Articles having electroconductive components of highly electroconductive resinous compositions
Assignee: Dow Chemical Co
•
Filing: 1975-02-13
•
Granted: 1976-08-31
•
Expires: 1995-02-13
Abstract
Abstract Non-conductive or poorly conductive resinous materials such as organic polymers are rendered highly conductive, e.g., volume resistivities as low as 10 - 3 ohm-cm, by including therein a finely divided, copper metal-containing solid and a salt such as zinc chloride. Such compositions can be fabricated into thin layers which are useful as electrodes or capacitors and into other articles wherein electroconductivity is required.
Inventors
- 👤 Reuben A. Tigner
- 👤 James W. Berg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:58
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/14; H01B; H01B1/00; H01B1/20; H01B1/22
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
107 words
An article having an electroconductive component of an electroconductive resinous composition comprising a resinous material having a volume resistivity greater than 10 6 ohm-cm as the matrix having dispersed therein a finely divided, copper metal-containing solid wherein copper metal is distributed throughout the solid and constitutes at least 50 volume percent of the solid and a salt selected from the group consisting of chlorides, bromides, bicarbonates, tetraborates and carboxylates of the alkali metals, calcium, zinc, lead, silver, and copper and the fluorides of sodium and potassium, said solid and salt being present in amounts sufficient to reduce the volume resistivity of said composition below 10 4 ohm-cm.
Claim 2
Dependent Claim
107 words
An article having an electroconductive component of an electroconductive resinous composition comprising a resinous material having a volume resistivity greater than 10 6 ohm-cm as the matrix having dispersed therein a finely divided, copper metal-containing solid wherein copper metal is distributed throughout the solid and constitutes at least 50 volume percent of the solid and a salt selected from the group consisting of chlorides, bromides, bicarbonates, tetraborates and carboxylates of the alkali metals, calcium, zinc, lead, silver, and copper and the fluorides of sodium and potassium, said solid and salt being present in amounts sufficient to reduce the volume resistivity of said composition below 10 4 ohm-cm.
Claim 3
Dependent Claim
25 words
The article of claim 1 wherein a metallic solid comprises at least 90 volume percent copper and the salt is zinc chloride or zinc bromide.
Claim 4
Dependent Claim
34 words
The article of claim 1 which is a capacitor having at least two electrodes comprising the resinous composition insulated from each other by a dielectric material wherein electrical leads are connected to the electrodes.
Claim 5
Dependent Claim
19 words
The article of claim 1 which is a printed circuit board comprising an electroconductive component of the resinous composition.
Claim 6
Dependent Claim
18 words
The article of claim 1 which is an electrical wire comprising an electroconductive component of the resinous composition.
Claim 7
Dependent Claim
107 words
An article having an electroconductive coating comprising an electroconductive resinous composition comprising a resinous material having a volume resistivity greater than 10 6 ohm-cm as the matrix having dispersed therein a finely divided, copper metal-containing solid wherein copper metal is distributed throughout the solid and constitutes at least 50 volume percent of the solid and a salt selected from the group consisting of chlorides, bromides, bicarbonates, tetraborates and carboxylates of the alkali metals, calcium, zinc, lead, silver, and copper and the fluorides of sodium and potassium, said solid and salt being present in amounts sufficient to reduce the volume resistivity of said composition below 10 4 oh-cm.
Claim 8
Dependent Claim
107 words
An article having an electroconductive coating comprising an electroconductive resinous composition comprising a resinous material having a volume resistivity greater than 10 6 ohm-cm as the matrix having dispersed therein a finely divided, copper metal-containing solid wherein copper metal is distributed throughout the solid and constitutes at least 50 volume percent of the solid and a salt selected from the group consisting of chlorides, bromides, bicarbonates, tetraborates and carboxylates of the alkali metals, calcium, zinc, lead, silver, and copper and the fluorides of sodium and potassium, said solid and salt being present in amounts sufficient to reduce the volume resistivity of said composition below 10 4 oh-cm.
Claim 9
Dependent Claim
32 words
The article of claim 1 which is a multilayer structure comprising at least two electroconductive layers of the resinous composition that are insulated from each other by layers of a dielectric material.
Claim 10
Dependent Claim
22 words
The article of claim 7 wherein the thicknesses of the layers are within the range from about 0.004 to about 50 mils.
Claim 11
Dependent Claim
120 words
An article having an electroconductive component of an electroconductive resinous composition comprising a resinous material having a volume resistivity greater than 10 6 ohm-cm as the matrix having dispersed therein (1) a finely divided, copper metal-containing solid wherein the copper metal of said solid forms an essentially continuous layer covering the particle surfaces of said solid and constitutes at least 10 volume percent of said solid and (2) a salt selected from the group consisting of chlorides, bromides, bicarbonates, tetraborates and carboxylates of the alkali metals, calcium, zinc, lead, silver, and copper and the fluorides of sodium and potassium, said solid and salt being present in amounts sufficient to reduce the volume resistivity of said composition below 10 4 ohm-cm.
Claim 12
Dependent Claim
120 words
An article having an electroconductive component of an electroconductive resinous composition comprising a resinous material having a volume resistivity greater than 10 6 ohm-cm as the matrix having dispersed therein (1) a finely divided, copper metal-containing solid wherein the copper metal of said solid forms an essentially continuous layer covering the particle surfaces of said solid and constitutes at least 10 volume percent of said solid and (2) a salt selected from the group consisting of chlorides, bromides, bicarbonates, tetraborates and carboxylates of the alkali metals, calcium, zinc, lead, silver, and copper and the fluorides of sodium and potassium, said solid and salt being present in amounts sufficient to reduce the volume resistivity of said composition below 10 4 ohm-cm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-31 | 1980-03-01 | 1980-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-31 | 1984-03-01 | 1984-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-31 | 1988-03-01 | 1988-08-31 | $7700.00 | Window Closed / Lapsed |