Tungsten and tungsten nitride coatings for metals and ceramics
Assignee: Dow Chemical Co
•
Filing: 1990-11-06
•
Granted: 1992-05-19
•
Expires: 2010-11-06
Abstract
Abstract Compositions and a process are disclosed for producing tungsten and tungsten nitride coatings on metals or ceramics, utilizing a tungsten-containing metal-organic precursor compound dissolved in an organic solvent. Conversion of the precursor compound to a tungsten or tungsten nitride coating is accomplished by heating the coated metal or ceramic to a temperature of about 600°-1200° C. under a nitrogen or other inert gas atmosphere.
Inventors
- 👤 Kevin E. Howard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:40
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/80; C04B41/81; C04B41/85; C04B41/88; C04B41/009; C04B41/45; C04B41/4584; C04B41/50; C04B41/51; C04B41/5133; C23; C23C; C23C18/00; C23C18/02; C23C18/12; C23C18/1204; C23C18/125; C23C18/1275
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
91 words
A method of coating a metal or ceramic body for protection against mechanical and thermal deterioration comprising: (A) applying to the surface of said ceramic or metal body a precursor coating from a solution of a metal-organic compound, which is the reaction product of an alkyl or aryl amine and tungsten hexahalide, and (B) heating said metal or ceramic body containing said precursor coating under an inert gas atmosphere at a temperature of about 600°-1200° C. to convert said precursor coating to tungsten or a mixture of tungsten and tungsten nitride.
Claim 2
Independent Claim
91 words
A method of coating a metal or ceramic body for protection against mechanical and thermal deterioration comprising: (A) applying to the surface of said ceramic or metal body a precursor coating from a solution of a metal-organic compound, which is the reaction product of an alkyl or aryl amine and tungsten hexahalide, and (B) heating said metal or ceramic body containing said precursor coating under an inert gas atmosphere at a temperature of about 600°-1200° C. to convert said precursor coating to tungsten or a mixture of tungsten and tungsten nitride.
Claim 3
Dependent Claim
35 words
The method of claim 1, wherein said reaction product has the formula: (NHR).sub.2 --W--(NR).sub.2 wherein R is individually selected from an alkyl group of 1-5 carbon atoms or an aryl group of 5-10 carbon atoms.
Claim 4
Dependent Claim
18 words
The method of claim 2, wherein the metal-organic compound is the reaction product of tungsten hexachloride and tertiary-butylamine.
Claim 5
Dependent Claim
27 words
The method of claim 3, wherein said precursor coating is applied by dipping said metal or ceramic body into an organic solvent solution of said metal-organic compound.
Claim 6
Dependent Claim
41 words
The method of claim 1, wherein said metal-organic compound is applied to mullite whiskers by dip coating said mullite whiskers in an alkyl aliphatic solvent solution of said metal-organic compound and converted to tungsten by heat treatment in an argon atmosphere.
Claim 7
Dependent Claim
27 words
The method of claim 1, wherein said metal-organic compound is coated onto a silicon nitride substrate and, thereafter, converted to tungsten by heating in a nitrogen atmosphere.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-05-19 | 1995-11-18 | 1996-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-05-19 | 1999-11-18 | 2000-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-05-19 | 2003-11-18 | 2004-05-19 | $7700.00 | Window Closed / Lapsed |