Thermoplastic resin composition
Assignee: Eneos Corp
•
Filing: 1990-06-20
•
Granted: 1992-05-26
•
Expires: 2010-06-20
Abstract
Abstract Partially crosslinked, thermoplastic resin compositions prepared by dynamically heat-treating a thermoplastic resin, having substantially no carbon-carbon bond unsaturation, in the presence of: a dihydroaromatic compound as a crosslinking agent, said dihydroaromatic compound being selected from the group consisting of a 1,2-dihydroquinoline compound, a polymer thereof and 9,10-dihydrophenanthrene; and a polyfunctional monomer, such as a bismaleimide compound.
Inventors
- 👤 Toshio Inoue
- 👤 Masaaki Miyazaki
- 👤 Shiuzi Kashiwase
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:44
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08F; C08F255/00; C08F255/02; C08F255/04; C08F257/00; C08F257/02; C08F283/00; C08K; C08K5/00; C08K5/01; C08L23/08; C08L23/0807; C08L23/0815; C08L23/0846; C08L23/0869; C08L23/10; C08L23/16; C08L25/00; C08L25/02; C08L25/04; C08L25/06; C08L67/00; C08L77/00; C08L77/02; C08K5/16; C08K5/20; C08K5/34; C08K5/3412; C08K5/3432; C08K5/3437; C08L2205/00; C08L2205/03; C08L2205/035; C08L23/18; C08L23/20; C08L2312/00; C08L79/00; C08L79/04
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
52 words
A partially crosslinked thermoplastic resin composition prepared by dynamically heat-treating a thermoplastic resin having substantially no carbon-carbon bond unsaturation in the presence of a dihydroaromatic compound as a crosslinking agent, said dihydroaromatic compound being selected from the group consisting of a 1,2-dihydroquinoline compound, a polymer thereof and 9,10-dihydrophenanthrene; and a polyfunctional monomer.
Claim 2
Dependent Claim
52 words
A partially crosslinked thermoplastic resin composition prepared by dynamically heat-treating a thermoplastic resin having substantially no carbon-carbon bond unsaturation in the presence of a dihydroaromatic compound as a crosslinking agent, said dihydroaromatic compound being selected from the group consisting of a 1,2-dihydroquinoline compound, a polymer thereof and 9,10-dihydrophenanthrene; and a polyfunctional monomer.
Claim 3
Dependent Claim
23 words
A thermoplastic resin composition as set forth in claim 1, wherein said thermoplastic resin comprises a polyolefin resin and a heterogeneous thermoplastic resin.
Claim 4
Dependent Claim
28 words
A thermoplastic resin composition as set forth in claim 1, wherein said thermoplastic resin is constituted by only a mixture of at least two kinds of polyolefin resins.
Claim 5
Dependent Claim
29 words
A thermoplastic resin composition as set forth in claim 2, wherein said polyolefin resin includes at least one member selected from the group consisting of polypropylenes and ethylene (co)polymers.
Claim 6
Dependent Claim
18 words
A thermoplastic resin composition as set forth in claim 1, wherein said polyfunctional monomer is a bismaleimide compound.
Claim 7
Dependent Claim
22 words
A thermoplastic resin composition as set forth in claim 1, wherein a softening agent is also used together with the thermoplastic resin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-05-26 | 1995-11-25 | 1996-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-05-26 | 1999-11-25 | 2000-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-05-26 | 2003-11-25 | 2004-05-26 | $7700.00 | Window Closed / Lapsed |