3,4-polyisoprene-containing rubber blend mixtures for tire treads
Assignee: KARBOCHEM Pty Ltd
•
Filing: 1991-03-20
•
Granted: 1992-04-14
•
Expires: 2011-03-20
Abstract
Abstract Rubber mixtures for tire treads are found, which show an improved wet skid resistance coupled with balanced abrasion and rolling resistance properties. This is achieved by rubber blend mixtures which contain 3,4-polyisoprene having a 3,4-content from 55 to 75%, a glass transition temperature from 0° to -25° C., a number average molecular weight of 200,000 and higher and an inhomogeneity U of less than 1.8. Motor vehicle tires can be prepared in an advantageous manner with these rubber mixtures.
Inventors
- 👤 Jurgen Wolpers
- 👤 Hans B. Fuchs
- 👤 Christoph Herrmann
- 👤 Walter Hellermann
- 👤 Karl-Heinz Nordsiek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:01
CPC Classifications
B; B60; B60C; B60C1/00; B60C1/0016; C; C08; C08L; C08L9/00; C08L21/00; Y; Y02; Y02T; Y02T10/00; Y02T10/80; Y02T10/86; Y10; Y10S; Y10S152/00; Y10S152/905
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
125 words
A rubber mixture for a tire tread having improved wet skid resistance, comprising from 5 to 35 parts by weight of a 3,4-polyisoprene and from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content from 55 to 75%, determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning calorimetry at a heating rate of 10° K/minute, c) a number average molecular weight Mn, determined by gel permeation chromatography of 220,000 or higher, and d) an inhomogeneity U of less than 1.8, the inhomogeneity being defined by the equation U=Mw/Mn-1, where Mw and Mn are determined by gel permeation chromatography.
Claim 2
Dependent Claim
125 words
A rubber mixture for a tire tread having improved wet skid resistance, comprising from 5 to 35 parts by weight of a 3,4-polyisoprene and from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content from 55 to 75%, determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning calorimetry at a heating rate of 10° K/minute, c) a number average molecular weight Mn, determined by gel permeation chromatography of 220,000 or higher, and d) an inhomogeneity U of less than 1.8, the inhomogeneity being defined by the equation U=Mw/Mn-1, where Mw and Mn are determined by gel permeation chromatography.
Claim 3
Dependent Claim
23 words
The rubber mixture of claim 1, comprising 10-20 parts by weight of said 3,4-polyisoprene and 90-80 parts by weight of said sulfur-vulcanizable elastomer.
Claim 4
Dependent Claim
23 words
The rubber mixture of claim 1, wherein said sulfur-vulcanizable elastomer is a styrene/butadiene rubber, a polybutadiene rubber, a natural rubber or mixture thereof.
Claim 5
Dependent Claim
18 words
The rubber mixture of claim 3, wherein said styrene/butadiene rubber is prepared by solution polymerization or emulsion polymerization.
Claim 6
Dependent Claim
19 words
The rubber mixture of claim 1, wherein said 3,4-polyisoprene has a glass transition temperature from -5° to -16° C.
Claim 7
Dependent Claim
107 words
A rubber mixture for a tire tread having improved wet skid resistance, comprising from 5 to 35 parts by weight of a 3,4-polyisoprene and from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content from 55 to 75%, determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning colorimetry at a heating rate of 10° K/minute, c) a number average molecular weight Mn, determined by gel permeation chromatography from 200,000 to 218,000, and d) an inhomogeneity (U) of 1.4 or less.
Claim 8
Dependent Claim
107 words
A rubber mixture for a tire tread having improved wet skid resistance, comprising from 5 to 35 parts by weight of a 3,4-polyisoprene and from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content from 55 to 75%, determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning colorimetry at a heating rate of 10° K/minute, c) a number average molecular weight Mn, determined by gel permeation chromatography from 200,000 to 218,000, and d) an inhomogeneity (U) of 1.4 or less.
Claim 9
Dependent Claim
23 words
The rubber mixture of claim 6, comprising 10-20 parts by weight of said 3,4-polyisoprene and 90-80 parts by weight of said sulfur-vulcanizable elastomer.
Claim 10
Dependent Claim
23 words
The rubber mixture of claim 6, wherein said sulfur-vulcanizable elastomer is a styrene/butadiene rubber, a polybutadiene rubber, a natural rubber or mixture thereof.
Claim 11
Dependent Claim
18 words
The rubber mixture of claim 8, wherein said styrene/butadiene rubber is prepared by solution polymerization or emulsion polymerization.
Claim 12
Dependent Claim
19 words
The rubber mixture of claim 6, wherein said 3,4-polyisoprene has a glass transition temperature from -5° to -16° C.
Claim 13
Independent Claim
139 words
A method of improving the wet skid resistance of a rubber mixture for a tire tread, comprising adding from 5 to 35 parts by weight of a 3,4-polyisoprene to from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer containing conventional fillers, oils, auxiliaries and vulcanizing agents, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content from 55 to 75%, as determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning calorimetry at a heating rate of 10° K/minute, c) a number average molecular weight Mn, determined by gel permeation chromatography of 220,000 or higher, and d) an inhomogeneity U of less than 1.8, the inhomogeneity being defined by the equation U=Mw/Mn-1, where Mw and Mn are determined by gel permeation chromatography.
Claim 14
Independent Claim
139 words
A method of improving the wet skid resistance of a rubber mixture for a tire tread, comprising adding from 5 to 35 parts by weight of a 3,4-polyisoprene to from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer containing conventional fillers, oils, auxiliaries and vulcanizing agents, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content from 55 to 75%, as determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning calorimetry at a heating rate of 10° K/minute, c) a number average molecular weight Mn, determined by gel permeation chromatography of 220,000 or higher, and d) an inhomogeneity U of less than 1.8, the inhomogeneity being defined by the equation U=Mw/Mn-1, where Mw and Mn are determined by gel permeation chromatography.
Claim 15
Dependent Claim
21 words
The method of claim 11, comprising adding 10-20 parts by weight of said 3,4-polyisoprene to 90-80 parts of said sulfur-vulcanizable elastomer.
Claim 16
Dependent Claim
18 words
The method of claim 11, wherein said 3,4-polyisoprene has a glass transition temperature of -5° to -16° C.
Claim 17
Dependent Claim
22 words
The method of claim 11, wherein said sulfur-vulcanizable elastomer is a styrene/butadiene rubber, a polybutadiene rubber, a natural rubber or mixture thereof.
Claim 18
Independent Claim
118 words
A method for improving the wet skid resistance of a rubber mixture, comprising adding from 5 to 35 parts by weight of a 3,4-polyisoprene to from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer, further containing conventional fillers, oils, auxiliaries or vulcanizing agents, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content of from 55 to 75%, determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning colorimetry at a heating rate of 10° K/minute, c) a number average molecular weight, determined by gel permeation chromatography, of from 200,000 to 218,000, and d) an inhomogeneity U of 1.4 or less.
Claim 19
Independent Claim
118 words
A method for improving the wet skid resistance of a rubber mixture, comprising adding from 5 to 35 parts by weight of a 3,4-polyisoprene to from 95 to 65 parts by weight of a sulfur-vulcanizable elastomer, further containing conventional fillers, oils, auxiliaries or vulcanizing agents, wherein said 3,4-polyisoprene is at least partially incompatible with said sulfur-vulcanizable elastomer and has a) a 3,4-content of from 55 to 75%, determined by NMR spectroscopy, b) a glass transition temperature from 0° to -25° C., determined by differential scanning colorimetry at a heating rate of 10° K/minute, c) a number average molecular weight, determined by gel permeation chromatography, of from 200,000 to 218,000, and d) an inhomogeneity U of 1.4 or less.
Claim 20
Dependent Claim
21 words
The method of claim 15, comprising adding 10-20 parts by weight of said 3,4-polyisoprene to 90-80 parts of said sulfur-vulcanizable elastomer.
Claim 21
Dependent Claim
18 words
The method of claim 15, wherein said 3,4-polyisoprene has a glass transition temperature of -5° to -16° C.
Claim 22
Dependent Claim
22 words
The method of claim 15, wherein said sulfur-vulcanizable elastomer is a styrene/butadiene rubber, a polybutadiene rubber, a natural rubber or mixture thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-04-14 | 1995-10-14 | 1996-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-04-14 | 1999-10-14 | 2000-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-04-14 | 2003-10-14 | 2004-04-14 | $7700.00 | Window Closed / Lapsed |