composition; and heating the composition to cause solder precipitation for forming a solder alloy, thereby soldering the pads with leads of the electronic part.
Claim 5
Independent Claim
88 words
A method of mounting electronic parts on a circuit board, comprising the steps of: forming preparatory solder layers formed of a Sn-Palloy substantially only on pads of a pad array portion on the circuit board; applying a paste-like composition containing a lead salt of an organic acid and tin powder on the preparation solder layers; putting an electronic part having leads on the paste-like composition; and heating the composition to cause solder precipitation for forming a solder alloy, thereby soldering the pads with leads of the electronic part.
Claim 6
Dependent Claim
39 words
The method according to claim 3, wherein said preparatory solder layers are formed by applying a paste-like composition comprising a lead salt of an organic acid and tin powder on the pad array portion, and heating the paste-like composition.
Claim 7
Dependent Claim
16 words
The method according to claim 3, wherein said preparatory solder layers are formed by electroless plating.
Claim 8
Dependent Claim
44 words
The method according to claim 3, wherein said solder precipitation is performed in a state that a liquid pool is formed on the pad array portion when the paste-like composition is liquefied by heating, and the tin powder is settled in the liquid pool.
Claim 9
Dependent Claim
18 words
The method according to claim 3, wherein said solder alloy comprises a Sn-Pb alloy having Pb rich composition.
Claim 10
Independent Claim
96 words
A method of mounting an electronic part on a circuit board, comprising the steps of: forming preparatory solder layers formed of a Sn-Pb alloy substantially only on pads of a pad array portion of the circuit board; applying a paste-like composition containing a lead salt of an organic acid and tin powder to leads of an electronic part to be soldered with the pads; putting the electronic part on the preparatory solder layers; and heating the composition to cause solder precipitation for forming a solder alloy, thereby soldering the pads with leads of the electronic part.
Claim 11
Independent Claim
96 words
A method of mounting an electronic part on a circuit board, comprising the steps of: forming preparatory solder layers formed of a Sn-Pb alloy substantially only on pads of a pad array portion of the circuit board; applying a paste-like composition containing a lead salt of an organic acid and tin powder to leads of an electronic part to be soldered with the pads; putting the electronic part on the preparatory solder layers; and heating the composition to cause solder precipitation for forming a solder alloy, thereby soldering the pads with leads of the electronic part.
Claim 12
Dependent Claim
38 words
The method according to claim 8, wherein said preparatory solder layers are formed by applying a paste-like composition comprising a lead salt of an organic acid and tin powder on the pad array, and heating the paste-like composition.
Claim 13
Dependent Claim
16 words
The method according to claim 8, wherein said preparatory solder layer is formed by electroless plating.
Claim 14
Dependent Claim
44 words
The method according to claim 8, wherein said solder precipitation is performed in a state that a liquid pool is formed on the pad array portion when the paste-like composition is liquefied by heating, and the tin powder is settled in the liquid pool.
Claim 15
Dependent Claim
19 words
The method according to claim 8, wherein said solder alloy comprises a Sn-Pb alloy having a Pb rich composition.
Claim 16
Independent Claim
137 words
A method of mounting an electronic part on a circuit board, comprising the steps of: forming preparatory solder layers formed of a Sn-Pb alloy substantially only on pads of a pad array portion on the circuit board; applying a paste-like composition comprising a lead salt of an organic acid and tin powder to leads of an electronic part to be soldered with the pads; heating the paste-like composition to cause solder precipitation for forming preparatory solder layers on the leads; applying a flux at least one of the preparatory solder layers on the pads and the preparatory solder layers on the leads; putting the electronic part on the preparatory solder layer on the pads; and heating the preparatory solder layers on the pads and the leads, thereby soldering the pads to the leads of the electronic part.
Claim 17
Independent Claim
137 words
A method of mounting an electronic part on a circuit board, comprising the steps of: forming preparatory solder layers formed of a Sn-Pb alloy substantially only on pads of a pad array portion on the circuit board; applying a paste-like composition comprising a lead salt of an organic acid and tin powder to leads of an electronic part to be soldered with the pads; heating the paste-like composition to cause solder precipitation for forming preparatory solder layers on the leads; applying a flux at least one of the preparatory solder layers on the pads and the preparatory solder layers on the leads; putting the electronic part on the preparatory solder layer on the pads; and heating the preparatory solder layers on the pads and the leads, thereby soldering the pads to the leads of the electronic part.
Claim 18
Dependent Claim
37 words
The method according to claim 13, wherein said preparatory solder layers on the pads are formed by applying a paste-like composition comprising a lead salt of an organic acid and tin powder, and heating the paste-like composition.
Claim 19
Dependent Claim
19 words
The method according to claim 13, wherein said preparatory solder layers on the pads are formed by electroless plating.
Claim 20
Dependent Claim
44 words
The method according to claim 13, wherein said solder precipitation is performed in a state that a liquid pool is formed on the pad array portion when the paste-like composition is liquefied by heating, and the tin powder is settled in the liquid pool.
Claim 21
Dependent Claim
19 words
The method according to claim 13, wherein said solder alloy comprises a Sn-Pb alloy having a Pb rich composition.
Claim 22
Independent Claim
120 words
A method of mounting an electronic part on a circuit board, comprising the steps of: applying a paste-like composition comprising a lead salt of an organic acid and tin powder on a pad array portion on the circuit board; heating the paste-like composition to cause solder precipitation, thereby forming solder layers formed of a Sn-Pb alloy in an amount required for mounting an electronic part on pads of the pad array portion; applying a flux on at least one of the solder layer and leads of an electronic part which is to be mounted on the pads; putting the electronic part on the pads; and heating the solder layers, thereby soldering the pads to the leads of the electronic part.
Claim 23
Independent Claim
120 words
A method of mounting an electronic part on a circuit board, comprising the steps of: applying a paste-like composition comprising a lead salt of an organic acid and tin powder on a pad array portion on the circuit board; heating the paste-like composition to cause solder precipitation, thereby forming solder layers formed of a Sn-Pb alloy in an amount required for mounting an electronic part on pads of the pad array portion; applying a flux on at least one of the solder layer and leads of an electronic part which is to be mounted on the pads; putting the electronic part on the pads; and heating the solder layers, thereby soldering the pads to the leads of the electronic part.
Claim 24
Dependent Claim
43 words
The method according to claim 18, wherein said solder precipitation is performed in a state that a liquid pool is formed on the pad array portion when the paste-like compositionis liquefied by heating, and the tin powder is settled in the liquid pool.
Claim 25
Dependent Claim
14 words
The method according to claim 18, wherein said flux is of a non-halogen type.
Claim 26
Dependent Claim
19 words
The method according to claim 18, wherein said solder alloy comprises a Sn-Pb alloy having a Pb rich composition.
Claim 27
Dependent Claim
41 words
The method according to claim 18, further comprising the step of applying pressure to the upper surfaces of the solder layers, after the step of forming the solder layers, and before the step of putting an electronic part on the pads.
Claim 28
Dependent Claim
23 words
The method according to claim 22, wherein pressure is applied to the upper surfaces of the solder layers while heating the solder layer.
Claim 29
Dependent Claim
37 words
The method according to claim 18, wherein a relationship between the width W of the pads and the thickness H of the solder precipitated on the pads is represented by the formula H=aW, wherein a is 0.05>a>0.5.
Claim 30
Dependent Claim
10 words
The method according to claim 24, wherein a is 0.1>a>0.3.
Claim 31
Dependent Claim
65 words
The method according to claim 4, wherein said preparatory solder layers are formed by electroless plating; said solder precipitation is performed in a state whereby a liquid pool is formed on the pad array portion when the paste-like composition is liquefied by heating and the tin-powder is settled in the liquid pool; and said solder alloy comprises a Sn-Pb alloy having a Pb rich composition.
Claim 32
Dependent Claim
65 words
The method according to claim 9, wherein said preparatory solder layers are formed by electroless plating; said solder precipitation is performed in a state whereby a liquid pool is formed on the pad array portion when the paste-like composition is liquefied by heating and the tin-powder is settled in the liquid pool; and said solder alloy comprises a Sn-Pb alloy having a Pb rich composition.
Claim 33
Dependent Claim
65 words
The method according to claim 14, wherein said preparatory solder layers are formed by electroless plating; said solder precipitation is performed in a state whereby a liquid pool is formed on the pad array portion when the paste-like composition is liquefied by heating and the tin-powder is settled in the liquid pool; and said solder alloy comprises a Sn-Pb alloy having a Pb rich composition.
Claim 34
Dependent Claim
87 words
The method according to claim 23, wherein said flux is a non-halogen type; said solder alloy comprises a Sn-Pb alloy having a Pb rich composition; said solder precipitation is performed in a state whereby a liquid pool is formed on the pad array portion, liquefied by heating, and the tin powder is settled in the liquid pool; and there is a relationship between the width W of the pads and the thickness H of the solder precipitated on the pads represented by the formula H=aW, wherein 0.1>a>0.3.
References Cited (Backward Citations)
US3978378A
Cited
US4293592A
Cited
US4132341A
Cited
US4490283A
Cited
US4728023A
Cited
JPS62227593A
Cited
US4810672A
Cited
JPS63114979A
Cited
US4851153A
Cited
US5021269A
Cited
US4661173A
Cited
US4960236A
Cited
JPH01157796A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-02 | 1995-12-02 | 1996-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-02 | 1999-12-02 | 2000-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-02 | 2003-12-02 | 2004-06-02 | $7700.00 | Window Closed / Lapsed |