Baton method of heat treating expandable
Assignee: Armament Systems and Procedures Inc
•
Filing: 1991-08-22
•
Granted: 1992-05-05
•
Expires: 2011-08-22
Abstract
Abstract An expandable baton is constructed of heat treatable alloy steel and is formed according to a method which provides both ease of workability of the component materials and strength for the resultant baton. The disclosed method comprises the steps of first forming the sections from heat treatable alloy steel, then annealing the baton components to soften them, then forming the components into the desired shapes, and finally hardening the components. The resulting baton provides the strength and reliability required in such a device.
Inventors
- 👤 Kevin L. Parsons
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:54
CPC Classifications
F; F41; F41B; F41B15/00; F41B15/02; F41B15/022; F41B15/025; C; C21; C21D; C21D9/00; C21D9/0068
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
107 words
A method for manufacturing a expandable baton comprising steps of: (a) forming heat treatable alloy steel into a main section and a telescoping section; (b) annealing the main section and the telescoping section formed in step (a) by heat treating; (c) after annealing the main section and the telescoping section in step (b), forming a portion of a joint on both the main and telescoping sections such that the joint portions on the main and telescoping sections form a complete joint when the baton is in an extended position; (d) after forming the joint portions in step (c), hardening the main and telescoping sections by heat treating.
Claim 2
Independent Claim
107 words
A method for manufacturing a expandable baton comprising steps of: (a) forming heat treatable alloy steel into a main section and a telescoping section; (b) annealing the main section and the telescoping section formed in step (a) by heat treating; (c) after annealing the main section and the telescoping section in step (b), forming a portion of a joint on both the main and telescoping sections such that the joint portions on the main and telescoping sections form a complete joint when the baton is in an extended position; (d) after forming the joint portions in step (c), hardening the main and telescoping sections by heat treating.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein the hardening of step (d) results in a hardness of at least 30 Rockwell C scale.
Claim 4
Dependent Claim
17 words
The method of claim 2 wherein the hardening of step (d) is performed by an austempering process.
Claim 5
Dependent Claim
63 words
The method of claim 1 in which step (c) of forming joint portions on the main and telescoping sections comprises the steps of: (i) swaging one end of the main section; and (ii) flaring one end of the telescoping section, the flared end of the telescoping section being mated to form a deadlock taper joint with the swaged end of the main section.
Claim 6
Dependent Claim
65 words
The method of claim 4 wherein the baton includes a plurality of telescoping sections with progressively smaller diameters, each joint between the telescoping sections comprising a flare on one section in mating engagement with a swage on the adjoining telescoping section, and the method of forming the swages and flares follows the steps (b)-(d) of annealing, then forming the swages and flares, and then hardening.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-05-05 | 1995-11-04 | 1996-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-05-05 | 1999-11-04 | 2000-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-05-05 | 2003-11-04 | 2004-05-05 | $7700.00 | Window Closed / Lapsed |